Search

• Anodic oxidation coating's cracking causes a severe substrate stress concentration. • Sealing weakens anodic oxidation coating's cracking resistance during fatigue tests. • Prior shot peening enhances the fatigue property of anodic oxidation coated specimen. In this study, the effects of sealing and prior shot peening treatments on the fatigue behavior of the sulphuric acid anodic oxidation coated 6082-T6 aluminium alloy were investigated. Experimental results indicate that the preferential fracture of anodic oxidation coatings due to its higher brittleness and lower fracture toughness as well as the stress concentration of near-interface substrate caused by the interface cyclic dislocation accumulation could cause the fatigue failure of anodic oxidation coated specimens. Consequently, the fatigue property of anodic oxidation coated specimens notably decreases compared to as-machined specimens, with a decrease of 26.7 % in the fatigue limit corresponding to 2 × 107 fatigue cycles. Additionally, the sealing treatment introduces numerous cracks that penetrate the coating entirely, diminishing the coating's resistance to cracking under fatigue loading; this alteration changes the fatigue failure mechanism of anodic oxidation coated specimens, ultimately resulting in a decrease of 15.5 % in the fatigue limit of anodic oxidation coated specimens. Despite exacerbating the surface integrity and increasing the surface roughness of anodic oxidation coated specimens, the prior shot peening treatment increases the fatigue limit of anodic oxidation coated specimens by 82.8 % since the affecting layer beneath the interface plays a crucial role in inhibiting the further propagation of coating cracks into the substrate as well as the crack propagation in the substrate beneath the interface. [ABSTRACT FROM AUTHOR]

• Prior shot peening improves the CF limit of AO coated aluminum alloy by 50 %. • AO specimens exhibit different CF failure modes under low and high applied stress. • Substrate residual stress and microstructure affect the CF crack propagating path. • Substrate residual stress relaxes in distinct mode under low and high applied stress. Plain (anodic oxidation) and composite (prior shot peening + anodic oxidation) coatings were prepared to investigate their effects on the corrosion-fatigue (CF) property of 6082-T6 aluminium alloy in a 3.5 wt% NaCl aqueous solution. The results indicate that plain coated specimens exhibited similar CF properties to as-machined specimens at low applied stresses. However, under high applied stresses, the plain coating led to a preferential fracture and was unable to effectively prevent corrosion medium. Hence, the CF property of plain coated specimens was found to be inferior to as-machined specimens at high applied stresses. The synergetic effect of substrate residual stress and microstructure beneath the coating-substrate interface reduced the crack propagating rate in the initial stage by deflecting the crack at the grain boundary. Therefore, the CF property of composite coated specimens improved as a whole when compared with as-machined and plain coated specimens. Besides, under low applied stresses, the near-interface substrate residual stress of composite coated specimens occurred the relaxation due to the substrate crack propagation, while under high applied stresses, this was due to the synergetic effect of materials' local cyclic yield and plastic flow, as well as the substrate crack propagation. [ABSTRACT FROM AUTHOR]