In view of the lack of conformal, load‐bearing, light‐weight, and high temperature‐resistant integrated wave‐absorbing composites suitable for extremely complex conditions, the gel‐casting process was successfully applied to porous Si3N4 wave‐absorbing composites in this work. A universal low‐slurry for gel casting was prepared by using two dispersants acting together (tetramethylammonium hydroxide solution and sodium lauryl sulfate), which ensured the smooth completion of the gel casting process. Combining the thermogravimetric and differential thermal gravity curves of the composite green body, reasonable parameters of the rubber discharge process are given to avoid the problem of the green body swelling and cracking. The porous TiC/Si3N4 composites were successfully prepared by holding them at 1650°C for 3 h. The bending strength, density, minimum reflection loss, absorption bandwidth, and matched thickness in the P‐band of the composites with 30 wt.% TiC addition were 54.08 ± 3.02 MPa, 1.906 g/cm3, ‐37.75 dB, 1.9 GHz, and 4.1 mm, respectively. The electromagnetic wave loss mechanisms of the composites are a combination of conductivity loss, multiple reflections and scattering, interfacial polarization, and defect polarization. [ABSTRACT FROM AUTHOR]

The boron nitride nanosheets (BNNSs)/aluminum nitride (AlN) composites were prepared by hot press sintering at 1600°C. The microstructure, mechanical properties, and thermal conductivity of the samples were measured, and the effect of adding BNNSs to AlN ceramics on the properties was studied. It is found that the addition of BNNSs can effectively improve the mechanical properties of AlN. When the additional amount is 1 wt%, the bending strength of the sample reaches the maximum value of 456.6 MPa, which is 23.1% higher than that of the AlN sample without BNNSs. The fracture toughness of the sample is 4.47 MPa m1/2, a 68.7% improvement over the sample without BNNSs. The composites obtained in the experiment have brilliant mechanical properties. [ABSTRACT FROM AUTHOR]