With the methods of compound-melting and high-temperature molding, PC/YAG:Ce fluorescent resin pieces were prepared. The transmittance of the prepared PC/YAG:Ce fluorescent resin in 500~800 nm reaches approximately 65% (0.71 mm thick, double sides polished). The fluorescent resin was characterized by XRD, SEM and PL. The X-ray diffraction (XRD) patterns demonstrated that the fluorescent resin was pure Y3Al5O12 phase. The scanning electron microscopy (SEM) images showed that YAG phosphor was distributed evenly in the fluorescent resin. The excitation spectra had a weak peak at 342 nm and a strong band at 448 nm. The broad emission peaks at about 532 nm can be attributed to 5d--4f transition of Ce3+ ions. Decay curves for the fluorescence of PC/YAG:Ce fluorescent resin show that the lifetime of the fluorescent resin was 61.5 ns. The luminous efficacy of the white LED packaged by the fluorescent resin and blue LED chip was 81.12 lm · W(-1) at 100 mA. All results above of PC/YAG:Ce fluorescent resin indicate a promising fluorescent material for white LEDs.

High-purity ultrafine MgAl2O4 powder was synthesized by metal-alkoxide method and calcining for 2-4 h. And then MgAl2O4/Ce:YAG transparent ceramics were fabricated by hot-pressed sintering and hot isostatic pressed sintering technique with YAG:Ce powder and MgAl2O4 powder. The transparent ceramics were characterized by XRD, SEM, EDS and fluorescence spectrometer, respectively. The results show that the crystal phase of the transparent ceramic was composed of MgAl2O4 and YAG,and the YAG phase dispersed well in the matrix of MgAl2O4. The excitation spectra had a weak band at 345 nm and a strong band at 475 nm. The broad emission peaks at about 533 nm were attributed to 5d--4f transition of Ce3+ ions. Decay curves for the fluorescence of MgAl2O4/Ce:YAG transparent ceramic test show that the lifetime of the Ce:YAG glass ceramic was 59.74 ns. All results show that MgAl2O4/Ce:YAG transparent ceramic may be a promising fluorescent material for white LED applications.