Purpose: To investigate the effect of Colloidal Platinum Nanoparticles (CPN) on the bond strength between dentin and 4-META/MMA-TBB resin using different concentrations of CPN. Materials and Methods: Twenty-five extracted human third molars were stored in 0.5% chloramine T. The occlusal dentin slices were prepared by grinding occlusal surfaces of each tooth and polishing with 600-grit silicon carbide paper under running water. One control and four experimental groups (2 specimens per group) were used as follows: a) dentin surfaces treated with 10-3 solution, followed by rinsing with water and subsequently an acrylic rod bonded with hand-mixed 4META/MMA-TBB resin (Super-Bond C&B, Sun Medical) (control); b) dentin surfaces treated with 10-3 etching solution, followed by rinsing with water and application of CPN (100% or 10%) as a primer solution for 60 s and rinsed with water for 20 s, then an acrylic rod bonded with Super-Bond C&B(Etch-CPN [100% or 10%]); c) dentin surfaces treated with CPN (100% or 10%) for 60 s, rinsed with water for 20 s, followed by application of 10-3 solution, then an acrylic rod bonded with Super-Bond C&B (CPN-Etch [100% or 10%]). After storage in 37°C water, specimens were sectioned into beams (cross-sectional area: 1 mm2) for microtensile bond strength testing at a crosshead speed of 1mm/min. The data were analyzed using the Games-Howell method (p < 0.05; n = 15). Results: Etch-CPN (100), CPN-Etch(100) and CPN-Etch (10) showed significantly higher bond strengths compared to the control. When using 10% CPN, the highest bond strength was demonstrated. The bond strength of 4META/MMA-TBB resin was approximately doubled by CPN application. Conclusion: The results of this study showed that higher bond strengths are obtained when treating dentin with a lower concentration of CPN. Further evaluation to optimize conditions such as the application time and rinsing time are required. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the effects of 1) wall grinding status, 2) thermal stress, and 3) time of polishing on sealing performance of two one-step bonding systems in cervical cavities. Materials and Methods: Semicircular cavities with dimensions of 3 × 3 × 1.5 mm were prepared along the CEJ of extracted human premolars. In experiment 1, the cavity walls were additionally ground with round steel diamond burs (regularly ground) or finished with superfine diamond burs. The cavities were treated with AQ Bond (AQ) or One-up Bond F (OB) and filled with a resin composite. Then thermocycling (5°C to 55°C, 1000 ×) was performed. In experiment 2, the regularly ground cavities were used. After restoration, the teeth were subjected to thermocycling (1,000 to 5,000 ×). In experiment 3, the restorations in the regularly ground cavities were polished immediately or 24 h after filling. No thermocycling was carried out in this group. All specimens were immersed in a dye solution for 2 h. Microleakage at coronal and apical walls was evaluated on the longitudinal sections of the restorations. Results: For OB, the cavities finished with superfine burs exhibited more microleakage at the coronal wall than the regularly ground cavity (p < 0.05). The leakage at the coronal walls increased with the number of thermal cycles for both systems (p < 0.05). The delayed polishing generated better adaptation at the apical wall of AQ and at the coronal wall of OB (p < 0.05). Conclusion: Grinding status, thermocycling, and time of polishing had influences on the sealing performance of the two one-step adhesive systems. [ABSTRACT FROM AUTHOR]

Purpose: The purpose of this study was to photoelastically evaluate contraction stresses associated with various resin composite build-up procedures for pulpless molars. Materials and Methods: Photoelastic models of endodontically treated mandibular molars were fabricated to simulate a preparation for a full-cast crown. The model configuration included three lateral walls, but no post space. The buildups were made with dual-curing resin composite using the following procedures: 1) bulk dual cure, 2) bulk chemical cure, 3) horizontal two increments, dual cure, and 4) indirect. Five specimens were fabricated for each condition. The stresses developed in the models were recorded photographically in the field of a circular polariscope. Results: The build-up procedures tested generated widely different stress distributions and intensities. The highest stresses were seen with the bulk dual-cure method. The slower polymerization chemical-cure group developed distributions similar to the bulk dual-cure group with a significantly lower fringe order. The two horizontal increments dual-cure techniques developed an individual group of fringes for each layer. Compared with the bulk dual-cure group, stresses around the occlusal margin were reduced by incrementalization, while fringes were more closely spaced at the line angles with a slightly lower fringe order. The indirect method demonstrated the lowest stress which extended over the smallest area. Conclusion: Contraction stress in resin composite buildups varied significantly depending upon the procedures of fabrication. The bulk dual-cure method developed the most severe contraction stresses, while the indirect technique resulted in significantly lower contraction stresses than the other techniques tested. [ABSTRACT FROM AUTHOR]

