Search

The development of new biomaterials for musculoskeletal tissue repair is currently an important branch in biomedicine research. The approach presented here is centered around the development of a prototypic synthetic glycerogel scaffold for bone regeneration, which simultaneously features therapeutic activity. The main novelty of this work lies in the combination of an open meso and macroporous nanocrystalline cellulose (NCC)-based glycerogel with a fully biocompatible microporous bioMOF system (CaSyr-1) composed of calcium ions and syringic acid. The bioMOF framework is further impregnated with a third bioactive component, i.e., ibuprofen (ibu), to generate a multifold bioactive system. The integrated CaSyr-1(ibu) serves as a reservoir for bioactive compounds delivery, while the NCC scaffold is the proposed matrix for cell ingrowth, proliferation and differentiation. The measured drug delivery profiles, studied in a phosphate-buffered saline solution at 310 K, indicate that the bioactive components are released concurrently with bioMOF dissolution after ca. 30 min following a pseudo-first-order kinetic model. Furthermore, according to the semi-empirical Korsmeyer-Peppas kinetic model, this release is governed by a case-II mechanism, suggesting that the molecular transport is influenced by the relaxation of the NCC matrix. Preliminary in vitro results denote that the initial high concentration of glycerol in the NCC scaffold can be toxic in direct contact with human osteoblasts (HObs). However, when the excess of glycerol is diluted in the system (after the second day of the experiment), the direct and indirect assays confirm full biocompatibility and suitability for HOb proliferation.

Lightweight materials that combine high mechanical strength, insulation, and fire resistance are of great interest to many industries. This work explores the properties of environmentally friendly alginate aerogel composites as potential sustainable alternatives to petroleum-based materials. This study analyzes the effects of two additives (tannic acid and montmorillonite clay), the orientation that results during casting, and the crosslinking of the biopolymer with glutaraldehyde on the properties of the aerogel composites. The prepared aerogels exhibited high porosities between 90% and 97% and densities in the range of 0.059–0.191 g/cm3. Crosslinking increased the density and resulted in excellent performance under loading conditions. In combination with axial orientation, Young’s modulus and yield strength reached values as high as 305 MPa·cm3/g and 7 MPa·cm3/g, respectively. Moreover, the alginate-based aerogels exhibited very low thermal conductivities, ranging from 0.038 W/m·K to 0.053 W/m·K. Compared to pristine alginate, the aerogel composites’ thermal degradation rate decreased substantially, enhancing thermal stability. Although glutaraldehyde promoted combustion, the non-crosslinked aerogel composites demonstrated high fire resistance. No flame was observed in these samples under cone calorimeter radiation, and a minuscule peak of heat release of 21 kW/m2 was emitted as a result of their highly efficient graphitization and fire suppression. The combination of properties of these bio-based aerogels demonstrates their potential as substituents for their fossil-based counterparts.

With the commitment to reducing environmental impact, bio-based and biodegradable aerogels may be one approach when looking for greener solutions with similar attributes to current foam-like materials. This study aimed to enhance the mechanical, thermal, and flame-retardant behavior of poly(vinyl alcohol) (PVA) aerogels by adding sodium alginate (SA) and tannic acid (TA). Aerogels were obtained by freeze-drying and post-ion crosslinking through calcium chloride (CaCl2) and boric acid (H3BO3) solutions. The incorporation of TA and SA enhanced the PVA aerogel’s mechanical properties, as shown by their high compressive specific moduli, reaching up to a six-fold increase after crosslinking and drying. The PVA/TA/SA aerogels presented a thermal conductivity of 0.043 to 0.046 W/m·K, while crosslinked ones showed higher values (0.049 to 0.060 W/m·K). Under TGA pyrolytic conditions, char layer formation reduced the thermal degradation rate of samples. After crosslinking, a seven-fold decrease in the thermal degradation rate was observed, confirming the high thermal stability of the formed foams. Regarding flammability, aerogels were tested through cone calorimetry. PVA/TA/SA aerogels showed a significant drop in the main parameters, such as the heat release rate (HRR) and the fire growth (FIGRA). The ion crosslinking resulted in a further reduction, confirming the improvement in the fire resistance of the modified compositions.

A series of low density, highly porous clay/poly(vinyl alcohol) composite aerogels, incorporating ammonium alginate, were fabricated via a convenient and eco-friendly freeze drying method. It is significant to understand rheological properties of precursor gels because they directly affect the form of aerogels and their processing behaviors. The introduction of ammonium alginate impacted the rheological properties of colloidal gels and improved the mechanical performance of the subject aerogels. The specific compositions and processing conditions applied to those colloidal gel systems brought about different aerogel morphologies, which in turn translated into the observed mechanical properties. The bridge between gel rheologies and aerogel structures are established in the present work.