Search

The CVD diamond films at different growth stages were prepared on the same substrate by DC arc plasma jet CVD. The surface morphologies and residual stress of diamond films were characterized by scanning electron microscope and Raman spectroscopy. The intrinsic stress of diamond films were obtained by subtracting thermal stress from residual stress. The results showed that the intrinsic compress stress was 0.42 GPa for the precoalescence stage due to the sp 2 carbon inclusions in diamond islands. With the diamond islands growing up and even snapping together to form grain boundary at the coalescence stage the intrinsic compress stress was 0.06 GPa. Eventually, the diamond islands coalesced into a continuous polycrystalline film, the intrinsic compress stress vanished and converted to tensile stress, the intrinsic tensile stress reached 1.41 GPa due to the number of grain boundaries increasing. The evolution of intrinsic stress during diamond film initial growth was mainly attributed to the surface free energy of diamond islands changed to the free energy of grain boundaries which was consistent with the Nix-Clemens model. [ABSTRACT FROM AUTHOR]

Diamond radiation detector is an ideal choice for the next-generation radiation detection in harsh environments, due to its small size, high irradiation resistance and fast response. However, high-purity single crystal diamond is hard to be prepared at the high growth rate due to the inevitable impurity incorporation. In this paper, based on the high-quality high-temperature/high-pressure (HPHT) single crystal diamond substrate, detector-grade single crystal diamonds material with high purity and low defect density were epitaxially grown at growth rate of about 4 μm/h by using plasma environment purification technology. It showed that the full width at half maximum of X-ray rocking curve of high-quality single crystal diamond could reach 0.007°, there was no nitrogen related impurity in PL spectrum, and the substitutional nitrogen content estimated by UV absorption spectrum was less than 10 ppb. After metallization and packaging process, the diamond detectors were prepared and the detector response under irradiation with 241Am α-particles was realized. For the sample with fewer dislocations, the charge collection efficiency and energy resolution of this detector were 86.8 % and 7.85 % for electrons, and 96.7 % and 2.48 % for holes. The product of mobility and lifetime of electrons and holes were 1.7 × 10−4 cm2V−1 and 3.7 × 10−4 cm2V−1, respectively. The high performances of the detector indicate that the current diamond detector can meet the application requirements of commercial diamond detectors. [Display omitted] • Detector-grade diamond was prepared by plasma environment purification technology. • The high-purity single crystal diamond was grown at growth rate of about 4 μm/h. • The diamond detector with charge collection efficiency of 96.7 % was realized. • The products of mobility and lifetime of electrons and holes were 1.7 × 10−4 and 3.7 × 10−4 cm2V−1. [ABSTRACT FROM AUTHOR]

Lift-off is a promising method to prepare thin, high-finish, and freestanding large-area single crystal and polycrystalline diamonds. However, accurate control of the damage layer characteristic to achieve both stress release and lift-off process is difficult. In this work, high-energy C+ was implanted in single crystal diamond and polycrystalline diamond to create subsurface damage. The defect behavior and structural transformation of the ion implantation and annealing process were investigated. The homoepitaxial growth was subsequently carried out and the epitaxial layer was lifted off from the substrate by selectively etching the damaged layer. The results show that the cap layer and the substrate (below the damage layer) keep the sp3 carbon structure before and after annealing, which is confirmed by the atomic-scale electron energy loss spectroscopy (EELS). The high-resolution transmission electron microscopy (HRTEM) images show that after annealing at 1000 °C for 1 h, the damaged layer was transformed from amorphous carbon to a mixture of graphite and amorphous carbon, providing the damaged layer that could be removed by electrochemical solution. Meanwhile, the distorted diamond area was changed to a sharp interface, which ensures the low roughness of the substrate surface after the lift-off process. After etching for 30 h, a freestanding polycrystalline diamond film with a thickness of 100 μm and a surface roughness of 1.68 nm was obtained. The roughness of the lift-off substrate surface is 1.10 nm, indicating the epitaxial growth can be repeated directly without polishing. [Display omitted] • The defect behavior and structural transformation of the high-energy C+ implanted diamonds were investigated. • The stress state of the diamonds before and after ion implantation and after lift-off process were evaluated. • A 100 μm-thick freestanding polycrystalline diamond film with a surface roughness of 1.68 nm was successful obtained. [ABSTRACT FROM AUTHOR]

In order to realize the practical use of diamond as a semiconductor material, large-area single-crystal diamond wafers with uniform quality are required. Mosaic growth is an effective method to produce inch-grade single-crystal diamonds. However, the quality of the wafer is limited by the junction interface seriously, because cracking occurs easily due to the high internal stress. In this paper, the repetition growth method was adopted to grow mosaic splicing single-crystal diamond without polycrystalline diamond interface. The high-quality single crystal diamond slices were reduplicated by microwave plasma chemical vapor deposition (MPCVD). The substrates were obtained by cutting a piece of CVD diamond along a plane perpendicular to 〈001〉 (with a (100)-oriented surface). The evolution of the growth characteristics around the junction of the substrates at different stages was studied. The results show that the surface of the epitaxial layers gradually evolves from blurry terraces to a regular well-ordered step flow. When the substrates have the same deviation direction and the off-direction angles are within 3°, the junction of the substrates can connect smoothly. Raman mapping shows that there is a mixture of tensile stress and compressive stress near the junction. As the thickness of the epitaxial layer increases from 280 μm to 560 μm, the range of tensile stress near the joint area expands from 85 μm to 150 μm, the maximum tensile stress increases from 0.08 GPa to 0.16 GPa. In addition, the value of FWHM in the X-ray rocking curve is less than 2.80 cm−1 around the junction, which indicates good crystal quality. [Display omitted] • The evolution of growth characteristics around the junction in the mosaic diamond was studied. • The mosaic boundary evolved from blurry terraces to a well-ordered step flow and finally connected. • The lowest value of tensile stress near the joint area was reported as the film thickness increased. • The larger FWHM of Raman peak around the junction is caused by the increased tensile stress. • The "inherit" effect of NV content of the epitaxial layer was observed for the corresponding substrate. [ABSTRACT FROM AUTHOR]