Purpose: The objective of this work was to evaluate the in vivo long-term durability of bond strength and morphological appearance of interfaces between dentin and two adhesive systems. Materials and Methods: Class V cavities were prepared on the facial surfaces of 6 intact teeth of a monkey, and restored with Unifil Bond/Unifil F and Fuji Bond LC/Clearfil AP-X. One year later, 10 other teeth were restored with the same materials and the monkey was sacrificed after 24 hours. For in vitro examination, 6 more teeth were extracted from the monkey, restored in a similar manner with the two materials, and stored in 37°C water for 1 day. All specimens were subjected to the microtensile bond strength (μTBS) test. The debonded surfaces of specimens were morphologically observed with the FE-SEM. Results: There were no statistically significant differences among the mean μTBS obtained for Unifil Bond/Unifil F under the three conditions (1 day and 1 year in vivo, and 1 day in vitro), and most specimens showed cohesive failure within resin composite (Unifil F). However, FE-SEM observations showed that resinous material within the hybrid layer made by Unifil Bond seemed to increase in porosity after 1 year. For Fuji Bond LC/Clearfil AP-X, μTBS at 1 day in vitro was significantly higher than that at 1 year in vivo, and bond strengths in vivo tended to decrease over time, although a statistically significant difference was not observed. From FE-SEM observations, most specimens showed cohesive failure within the adhesive (Fuji Bond LC). Conclusion: Bond strengths of the two adhesive systems tended to decrease for 1 year in vivo. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the influence of the orientation of dentinal tubules on the bonding performance, microtensile bond strengths (MTBS) to dentin in cervical dentin cavities were measured for three current bonding systems. Materials and Methods: Wedge-shaped cervical cavities (5 x 5 x 3 mm) prepared in extracted human premolars were treated with one of the three adhesive systems, Gluma One Bond, UniFil Bond and Mega Bond in combination with a hybrid-type resin composite. After storage in water for 24 h, the teeth were sectioned longitudinally through the restoration for determination of MTBS, either at the coronal or at the apical wall of the lesion. In an additional group, either the coronal or the apical walls were coated with vaseline prior to adhesive bonding and insertion of the resin composite, and then MTBS was measured. Results: MTBSs (mean ± SD, MPa) to coronal and apical dentin were 35.1 ± 19.1 and 16.4 ± 7.9 for Gluma One Bond, 37.7 ± 11.5 and 18.6 ± 8.6 for UniFil Bond, and 27.0 ± 15.2 and 30.3 ± 17.0 for Mega Bond, respectively. MTBS to the coronal wall was higher than to the apical wall (p < 0 05) with Gluma One Bond and UniFil Bond, whereas no difference was found with Mega Bond. With all three systems, vaseline coating had no effect on the bond strength (p > 0.05), indicating that the wall-to-wall contraction stresses exerted in the noncoated group had no influence on the bond strength generated. Conclusion: In cervical dentin cavities, apart from the individual adhesive's bonding capacity, the dentinal tubular orientation may have an influence on the bond strength. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the microtensile bond strength (µTBS) of eleven contemporary adhesives to dentin, including three one-step self-etch systems, four two-step self-etch systems, three two-step total-etch systems, and one three-step total-etch system. Materials and Methods: Resin composite (Z100) was bonded to flat, mid-coronal dentin from 33 extracted human third molars using the adhesives strictly according to the respective manufacturer's instructions. After storage overnight in 37°C water, the bonded specimens were sectioned Into 3 to 6 slabs of approximately 1 mm thickness and 2.5 mm width. They were then trimmed into an hourglass shape resulting in an Interface area of approximately 1 mm², and subsequently subjected to µTBS testing with a crosshead speed of 1 mm/min. Results: The µTBS varied from 30.0 MPa for the one-step self-etch adhesive Prompt L-Pop 2 (ESPE) to 63.1 MPa for the three-step total-etch adhesive OptiBond FL (Kerr), the latter being the only one that significantly differed from all other µTBS values. Although not significantly different, one-step self-etch adhesives tended to have lower µTBS than two-step self-etch and two-step total-etch adhesives. Specimen failures during sample preparation occurred with Prompt L-Pop 2 (4 pretesting failures out of 17 specimens) and NRC/Prime&Bond NT (7 pretesting failures out of 14 specimens). Conclusion: Adhesives with simplified application procedures, either following a total-etch or self-etch approach, produced lower bond strengths to dentin than a conventional three-step total-etch adhesive. Some concern exists regarding the consistency in bonding effectiveness to dentin of some self-etch adhesives. [ABSTRACT FROM AUTHOR]

