Failure mechanism of complex profile component is always different from that of conventional plate counterpart due to the coupling effect of material and structure. In this work, the low-velocity impact (LVI) and compression after impact (CAI) behaviors of Ω-shape hybrid carbon/Kevlar 3 D orthogonal woven (3DOW) composite made for vehicle B-pillar were comprehensively studied by mechanical tests and mesoscale finite element (FE) analysis at component level, high-speed infrared (IR) thermal imaging, acoustic emission (AE) detection, and microscopic damage morphology characterization. It is found that a through-thickness stress concentration ring leads to high stress state and damage zone penetrating from the impact side to non-impact side along the ring path instead of at the lowest impactor position. The slope effect can not only help the stress conduction downward, but also inhibit the damage propagation from the impact side to the slope. Impact-induced cracks are concentrated around the R corners and extended along the axial direction of the specimen, forming the strip-shaped damage concentration zone along the upper eave of the slope. The Progressive Top-Down Crushing (PTDC) mode of compression after impact is due to the complex deformation process of each yarn such as squeezing, folding and eversion in the crushing process from the top of specimen. And the Middle Indentation Fracture (MIF) mode is the result of bending instability and abrupt fracture. This work presents a reference significance for the further development of composite strengthening components in vehicle bodywork. [ABSTRACT FROM AUTHOR]

In this study, the performance of braided composite tubes under low-velocity transverse impact loading at mid-span was investigated using both numerical and experimental methods. Three types of braided composite tubes with different braiding angles (30°, 45°, and 60°) were manufactured. The transverse punch behavior of the tubes was examined on a low-velocity imspact test bench. A meso-level finite element model of the composite tube was also established for identifying the damage initiation and development. The numerical results showed a good correlation with the experimental data. The mechanical response including force–time histories, force–displacement histories, and fracture morphologies was compared between three types of composite tubes for analyzing the influence of braiding angle on the impact response and failure mode. Although suffering from the low bending stiffness depends on fiber volume fraction at initial impact stage, the braided tube with 30° angle engaged more portion to resist impact loading in subsequent process and thus presented higher peak loading than the one with large angle. In addition, there are distinct different failure modes between composite tubes with various braiding angles. Shear yarn breakage underneath the punch was prone to occur in 30° sample because the braiding yarn was closer to the axial direction of tube. In contrast, the resin was deboned severely from the braiding yarn and then the braiding yarn exhibits plastic deformation in 60° sample due to the stress concentration caused by the large braiding angle. [ABSTRACT FROM AUTHOR]