Abstract: Well dispersed PtSn/C, PtRu/C and Pt/C electrocatalysts were synthesized by a modified polyol process and characterized by X-ray diffraction (XRD), transmission electron microscope (TEM) and inductively coupled plasma-atomic emission spectrometry techniques. XRD patterns show that Ru induces the contraction of Pt lattice parameter while Sn makes the Pt crystal lattice extended. Ethanol oxidation activities on the catalysts were studied via cyclic voltammetry (CV) and chronoamperometry (CA) methods at room temperature. It is found that the electrode potential plays an important role in the electrochemical behavior of ethanol oxidation on PtRu/C and PtSn/C catalysts. In the lower potential region, PtSn/C possesses higher performance for ethanol oxidation, while in the higher potential region PtRu/C is more active. The different promotion effects of PtSn/C and PtRu/C to ethanol oxidation can be explained by the structural effect and modified bi-functional mechanism in different potential region. Single cell test of a direct ethanol fuel cell (DEFC) was also carried out to elucidate the promotion effect of PtRu/C and PtSn/C catalysts on the ethanol oxidation at 90°C. [Copyright &y& Elsevier]

Abstract: Carbon supported PtSn alloy and PtSnO x particles with nominal Pt:Sn ratios of 3:1 were prepared by a modified polyol method. High resolution transmission electron microscopy (HRTEM) and X-ray microchemical analysis were used to characterize the composition, size, distribution, and morphology of PtSn particles. The particles are predominantly single nanocrystals with diameters in the order of 2.0–3.0nm. According to the XRD results, the lattice constant of Pt in the PtSn alloy is dilated due to Sn atoms penetrating into the Pt crystalline lattice. While for PtSnO x nanoparticles, the lattice constant of Pt only changed a little. HRTEM micrograph of PtSnO x clearly shows that the change of the spacing of Pt (111) plane is neglectable, meanwhile, SnO2 nanoparticles, characterized with the nominal 0.264nm spacing of SnO2 (101) plane, were found in the vicinity of Pt particles. In contrast, the HRTEM micrograph of PtSn alloy shows that the spacing of Pt (111) plane extends to 0.234nm from the original 0.226nm. High resolution energy dispersive X-ray spectroscopy (HR-EDS) analyses show that all investigated particles in the two PtSn catalysts represent uniform Pt/Sn compositions very close to the nominal one. Cyclic voltammograms (CV) in sulfuric acid show that the hydrogen ad/desorption was inhibited on the surface of PtSn alloy compared to that on the surface of the PtSnO x catalyst. PtSnO x catalyst showed higher catalytic activity for ethanol electro-oxidation than PtSn alloy from the results of chronoamperometry (CA) analysis and the performance of direct ethanol fuel cells (DEFCs). It is deduced that the unchanged lattice parameter of Pt in the PtSnO x catalyst is favorable to ethanol adsorption and meanwhile, tin oxide in the vicinity of Pt nanoparticles could offer oxygen species conveniently to remove the CO-like species of ethanolic residues to free Pt active sites. [Copyright &y& Elsevier]