Purpose: To compare the microtensile bond strength (MTBS) of two single-step adhesive systems to two types of bur-prepared dentin. Materials and Methods: Using either of two adhesives, the experimental MZ-2000 (MZ) and the commercial One-Up Bond F (OUB), resin composite was bonded to flat buccal and root dentin surfaces of eight extracted human premolars. These surfaces were produced by grinding with either regular-grit or superfine-grit diamond burs in a high-speed handpiece. After storage overnight in 37°C water, the bonded specimens were sectioned into ten slices approximately 0.7 mm thick, perpendicular to the bonded surface. They were then subjected to microtensile testing. The surfaces of the fractured specimens were observed both visually and microscopically to determine the failure mode. In addition, to observe the effect of conditioning, the two types of bur-ground dentin surfaces were conditioned with the adhesives, rinsed with acetone, and observed under SEM. Results: When MZ was bonded to dentin prepared with a regular-grit diamond bur, MTBS was the lowest and failures occurred adhesively at the interface, whereas other groups revealed primarily mixed failures. MZ-conditioned dentin surfaces ground with a regular-grit diamond bur were covered with a residual smear layer. However, the smear layers on the surface of MZ-conditioned dentin ground with a superfine-grit diamond bur and on OUB-conditioned dentin prepared either with a regular-grit or superfine-grit diamond bur were mostly or partially dissolved. Conclusion: Some of the single-step adhesive systems may produce low bond strengths to smear layers created by regular-grit diamond burs. [ABSTRACT FROM AUTHOR]

Purpose: The objective of this study was 10 evaluate the ability of three adhesive systems to seal dentin by measuring the permeability of dentin before and after bonding procedures. Materials and Methods: Thirty-six flat dentin surfaces were prepared from human extracted teeth and connected to a fluid-filled system for permeability measurements The hydraulic conductance of the flat occlusal surface of dentin was measured by the nitration technique. Before and after application of ScotchBond MP Plus, Prime & Bond 2.0. and All-Bond 2. Bonding procedures were followed by P-50 resin composite application. The specimens were then perfused with silver nitrate to permit morphologic localization of microleakage pathways using SEM. Results: The results showed that the best dentin seal was produced By All-Bond 2, followed By Prime & Bond 2.0, and ScotchBond MP Plus. However, none of the three bonding systems tested was able to totally prevent the passage of fluid across the dentin m every specimen. When observed with SEM, each adhesive system exhibited different patterns of leakage. Conclusion: The inability of all three materials to create a perfect seal in vitro raises concerns about the ability of these adhesive systems to provide completely sealed restorations in vivo. However, Because [he current study applied pressure 3 to 6 times higher than physiologically normal, it is likely that the leakage represents a worst-case scenario. [ABSTRACT FROM AUTHOR]

