Impedance measurements were made on technological important ferroelectric ceramics, namely PZT and La0.75 Bi3.25Ti3O12 (BLT), in the frequency range of 100 Hz to 1 MHz, from room temperature to 500°C. Combined impedance and modulus spectroscopic analysis along with the detailed conductivity (ac and dc) data was used to understand the heterogeneity of the ceramics and the results were corroborated with temperature coefficient of dc-conductivity (figure of merit) data for the further understanding. AC-conductivity plots against frequency at different temperatures for PZT and BLT suggest the response of obeying Jonscher's and modified Jonscher's law, respectively. [ABSTRACT FROM AUTHOR]

A and B site modified new bismuth layered structure ferroelectric ceramics of the Aurivillius family were prepared by the solid-state route. Impedance measurements were performed on these samples to understand the relaxation effects in the frequency range of 100 Hz to 1 MHz. From the detailed impedance and modulus spectroscopic analysis, it is found that the aliovalent modified B-site enhances the relaxor-like nature, compared to A-site substitution. These results were corroborated with ac-conductivity transport analysis. In this connection, a defect formula is also proposed. The results are discussed. [ABSTRACT FROM AUTHOR]

The Ac conductivity measurements of polycrystalline materials of rare earth substituted Bi[sub 6]Fe[sub 2]Ti[sub 3]O[sub 18] compound at different frequencies (1 kHz-1 MHz) and temperatures (30550°C) are reported. The dc conductivity, ionic hoping rate as well as carrier densities have been extracted from the ac conductivity data. The results show that hoping mechanism dominates at lower temperature. The results are discussed. [ABSTRACT FROM AUTHOR]

GdBi[sub 5]Fe[sub 2]Ti[sub 3]O[sub 18] (GBFT), a compound of Aurivillius family, was prepared by solid state reaction method. Complex impedance measurement was made on these samples from room temperature to 500°C in the frequency range of 1 kHz-1 MHz. Cole-Cole plots were found to become very broad near 400°C. Dielectric and dc conductivity measurements were made on these samples. The results are analysed to understand the conductivity mechanism. [ABSTRACT FROM AUTHOR]