For the first time, we report a facile one pot aqueous method for support-free Pd85Pt15 nano-porous structures (NPoS) synthesis from PdMn nano-alloys at ambient conditions. A hierarchical approach was successfully employed through a simple “self-settlement” process with descending amounts of carbon to carbon-free electro-catalysts to improve catalyst utilization and avoid carbon degradation during fuel cell operating conditions. Pd85Pt15 NPoS exhibits enhanced methanol resistive oxygen reduction reaction (ORR) activity owing to the presence of highly active and unique surface PdPt islands compared to HiSPEC Pt/C catalysts. Accelerated durability tests of the support-free PdPt NPoS show enhanced durability in harsh acidic environment (1.0 N H2SO4) compared to HiSPEC Pt/C and DOE 2017–2020 durability target. Preliminary direct methanol fuel cell studies using hierarchically derived Pd85Pt15 NPoS variants were performed at ultra-low Pt content. The effects of carbon content and catalyst layer thickness on fuel cell activities are well discussed.

We report an enhanced power conversion efficiency (PCE) of 11.7% ± 0.2 and a fill factor (FF) of 71% for dye-sensitized solar cells (DSSC) with an active area of 0.16 cm2 after modifying the TiO2photoanode with size-selective (ca. 2 nm) N,F,S-codoped graphene quantum dots (NFS-GQDs) that exhibit a photoluminescence quantum yield (PLQY) of 70%. An upward shift in the Fermi level has been observed, perhaps responsible for the improved performance along with the possibility of preventing the back electron transfer from TiO2. Mott Schottky analysis indicates a shift (52 mV)in the flat band potential, which is directly related to the Voc of the system. Detailed characterization (IPCE, TCSPC etc) indicates the important role of hetero atoms in facilitating the enhanced performance. Thus, our results suggest that the incorporation of size controlled, hetero atom doped GQDs can enhance the efficiency of DSSCs enabling more opto-electronic applications.

Fabrication of quasi solid state dye sensitized solar cell with a stable gel electrolyte employing poly(ethylene oxide) (PEO)-poly(ethylene glycol) (PEG) is reported in this paper. PEO-PEG with either one of alkali iodides (LiI or NaI or KI), 1,2-dimethyl-3-propyl imidazolium iodide (DMPI), 4-tertbutylpyridine (TBP) and iodine in acetonitrile were used for the gel electrolyte preparation. The ionic conductivity and the triiodide diffusion coefficient of the gel electrolytes were measured by Electrochemical Impedance Spectroscopy. The photoconversion efficiency of gel state DSSC with NaI was found to be 5.4% at 100 mW/cm 2 with AM 1.5 Gfilter. When nanocrystalline TiO 2 was used as the filler in the gel electrolyte, the photoconversion efficiency was found to be increased up to 6.3%. The quasi solid state DSSC retained its initial value for 600 hours aging under ambient conditions.