Purpose: To determine if collagen fibrils on the dentin side of failed resin-dentin interfaces undergo mechanical disruption during microtensile bond testing. Materials and Methods: Extracted, caries-free human third molars were divided into four groups. The occlusal enamel was removed, leaving a flat dentin surface for bonding. Resin composite buildups were made after the acid-conditioned dentin was bonded with either Single Bond {Si or One-Step (0}, and using either moist bonding (M) or air drying for 5 s (DJ. After storage in water for 24 h. the teeth were vertically sectioned into an array of 0.9 >■ 0.9 mm resin ccmposite-dentin beams They were stressed to failure using the nontrimming version of the microtensile bond test. Fractured dentin and resln composite sides of representative beams from each group that exhibited adhesive failures under tight microscopy examination were prepared for descanning (SEM) and transmission electron microscopy (TEM). Results: A two-way ANOVA showed that moist bond strengths were significantly higher than those made to dry dentin {M > 0; p < 0.001), but that there was no difference between the adhesive (S vs 0; p = 0.547). SEM analysis showed the presence of loose collagen fibrils within fractured hybrid layers ¡n the dry groups but not in the moist groups. TEM examination of the dry-bonded groups revealed collagen fibrils that wore thinner and exhibited abnormally wide interfibrillar spaces when hybrid layers were intact. Within dry-bonded fractured hybrid layers, broad mechanical disruption zones could be seen, consisting of fibrils that were devoid of cross banding, defibrillation of the subfibrillar architecture, and gross disaggregation into microfibrils. In the moist-bonded groups, only short mechanical disruption zones were found along the torn edges of the collagen fibrils. The rest of the fibrils beyond the fracture site were intact and retained their periodicity. Mechanical testing of demineralized matrices.. [ABSTRACT FROM AUTHOR]

Purpose: The objective of this work was to evaluate the effect of the absence and presence of smear layers on bonds made to dentin using a self-etching primer system, Clearfil SE Bond. Materials and Methods: Dentin surfaces with different smear layer thickness were created from mid-coronal sound dentin in extracted, human third molars. The control group was cryofractured to create a bonding surface that was devoid of a smear layer. The experimental teeth were ground with wet 60-, I8O- or 600-grit SIC paper. They were bonded using SE Bond, followed by resin composite buildups. After 1 day, bonded specimens were sectioned into multiple 1- x 1-mm beams. Microtensile bond strengths were determined and the results analyzed with ANOVA and the Student Neuman Keuls test. Fractographic study of cross sections of failed interfaces from the dentin side of representative beams was performed using both SEM and TEM. Results: SE Bond produced high bond strengths (ca 50 MPa) to both smear layer-free and smear layer-covered dentin. SEM examination was inadequate to define the exact nature of interfacial failures. TEM observations demonstrated a thin (ca 400 to 500 nm) hybrid layer in the fractured dentin and thicker (ca 1 to 4 µm) hybrid layers on smear layer-covered dentin. This included a thick, hybridized smear layer and a thin, underlying true hybrid layer in the intact dentin. Separation of the two hybrid layers was not evident in interfacial failures. Conclusion: Self-etching primers create thin hybrid layers that incorporate the smear layer. This study shows that formation of true hybrid layers occurs irrespective of smear layer thickness and that both hybrid layers may function as a unit during loading without separation. Identification of secondary cracks from TEM fractographic analysis exemplifies the complex reaction to tensile stresses in multilayered joint systems that comprise materials of variable compliance. [ABSTRACT FROM AUTHOR]

Purpose: The objectives of this study were (1) to determine the depth of demineralization into intact dentin using several self-etching primer systems with different pH values, and (2) to evaluate whether hybridization of intact dentin in Clearfil SE Bond may be affected by variation in the thickness of the smear layers. Materials and Methods: Dentin disks were created from mid-coronal dentin in extracted, human third molars. Three self-etching primer systems (Clearfil Liner Bond II, Liner Bond 2V, and SE Bond) were applied separately to these disks to evaluate how deep self-etching systems penetrate through smear layers into intact dentin. Dentin treated with All-Bond 2 using the "no-etch" technique was used as a control group. In the second part of the study, dentin disks with different smear-layer thicknesses were produced. The cryofractured control group was devoid of a smear layer. The experimental teeth were ground with 60-, 180-, or 600-grit SiC paper and bonded using SE Bond. Dentin disks were bonded together and examined with TEM. Results: All-Bond 2 did not etch beyond the smear layer. The three self-etching primers etched beyond the smear layer to form true hybrid layers within intact dentin. This layer was thickest with Liner Bond 2 (ca 1.2 to 1.4 μm), but very thin (0.5 μm) using both Liner Bond 2V and SE Bond. Application of SE Bond to dentin of different surface roughness produced hybridized smear layers of variable thickness. However, the thickness of the underlying true hybrid remained consistent for the four groups (ca 0.4 to 0.5 μm). Conclusion: Self-etching primers create thin hybrid layers that incorporate the smear layer. The suspicion that thick smear layers may interfere with the diffusion of self-etching primers into the underlying intact dentin was not confirmed. [ABSTRACT FROM AUTHOR]

