Search

Fast heat and mass delivery with high cycling stability of the core component, hydrogen storage bed, in SDS are essential for the operation of the future tritium factory in ITER project. However, the aforementioned properties are still perplexing in large-capacity ZrCo bed, especially for that with secondary containment structure required by the actual tritium operation in the future. Herein, the performance including heating, cycling and cooling with two different size ZrCo beds (loading of ZrCo are 200 g and 2000 g respectively) were systematically studied. The experimental data shows that the maximum heating ability of the middle-size/full-scale storage bed are both about 10 °C/min, and the maximum hydrogen absorption capacity of these ZrCo beds are 44.6 L/405.5 L, respectively. Besides, hydrogen pressure and hydrogen retention during the following desorption can affect the cycling performance of the ZrCo bed. The use of transfer pump can reduce the pressure of the bed during the hydrogen desorption process (operated at 500 °C), which inhibits the disproportionation reaction of the ZrCo alloy. However, the degree of hydrogen pressure reduction in two the types of ZrCo bed are different. As a result, the cycling capacity of the middle-size bed (93.4%, lower hydrogen pressure) is higher than the full-scale bed (68.7%, higher hydrogen pressure) after 10 cycles. When the transfer pump was not used and operated at lower temperature (350 °C), the beds cannot release hydrogen completely, and partial hydrogen atoms are retained in the ZrCo alloy. The middle-size bed still maintains a hydrogen storage capacity of 94.5% after 10 cycles, while 75.9% of the hydrogen storage capacity remained for the full-scale bed. Therefore, the increase of hydrogen surplus in ZrCo alloy is helpful to improve its cycling stability. At last, the cooling performances of the beds under 10 different cooling methods were studied. Among the cooling methods, the best cooling rate was achieved by filling nitrogen in the secondary containment cavity and flowing water passing through the cooling circuit of the bed. This work will provide a crucial reference for the design and optimization of the subsequent operation technology of SDS in ITER. • Thin double-layered annulus ZrCo bed with secondary containment cavity is manufactured. • Real-time pumping transfer helps to improve the circulation stability of the ZrCo bed. • Keep remaining H in the ZrCo is benefits to improve its cycling stability. [ABSTRACT FROM AUTHOR]

Cycling stability of ZrCo–H system is extremely important for the long-term operation of the storage and delivery system (SDS) in ITER. Herein, the optimal cycling operation parameters were systematically investigated. It indicates that various parameters, such as hydrogen pressure, temperature, composition, and stoichiometric ratio of H atoms, will all affect the cycling performance of the ZrCo–H system significantly. The decline rate of the hydrogen capacity of the ZrCo–H system is positively correlated with the hydrogen pressure. The experimental result shows that 54% of hydrogen capacity decreases under 28.1 kPa hydrogen pressure, while 30% of attenuation is obtained when the pressure is decreased to 8.1 kPa after 14 cycles. In terms of temperature, the lowest cycling attenuation can be maintained at about 25% after 14 cycles when the dehydrogenation temperature at 550 °C. The effects of doping elements, Hf and Ti, on the cycling stability of ZrCo–H system are also compared. The Zr 0.8 Ti 0.2 Co sample exhibits higher cycling capacity than ZrCo and Zr 0.8 Hf 0.2 Co samples. The extremely excellent behavior can be achieved when all ZrCo alloys are continuously evacuated during the hydrogen release process, and the attenuation of only 1.1% is observed for Zr 0.8 Ti 0.2 Co after 15 cycles. Besides, the cycling attenuation is related to residual stoichiometric ratio of H atoms in ZrCo alloy during the cycling test. When the residual H atoms proportion exceeds 1 in ZrCo during dehydrogenation, hydrogen cycling capacity hardly fades. The XRD results reveal that the disproportionation of ZrCo is directly associated with the cycling degradation, yielding the more stable products of ZrCo 2 and ZrH 2 , However, the disproportionation can be avoided during the cycling process by controlling the stoichiometric ratio of H atoms remained in ZrCo above 1. This study demonstrates that the cycling performance of ZrCo can be substantially improved when the operation parameters are properly adjusted, which provides a significant important reference for durable running of SDS in ITER. • Relationship between cyclic property and operation parameters of ZrCo is revealed. • Residual H ratio above 1 in ZrCo after desorption indeed improves cyclic stability. • Cycling capacity retention ratio maintains at ~99% for the optimized parameter. [ABSTRACT FROM AUTHOR]