This study evaluated the mid-term (12-month) biomechanical, biocompatibility, and biological performance of additive-manufactured bioabsorbable iron-based interference screws (ISs). Two bioabsorbable iron IS types—manufactured using pure iron powder (iron_IS) and using pure iron powder with 0.2 wt% tricalcium phosphate (TCP_IS)—were compared with conventional metallic IS (control) using in vitro biocompatibility and degradation analyses and an in vivo animal study. The in vitro ultimate failure strength was significantly higher for iron_IS and TCP_IS than for control ISs at 3 months post-operatively; however, the difference between groups were nonsignificant thereafter. Moreover, at 3 months after implantation, iron_IS and TCP_IS increased bone volume fraction, bone surface area fraction, and percent intersection surface; the changes thereafter were nonsignificant. Iron_IS and TCP_IS demonstrated degradation over time with increased implant surface, decreased implant volume, and structure thickness; nevertheless, the analyses of visceral organs and biochemistry demonstrated normal results, except for time-dependent iron deposition in the spleen. Therefore, compared with conventional ISs, bioabsorbable iron-based ISs exhibit higher initial mechanical strength. Although iron-based ISs demonstrate high biocompatibility 12 months after implantation, their corrosive iron products may accumulate in the spleen. Because they demonstrate mechanical superiority along with considerable absorption capability after implantation, iron-based ISs may have potential applications in implantable medical-device development in the future. [ABSTRACT FROM AUTHOR]

This study evaluated the biocompatibility and biological performance of novel additive-manufactured bioabsorbable iron-based porous suture anchors (iron_SAs). Two types of bioabsorbable iron_SAs, with double- and triple-helical structures (iron_SA_2_helix and iron_SA_3_helix, respectively), were compared with the synthetic polymer-based bioabsorbable suture anchor (polymer_SAs). An in vitro mechanical test, MTT assay, and scanning electron microscope (SEM) analysis were performed. An in vivo animal study was also performed. The three types of suture anchors were randomly implanted in the outer cortex of the lateral femoral condyle. The ultimate in vitro pullout strength of the iron_SA_3_helix group was significantly higher than the iron_SA_2_helix and polymer_SA groups. The MTT assay findings demonstrated no significant cytotoxicity, and the SEM analysis showed cells attachment on implant surface. The ultimate failure load of the iron_SA_3_helix group was significantly higher than that of the polymer_SA group. The micro-CT analysis indicated the iron_SA_3_helix group showed a higher bone volume fraction (BV/TV) after surgery. Moreover, both iron SAs underwent degradation with time. Iron_SAs with triple-helical threads and a porous structure demonstrated better mechanical strength and high biocompatibility after short-term implantation. The combined advantages of the mechanical superiority of the iron metal and the possibility of absorption after implantation make the iron_SA a suitable candidate for further development. [ABSTRACT FROM AUTHOR]