Purpose: The purpose of this review is to describe all of the various modifications of the microtensile bond test in one paper, so that investigators can select the modification that best suits their needs. Methods: The essence of the microtensile test is the division of resin-bonded teeth into slabs between 0.5 and 1.0 mm thick that are then trimmed in such a manner that tensile force will be concentrated on the bonded interface during testing. Among the many advantages of the technique are that each tooth produces multiple specimens. Further, there is no need for a matrix to limit the bonded surface area, since the area is determined by the dimensions of the trimmed specimens. Results: The various modifications of the microtensile test have been used to measure differences in regional bond strength across occlusal dentin, down the external surface of teeth from crown through roots, down the internal surface of root canals from cervical to apical thirds, as well as to compare normal vs caries-affected occlusal dentin and normal vs sclerotic cervical dentin. The technique is ideal for evaluating the long-term durability of resin-hard-tissue bonds. Conclusion: The microtensile test methods offer versatility that cannot he achieved by conventional methods. It is more labor-intensive than conventional testing, but holds great potential for providing insight into the strength of adhesion of restorative materials to clinically relevant sites and substrates. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the long-term microtensile bond strength (µTBS) to dentin, water sorption (WSP) and solubility (WSL), and degree of conversion (DC) of self-adhesive resin composites (SACs)., Materials and Methods: The mid-coronal dentin of human molars was exposed, and teeth were randomly assigned to five groups according to the SACs (n = 10): 1. FIT SA F03 (FIT); 2. Experimental (EXP); 3. Fusio Liquid Dentin (FLD); 4. Vertise Flow (VER); 5. Constic (CON). The µTBS was evaluated after 24 hours (24 h) and 6 months (6 m) storage. A scanning electron microscope examined failure modes and resin-dentin interfaces. The WSP and WSL (n = 5) were evaluated following ISO 4049:2019 specifications, and DC (n = 3) was measured using Raman spectroscopy. The statistical analyses were performed accepting a significance level of p = 0.05., Results: FIT, EXP, and FLD produced significantly higher µTBS median values than VER and CON after 24 h and 6 m (p 0.05). After 6m, the µTBS median of FIT and EXP significantly decreased (p 0.05), while FLD, VER, and CON showed no significant difference (p > 0.05). FLD and CON exhibited lower WSP than FIT, EXP, and VER (p 0.05). FLD presented the lowest (p 0.05), and VER revealed the highest WSL (p 0.05). FIT and EXP showed the highest (p 0.05), and VER demonstrated the lowest DC (p 0.05)., Conclusions: Following the present study's design, SACs' bonding performance and physical properties remained restricted. Therefore, the application should be considered cautiously, and further clinical trials are necessary to evaluate their long-term performance.

Purpose: To evaluate whether varying thicknesses of universal adhesives utilizing the additional coating strategy would affect their microtensile bond strength (µTBS) to dentin, hardness, and elastic modulus (mechanical properties)., Materials and Methods: Ninety-nine human maxillary premolars were cut to expose coronal dentin, ground with regular-grit diamond burs, and randomly distributed into 9 groups based on 1. adhesive: Scotchbond Universal Adhesive (SB; universal), G Premio Bond (GP; universal) and Clearfil Megabond 2 (MB; two-step self-etch; control); and 2. application strategy (one, two or three coats; each coat light cured). After adhesive application and resin composite buildup, the bonded teeth were stored in distilled water (37°C; 24 h). Resin-dentin sticks from eight premolars per group (each premolar yielded 3 sticks; n = 24 sticks altogether) were prepared for the µTBS test, followed by measurement of the adhesive thicknesses at their fractured ends using SEM. The mechanical properties of the adhesive layers produced by different coats were evaluated on separate resin-dentin slices (n = 3 teeth per group)., Results: Two coats significantly increased the µTBS (p < 0.001) of all the adhesives. The correlation between adhesive thickness and bond strength was positive for GP but negative for SB. MB did not show any correlation. Additional coating significantly increased the mechanical properties of GP (p < 0.05) but did not affect SB and MB (p < 0.05)., Conclusion: An additional adhesive coating over the manufacturers' recommendations improved the bond strength of all the adhesives tested. However, the increased mechanical properties of the adhesives with additional curing was material dependent.

