Abstract: Co-precipitation method of SnCl2·2H2O and graphene oxide (GO) solution was performed to fleetly prepare graphene/SnO2 composite. The structure and composition of the nanocomposite were detected by means of XRD, SEM, TEM and FT-IR. The GO was reduced by bivalent tin ions to graphene nanosheet (GNS) via solution reaction and SnO2 nano-crystals with size of 4–6nm were homogeneously distributed on the matrix of GNS. It was found that the disorder degree of graphene in GNS/SnO2 composite prepared by the bivalent tin ion assisted reduction method was much lower than that of GNS obtained via pyrolysis reduction. The possible mechanism for this phenomenon was discussed in detail. The N2 adsorption tests showed an ink-bottle-like pore structure of GNS/SnO2 and the SnO2 nanoparticles were confined in the interlayer of GNS without agglomeration. These structural features were desirable and enabled GNS/SnO2 an excellent anode material in lithium ion battery. The electrochemical tests showed that the composite could deliver a reversible capacity of 775.3mAh/g and capacity retention of 98% after 50 cycles. [Copyright &y& Elsevier]

Abstract: The corrosion behavior of reinforcing steel in cement mortar has been studied by electrochemical noise (EN) compared with the electrochemical impedance spectroscopy (EIS). The wavelet transform, as well as the statistical methods including the standard deviation of current noise (σ I) and noise resistance (R n), has been employed to analyze the EN data of reinforcing steel in mortar. It is revealed that there exist three different corrosion stages of reinforcing steel in cement mortar, including a competition process between breakdown and repassivation of passive film, a pitting development and an active corrosion during the 20 cyclic immersion and drying tests. The energy distribution plot (EDP) is able to provide useful information about the dominant process for the different corrosion stages. [Copyright &y& Elsevier]

Abstract: In this paper, graphene-modified Li3V2(PO4)3 composites have been developed as Li-ion battery cathode materials with high specific capacity and excellent cycling stability. The composites are prepared by spray–drying process using graphene oxide nanosheet and citric acid as carbon source. X-ray diffraction patterns demonstrate that the as-prepared samples are well crystallized with orderly monoclinic structures. SEM and TEM images reveal that the 3D network graphene and Li3V2(PO4)3 primary nanoparticles interlace with each other. The citric acid-derived amorphous carbon species interrupt the stacking of graphene sheets and minimize in-plane anisotropy of electronic migration within graphene layers, which would facilitate fast electron migration and Li+ diffusion throughout the micro-sized spherical secondary particles. The discharge capacity of the composite could respectively achieve 131.4 and 181.5mAhg−1 in the voltage range 3.0–4.3V and 3.0–4.8V at 0.1C discharge rate, which almost reach the theoretical capacity of the cathode material. Both of them nearly showed no capacity decay at 0.1C charging and discharging rate after long cycles. [Copyright &y& Elsevier]