Search

Vanadium Nitride (VN) is attractive for energy storage due to its high conductivity (1.6 × 106 S/m) and specific capacitance (1350 F/g) but limited to alkaline electrolytes for redox. In contrast, V 2 O 3 is redox active but not very conductive. In these hybrids a mixture of VN and vanadium oxide (V 2 O 3) were encapsulated in electrospun carbon-nanofibers. A combination of VN and V 2 O 3 takes advantage of the high conductivity from VN and the redox activity from V 2 O 3. Additionally, having the vanadium encapsulated within the carbon can help with the stability as the electrolyte will not have direct interaction with the surface. These hybrids were made by in-situ nitridation of the encapsulated V 2 O 5 followed by ex-situ activation with carbon dioxide. The hybrids were characterized by XPS and Raman spectroscopy. Hybrids of VN/V 2 O 3 -CNF showed increased capacitance of 245 Fg−1 with energy and power densities of 70.2 Wh kg−1 and 1751 W kg−1 in ionic liquid electrolyte. The devices showed good cycle stability with ∼90 % retention after 10,000 cycles at a current density of 1 Ag−1. These findings highlight the potential of VN/V 2 O 3 -CNF hybrids as high-performance supercapacitor electrodes. The combination of high conductivity and redox activity, along with encapsulation within CNFs, opens promising avenues for advanced energy storage. [ABSTRACT FROM AUTHOR]

The synthesis of Laser-Induced Graphene (LIG) through the laser ablation process of carbon-containing materials is a rapid and scalable process which enables the production of graphene in a cost-effective manner. In recent years, metal oxide – graphene composite electrodes have gained a lot of importance due to their use in various Energy Storage Devices (ESDs). In our investigation, we manufacture composite electrodes of manganese dioxide (MnO 2) and LIG through a hydrothermal process and use it as electrodes in Flexible Supercapacitors. This method deviates from traditional procedures as it eliminates the requirement for binders in creating composite electrodes, given that MnO 2 can be directly deposited onto the LIG electrodes. The assembled all-Flexible Supercapacitor (FSC), featuring unique LIG-MnO 2 composite electrodes, showcased a remarkable areal capacitance of 66.5 mF cm−2 at 5 mV s−1 scan rate. The device also exhibited a very high areal energy density (2.3 mWh cm−2) and power density (19.7 mW cm−2) at 0.2 mA cm−2 current density. Also, 82 % capacitance retention was observed at the end of 2000 cycles and the device also exhibited a good flexibility during bending tests, as evidenced by an 80 % capacitance retention after 100 bending cycles. [ABSTRACT FROM AUTHOR]

• MnO 2 /CNF/Ag nanofabric electrodes are developed for flexible supercapacitors. • The brittle issue in the CNF electrode is greatly improved by an Ag incorporation. • The optimized MnO 2 /CNF/Ag electrode has a specific capacitance of 184 F/g at 1 A/g. • An energy density of 16.3 Wh/kg and a power density of 400 W/kg was achieved. • A capacitance retention rate of 87 % was demonstrated when subjected to bending. Flexible supercapacitors are gaining increasing popularity due to their potential in powering portable, wearable, and lightweight electronic devices. In this study, we have successfully developed a high-performance flexible electrode for quasi-solid-state supercapacitors by incorporating Ag into carbon nanofibers (CNF) through electrospinning, and growing MnO 2 as an active material on the electrode using an in-situ redox method. The Ag and MnO 2 co-decorated CNF electrode offers several advantages over conventional CNF electrodes, including an enlarged reaction area, higher charge storage capacity, and improved resistance to brittleness issues. Among all the quasi-solid-state supercapacitors tested, the MnO 2 -decorated electrode with an optimized Ag incorporation exhibited the highest specific capacitance of 184 F/g at a current density of 1 A/g, representing a remarkable 17-fold increase compared to the reference CNF electrode. Furthermore, the Ag and MnO 2 co-decorated electrode demonstrated an energy density of 16.3 Wh/kg and a power density of 400 W/kg at the same current density. Notably, the electrode exhibited excellent flexibility, with a capacitance retention rate of 87 % when subjected to bending with a curvature ranging from 5 to 1.25 cm. Our results suggest that the Ag and MnO 2 co-decorated CNF electrode holds great promise for flexible energy storage applications. [Display omitted] [ABSTRACT FROM AUTHOR]