Purpose: To morphologically evaluate the interface between a conventional glass-ionomer cement (GIC) and dentin one day after placement, as well as the changes at the interface after one year of aging/functioning in monkey teeth., Materials and Methods: On the buccal surfaces of seven intact teeth in each of two monkeys, shallow class V cavities were prepared, which were then filled with Fuji IX GP (GC) to provide 1-year in vivo data. A year later, two more teeth in each monkey were similarly prepared and restored for the 1-day in vivo group. The following day, the restored teeth were extracted and the restoration interfaces observed using transmission electron microscopy (TEM). In addition, restorations were similarly placed in two extracted human teeth (control, 1-day in vitro group) and observed a day after placement using TEM., Results: The 1-day in vivo and in vitro results showed that the GIC appeared to bond to dentin through a demineralized zone similar to the hybrid layer produced by resinous adhesives. However, the interface between GIC and dentin after 1 year in vivo appeared to change over time: many needle-like crystals were detected within the remineralized layer and along the collagen fibrils. Slow diffusion of ions resulted in pores, which filled with mineral crystals and made the pores smaller., Conclusion: The interface between GIC and dentin morphologically changes over time, and recrystallization or remineralization at the interface may occur (1 year in vivo).

Purpose: This study evaluated whether active application of self-etching adhesives would influence their microtensile bond strength (µTBS) to dentin cut with burs of different grit sizes., Materials and Methods: Eighty-four human premolars were divided into 12 groups according to 1) two dentin surface preparations with either superfine- or regular-grit diamond burs; 2) three adhesives - Clearfil SE Bond 2 (SE2), Scotchbond Universal (SBU, 3M Oral Care) and G-Premio Bond (GPB, GC); and 3) two application modes of each adhesive (active or passive). Six bonded teeth per group were sectioned into sticks for µTBS testing. Statistical analyses were performed using 3-way ANOVA followed by Duncan's test (p < 0.05). Additional teeth were prepared to observe the interaction between the dentin smear layer obtained from each bur with adhesives under different application modes using transmission electron microscopy (TEM)., Results: Active application significantly increased the dentin bond strength of SE2, irrespective of the kind of bur used (p < 0.05). The highest bond strength of SBU was observed when bonded to superfine-grit diamond bur-cut dentin with the active application. There was, however, no influence of the tested factors on GPB group (p > 0.05). TEM observation showed that active application promoted dentin smear layer dissolution in all adhesive groups., Conclusions: Bond strengths of self-etching adhesives to dentin are influenced by bur-cut smear layers and mainly by application mode of adhesive materials. Active application improves µTBS of self-etching adhesives by enhancing smear layer modification and resin penetration into bur-cut dentin.

Purpose: To evaluate the effects of double application of resin cement primers to dentin prepared with different diamond burs on the cement-dentin bond strengths., Materials and Methods: Sixty flat dentin surfaces were prepared and divided into 12 groups (n = 5) according to three experimental factors: 1. resin cements: RelyX Ultimate (RU), Multilink Automix (ML), and Panavia V5 (PV); 2. resin cement primer application: single or double; 3. dentin surface preparation with regular or superfine diamond burs. Cement-dentin sticks (1 mm2) were prepared for and underwent microtensile bond strength testing (µTBS). Statistical analysis was performed using three-way ANOVA and Duncan's test (α = 0.05). Fractured surfaces and cement-dentin interfaces were observed using SEM. Additional teeth were used to observe the demineralization effect of resin cement primers with SEM and transmission electron microscopy (TEM)., Results: All tested factors demonstrated significant effects on µTBS (p < 0.001). The combination of PV with superfine-grit bur and double application yielded the highest bond strengths. Surfaces prepared with superfine-grit burs demonstrated higher µTBS than did the regular-grit group, but a significant effect was not observed for all groups. The double application of primer significantly increased the bond strength for most combinations, except for PV with superfine-grit bur-prepared dentin., Conclusions: PV showed higher bond strengths than other resin cements. Double application of primer improved the bond strength of all cements to dentin. Bond strengths were higher when dentin was prepared with a superfine-grit bur.

