Search

In this work, the combined effects of anion substitution (with Br− and I−) and SiO2 addition on the Li-ion conductivity in LiBH4 have been investigated. Hexagonal solid solutions with different compositions, h-Li(BH4)1−α(X)α (X = Br, I), were prepared by ball milling and fully characterized. The most conductive composition for each system was then mixed with different amounts of SiO2 nanoparticles. If the amount of added complex hydride fully fills the original pore volume of the added silica, in both LiBH4-LiBr/SiO2 and LiBH4-LiI/SiO2 systems, the Li-ion conductivity was further increased compared to the h-Li(BH4)1−α(X)α solid solutions alone. The use of LiBH4-LiX instead of LiBH4 in composites with SiO2 enabled the development of an optimal conductive pathway for the Li ions, since the h-Li(BH4)1−α(X)α possesses a higher conductivity than LiBH4. In fact, the Li conductivity of the silica containing h-Li(BH4)1−α(X)α is higher than the maximum reached in LiBH4-SiO2 alone. Therefore, a synergetic effect of combining halogenation and interface engineering is demonstrated in this work. [ABSTRACT FROM AUTHOR]

In this work, the combined effects of anion substitution (with Br− and I−) and SiO2 addition on the Li-ion conductivity in LiBH4 have been investigated. Hexagonal solid solutions with different compositions, h-Li(BH4)1−α(X)α (X = Br, I), were prepared by ball milling and fully characterized. The most conductive composition for each system was then mixed with different amounts of SiO2 nanoparticles. If the amount of added complex hydride fully fills the original pore volume of the added silica, in both LiBH4-LiBr/SiO2 and LiBH4-LiI/SiO2 systems, the Li-ion conductivity was further increased compared to the h-Li(BH4)1−α(X)α solid solutions alone. The use of LiBH4-LiX instead of LiBH4 in composites with SiO2 enabled the development of an optimal conductive pathway for the Li ions, since the h-Li(BH4)1−α(X)α possesses a higher conductivity than LiBH4. In fact, the Li conductivity of the silica containing h-Li(BH4)1−α(X)α is higher than the maximum reached in LiBH4-SiO2 alone. Therefore, a synergetic effect of combining halogenation and interface engineering is demonstrated in this work.

In this study, we analyze and compare the physical and electrochemical properties of an all solid-state cell utilizing LiBH4 as the electrolyte and aluminum as the active anode material. The system was characterized by galvanostatic lithiation/delithiation, cyclic voltammetry (CV), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS), Raman spectroscopy, electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM). Constant current cycling demonstrated that the aluminum anode can be reversibly lithiated over multiple cycles utilizing a solid-state electrolyte. An initial capacity of 895 mAh/g was observed and is close to the theoretical capacity of aluminum. Cyclic voltammetry of the cell was consistent with the constant current cycling data and showed that the reversible lithiation/delithiation of aluminum occurs at 0.32 V and 0.38 V (vs. Li+/Li) respectively. XRD of the aluminum anode in the initial and lithiated state clearly showed the formation of a LiAl (1:1) alloy. SEM-EDS was utilized to examine the morphological changes that occur within the electrode during cycling. This work is the first example of reversible lithiation of aluminum in a solid-state cell and further emphasizes the robust nature of the LiBH4 electrolyte. This demonstrates the possibility of utilizing other high capacity anode materials with a LiBH4 based solid electrolyte in all-solid-state batteries. [ABSTRACT FROM AUTHOR]

In this study, we analyze and compare the physical and electrochemical properties of an all solid-state cell utilizing LiBH4 as the electrolyte and aluminum as the active anode material. The system was characterized by galvanostatic lithiation/delithiation, cyclic voltammetry (CV), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS), Raman spectroscopy, electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM). Constant current cycling demonstrated that the aluminum anode can be reversibly lithiated over multiple cycles utilizing a solid-state electrolyte. An initial capacity of 895 mAh/g was observed and is close to the theoretical capacity of aluminum. Cyclic voltammetry of the cell was consistent with the constant current cycling data and showed that the reversible lithiation/delithiation of aluminum occurs at 0.32 V and 0.38 V (vs. Li+/Li) respectively. XRD of the aluminum anode in the initial and lithiated state clearly showed the formation of a LiAl (1:1) alloy. SEM-EDS was utilized to examine the morphological changes that occur within the electrode during cycling. This work is the first example of reversible lithiation of aluminum in a solid-state cell and further emphasizes the robust nature of the LiBH4 electrolyte. This demonstrates the possibility of utilizing other high capacity anode materials with a LiBH4 based solid electrolyte in all-solid-state batteries.