A novel apatite structure phosphor Ca 9 La(PO 4 ) 5 (GeO 4 )F 2 :Dy 3+ (CLPGF:Dy 3+ ) with a hexagonal lattice in the P 6 3 / m space group was synthesized via a facile solid state technique. The crystal and fine local structure as well as their photoluminescence properties were investigated in detail. The CLPGF:Dy 3+ phosphor can absorb in the UV-vis spectral region of 290–475 nm and exhibit two intense emission bands centered at 485 and 580 nm, which ascribes to 4 F 9/2 → 6 H 15/2 and 4 F 9/2 → 6 H 13/2 transitions of Dy 3+ , respectively. The concentration quenching of Dy 3+ emission occurs via the energy transfer among the nearest-neighbor ions and the corresponding quenching mechanism was verified to be the dipole-dipole interaction. The quantum efficiencies of the phosphors were examined to be 72.9% and its luminescence intensity at 150 °C decreases to 93.8% and 98.6% of the initial value at room temperature, which corresponds to 4 F 9/2 to 6 H 15/2 transition and 4 F 9/2 to 6 H 13/2 transition of Dy 3+ ions, respectively. Their interesting photoluminescence properties indicate that the CLPGF:Dy 3+ phosphor is a promising white-emitting candidate for w -LEDs applications. [ABSTRACT FROM AUTHOR]

Developing color-tunable phosphors via the introduction of co-doping activators and sensitizers to the host with energy transfer processes has been a state-of-the-art topic for a long time. In this work, novel emission-tunable oxyapatites-type Ba 10 (PO 4 ) 6 O:Eu 2+ ,Tb 3+ /Li + phosphors were prepared via a high temperature solid state reaction for the applications in white light emitting diodes ( w -LEDs) with higher color rendering index. Tunable colors from blue to green can be realized in the Ba 10 (PO 4 ) 6 O:Eu 2+ ,Tb 3+ /Li + by varying the relative ratios of Eu 2+ to Tb 3+ , showing good absorption in the range of 230–400 nm. The energy transfer mechanism from Eu 2+ to Tb 3+ ions was demonstrated to be a quadrupole-quadrupole interaction by combining the Inokuti-Hirayama (I H) model and Reisfeld's approximation. Importantly, a prototype white lamp was packaged by mixing Ba 9.83 (PO 4 ) 6 O: 0.03Eu 2+ , 0.07Tb 3+ , 0.07Li + and commercial red phosphor CaAlSiN 3 : Eu 2+ , and the lamp exhibits a higher color rendering index (Ra = 92 and R9 = 56) and warm correlated color temperature of 4361 K for the actual application. Better luminescent properties compared to commercial Y 3 A l5 O 12 :Ce 3+ -based w -LEDs, indicating that Ba 10 (PO 4 ) 6 O: Eu 2+ , Tb 3+ /Li + phosphors are emerging as potential phosphor-converted w -LEDs. [ABSTRACT FROM AUTHOR]