Purpose: To evaluate the effects of double application of self-etch adhesives on their microtensile bond strength (μTBS) to dentin, as well as the hardness (H) of resin-dentin interfacial structures., Materials and Methods: Midcoronal dentin surfaces (n = 45) were polished with 180-grit SiC paper and randomly allocated to 9 groups based on three adhesives - Scotchbond Universal Adhesive (SB), G Premio Bond (GP), and Clearfil Megabond 2 (MB) - and three application modes: single application (S), double application with light curing after each application (DL), and double application with light curing only at the end (D). Following composite-resin build up and water storage (37°C; 24 h), μTBS were obtained. The hardness of adhesive, resin-dentin interface and dentin were evaluated by nanoindentation. The μTBS and H data were analyzed by two-way ANOVA to demonstrate the effects of adhesive and application mode as well as their interaction, followed by Tukey's test (α = 0.05). Fracture modes were determined using a stereomicroscope., Results: μTBS and H were significantly affected by the adhesives and their application modes (p ˂ 0.001). Double application significantly increased the µTBS and H of adhesive and resin-dentin interface (p ˂ 0.05). SB and MB showed significantly higher µTBS than GP (p ˂ 0.05)., Conclusion: Double applications during bonding of dentin having clinically relevant smear layers were beneficial for three contemporary self-etch adhesives. The improvement in bonding performance is believed to be the result of increased chemical interaction, better solvent removal, and improved resin infiltration, leading to improved mechanical properties of the resin-dentin interface or thicker adhesive layers providing improved stress distribution.

Purpose: To evaluate the potential of an additional application of two novel hydrophobic experimental adhesive resins with or without bioactive zinc fluoride glass to promote the bond strength of a one-step self-etch universal adhesive., Materials and Methods: Three self-etch universal adhesives, G-Premio Bond (GPB), Scotchbond Universal (SBU) and Clearfil SE Bond 2 (SE2), and two experimental adhesive resins, BZF210 and BZF21, were used in this study; thus, five groups were formed: GPB, GPB+BZF210, GPB+BZF21, SBU, and SE2. The adhesives were applied to flat dentin surfaces according to each manufacturer's instructions. The microtensile bond strengths (μTBS) were evaluated after 24-h water storage. The fracture modes and interfacial structures were analyzed using SEM, while elemental analysis was performed using SEM-EDS. The data were analyzed using one-way ANOVA and the Games-Howell test (p < 0.05)., Results: Significantly higher μTBS was achieved by additional application of BZF210 (48.68 ± 6.59 MPa) and BZF21 (58.58 ± 2.84 MPa) compared with GPB (33.57 ± 4.22 MPa) alone. Most failures occurred above the smear layer in GBP, while more cohesive and mixed failures were observed in GBP+BZF210, GPB+BZF21, SBU, and SE2. The interfacial structures revealed that GBP+BZF210 and GPB+BZF21 had more and longer resin tags than did GPB. SEM-EDS showed a particularly high peak of zinc in GPB+BZF21., Conclusions: The bond strength of GPB was significantly improved by the additional application of BZF210 and BZF21. Using an additional bioactive hydrophobic layer on a one-step, self-etch universal adhesive can significantly improve its bonding efficacy and extend its clinical options.

Purpose: To determine the microtensile bond strength (µTBS) of two 2-step self-etch adhesives (SEAs) to bur-cut and uncut enamel., Materials and Methods: The buccal and lingual enamel surfaces of 15 teeth were ground flat ("bur-cut" enamel), while the enamel surface of another set of 15 teeth was solely prophylactically cleaned ("uncut" enamel). Resin composite was bonded to the surfaces using the GPDM-based SEA OptiBond XTR (Kerr), the 10-MDP-based SEA Clearfil SE Bond (Kuraray Noritake), or the 3-step etch-and-rinse adhesive (E&RA) OptiBond FL (Kerr) that served as the gold-standard control. After 1-week water storage at 37°C, specimens were serially cut into 1-mm2 stick-shaped microspecimens, of which half per tooth were further subjected to 20,000 thermocycles (TC) prior to µTBS testing. Data were statistically analyzed using ANOVA and the post-hoc Tukey test. The interfacial ultrastructure of the GPDM-based SEA OptiBond XTR with uncut and bur-cut enamel was additionally characterized with transmission electron microscopy (TEM)., Results: After 1-week water storage and upon TC aging, both SEAs bonded significantly (p < 0.05) less effectively to both bur-cut and uncut enamel than did the control OptiBond FL, except when OptiBond XTR was bonded to bur-cut enamel; then a similarly high µTBS was recorded (p > 0.05). TEM interfacial characterization revealed a tight interaction of Optibond XTR with both bur-cut and uncut enamel., Conclusion: The best bonding efficacy to enamel is still achieved by etching with phosphoric acid, following an E&R approach, while the higher etching efficacy of the GPDM-based SEA may result in equally effective bonding, provided that the enamel is bur-roughened first.

