Asphalt in damp-heat and saline-alkali areas is prone to damage, which resulting in fatigue failure of the mixture. However, the aging damage of asphalt in these areas has not been paid enough attention, and there is a lack of effective evaluation method for asphalt's fatigue performance. In this paper, the base asphalt and SBS-modified asphalt were immersed in several solutions (water, NaCl and Na2CO3) to simulate aging conditions and the frequency sweep test was employed to determine the viscoelasticity properties of the asphalt. And the fatigue properties of the asphalt were analysed by the simplified viscoelastic continuum damage model. The microstructural and chemical evolution of asphalt was investigated by SEM, FTIR, the pH value and total organic carbon tests. After being immersed, the anti-deformation properties of two asphalts were strengthened. The solution erosion led to an increased loss rate of the integrity factor C*, and resulting in weakened fatigue properties of asphalt. The oxygen-containing functional group gradually increased with the extension of immersion. There were chemical interactions in addition to physical interface disruption during the immersion process. Moreover, the influence of Na2CO3 solution on asphalt ranked first due to the highest molar concentration of Na+ and the OH− produced by hydrolysis of ${\rm CO}_3^{2-}$ C O 3 2 − . [ABSTRACT FROM AUTHOR]

High-temperature rutting is one of the common forms of pavement damage. To further improve the high temperature performance of crumb rubber modified asphalt (CRMA) pavement, heavy calcium carbonate (HCC) modified by sodium pyrophosphate was combined with crumb rubber to prepare composite modified asphalt binder. Their physical properties, viscoelastic properties and chemical composition were investigated through conventional physical tests, DSR, FTIR and fluorescence microscopes. The results show that with the increase of HCC content, the mixing and compaction temperatures of composite modified asphalt binders continued to increase. Further, the high temperature performance and fatigue resistance of binders were better than the original CRMA, due to the enhanced lipophilicity of HCC after modification. It can be found from the FTIR spectrum that the addition of HCC only existed in physical action. However, excessive HCC would cause agglomeration of the asphalt matrix, so the optimum dosage of HCC was determined to be 4%. [ABSTRACT FROM AUTHOR]