Search

Ethylene (E)-co-norbornene (N) copolymerizations were conducted by using two ansa-metallocenes, isopropyliden(eta(5)-cyclopentadienyl)(eta(5)-indenyl)zirconium dichloride (1) and isopropyliden(eta(5)-3-methylcyclopentadienyl)(eta(5)-fluorenyl)zirconium dichloride (2), activated with dimethylanilinium tetrakis(pentafluorophenyl)borate, in presence of TIBA and variable amounts of Zn(Et)(2) as a potential chain transfer agent (CTA). The study evaluated the effect of CTA on microstructure, molecular weight, chain end group and structural, thermal and mechanical properties of poly(E-co-N)s. The analysis of the data revealed that in all copolymerization reactions with metallocenes 1 and 2 in presence of diethyl zinc chain transfer to zinc alkyl occurs along with the typical chain transfers of E-co-N polymerization. The chain transfer to zinc alkyl is more efficient at low N content in copolymers. The two catalysts show different behavior in copolymerization at high N content: molar masses of copolymers produced by 2 are more affected by CTA concentration, that is, the chain shortening with increasing CTA content is greater in copolymers obtained with catalyst 2. The analysis of mechanical properties revealed that CTA affects the polymer chain structure. An increase of CTA caused a change of ductility, rigidity, and mechanical strength; chains produced in presence of Zn(Et)(2) are, at least in part, characterized by segments produced as a result of exchange between different metal centers, possibly jointed through ethylene units.

The correlations between the thermal behavior and the crystal morphology of isotactic propene-pentene copolymers were studied through wide-angle (WAXS) and small-angle (SAXS) X-ray diffraction. Copolymers with pentene concentration lower than 11 mol% crystallize in the α form of isotactic polypropylene (iPP) and a concomitant decrease of melting temperature and of the thickness of crystalline lamellae with increasing pentene concentration has been observed. At higher pentene concentrations the trigonal form of iPP crystallizes and a neat increase crystalline lamellar thickness and of the long period, with a slower decrease of melting temperature and crystallinity have been observed. These results have been treated in the general framework of copolymer crystallization theories, using a method proposed by Crist and correlated with the different level of inclusion of pentene co-units in the crystals of α and trigonal forms. For copolymers with pentene concentration lower than 11 mol% pentene co-units are in part incorporated in the crystals of α form. For higher pentene concentrations the decrease of melting temperature coupled with the increase of lamellae thickness with increasing comonomer content is the hallmark of the almost total inclusion of pentene co-units in the crystals of the trigonal form.

Binary blends of samples of syndiotactic polypropylene of different stereoregularity have been prepared by mixing a more stereoregular and crystalline sample sPP1 having [ rrrr ] = 78%, with low stereoregular and poorly crystalline samples sam PP1 and sam PP2 having [ rrrr ] = 54.6 and 45.8%, respectively, and a nearly atactic fully amorphous sample am PP1 with [ rrrr ] = 26.5%. The blends show separate melting of the two components with the more stereoregular component sPP1 melting at high temperature and the poorly syndiotactic component melting at lower temperature. Crystals of sPP1 are formed by cooling from the melt whereas more defective crystals of sam PP1 and sam PP2 are formed by cold crystallization during aging at room temperature. The presence of the strereoirregular component disturbs the melt crystallization of the stereoregular component sPP1 and depression of the crystallization and melting temperatures of sPP1 in the blends is observed. On the other hand, the cold crystallization at room temperature of the irregular component is accelerated and favored by the presence of the more stereoregular component sPP1, whose crystals act as crystallization nuclei. All data indicate interactions between the components in the melt and amorphous state, compatible with a good degree of mixing.

A method is developed for rapid preparation of titania substrates using a sol–gel preparation route in combination with an amphiphilic block copolymer (BCP) template, acting as structure directing agent. The method consists in performing the spin coating of an initial solutions of BCP and titania species in a controlled atmosphere using a flux of solvent vapors (Rapid-Flux-Solvent-Atmosphere, RFSA method). The method is demonstrated in the case of thin films of polystyrene-b-poly(oxyethylene) BCP (PS-PEO) with cylindrical morphology of PEO domains in the PS matrix, characterized by the selective inclusion of titanium species inside the PEO cylinders. Upon removal of the organic matrix by heat treatment at 600 °C, titania substrates of different morphology are obtained depending on the concentration of titania precursor and processing conditions. The method allows preventing the negative effect of hydrolysis and condensation reactions of Ti species and titania substrates with morphology reminiscent of that one achieved in the hybrid nanostructured thin films are obtained. The RFSA method is simple, direct, and it is of particular interest for systems that require a short processing time to eliminate the solvent and to obtain regular nanostructured thin-films over large area. Merit figures such as the degree of hexagonal order and the degree of coverage of the surface with titania motifs are identified to characterize the hybrid composites and titania substrates.