Purpose: To determine the bond stability and the change in interfacial ultrastructure of a conventional glassionomer cement bonded to dentin, with and without pretreatment using a polyalkenoic acid conditioner., Materials and Methods: The occlusal dentin surfaces of 10 teeth were ground flat. Glass-ionomer cement was bonded to the surfaces either with or without polyalkenoic acid conditioning. The teeth were sectioned into 1-mm2 stick-shaped specimens. The 200 specimens obtained were randomly assigned to four groups with different periods of storage in water: 1 week, 1 month, 3 months, and 6 months. The microtensile bond strength (μTBS) was determined for each storage time. Additional specimens were prepared for transmission electron microscopy (TEM); they were produced with or without prior polyalkenoic acid conditioning in the same manner as for the μTBS test., Results: There was no significant difference in μTBS to conditioned dentin (p > 0.05). After 6 months of aging, the μTBS to non-conditioned dentin was significantly reduced as compared to the 1-week, 1-month, and 3-month results (p < 0.05). The failures appeared to be of a mixed nature, although aging caused more areas of cohesive than adhesive failure in all groups. TEM observation showed a demineralized layer and an amorphous gel phase in the polyalkenoic acid conditioned group., Conclusion: Aging did not reduce the bond strength of the conventional glass-ionomer cement to dentin when the surface was pretreated with a polyalkenoic acid conditioner.

Purpose: To evaluate the hydrolytic stability of three one-step self-etching adhesives (1-SEAs) bonded to dentin through bond strength testing and ultra-morphological interfacial analysis before and after long-term thermocycling., Materials and Methods: Eighteen flattened mid-coronal dentin surfaces of extracted human molars were subjected to bonding treatment using three 1-SEAs (Clearfil S3 Bond, Kuraray (S3), G-Bond, GC (GB), Absolute, Dentsply-Sankin (AB)), after which the bonded surfaces were built up with composite. After storage overnight at 37°C, the specimens were sectioned into slabs and further trimmed into an hourglass shape with an interface area of approximately 1 mm2. The specimens were left untouched (control) or were thermocycled for 100,000 cycles. The microtensile bond strength (μTBS) was measured and the ultrastructure of the adhesive/dentin interface characterized using transmission electron microscopy (TEM)., Results: Long-term thermocycling significantly decreased the μTBS of all one-step adhesives tested (p < 0.05, one way ANOVA and Games-Howell test). TEM revealed a similar interfacial ultrastructure before and after thermocycling for S3. For GB, many voids were observed at the interface after 100,000 thermocycles. Regarding AB, collagen fibrils could no longer be clearly observed upon staining, while the adjacent unaffected dentin was rich in voids., Conclusion: The bond strength and ultramorphological data demonstrated that the bond of 1-SEAs to dentin degrades with time, although the degree of degradation is obviously material dependent.

Purpose: To compare the microtensile bond strength (MTBS) of two all-in-one adhesive systems and one experimental two-step self-etching adhesive system to two types of bur-cut dentin., Materials and Methods: Using one of the three adhesives, Xeno CF Bond (Xeno), Prompt L-Pop (PL), or the experimental two-step system ABF (ABF), resin composite was bonded to flat buccal and root dentin surfaces of eight extracted human premolars. These surfaces were produced using either regular-grit or superfine-grit diamond burs. After storage overnight in 37 degrees C water, the bonded specimens were sectioned into six or seven slices approximately 0.7 mm thick perpendicular to the bonded surface. They were then subjected to microtensile testing. The surfaces of the fractured specimens were observed microscopically to determine the failure mode. In addition, to observe the effect of conditioning, the two types of bur-cut dentin surfaces were conditioned with the adhesives, rinsed with acetone, and observed with SEM., Results: When Xeno and PL were bonded to dentin cut with a regular-grit diamond bur, MTBS values were lower than to superfine bur-cut dentin, and failures occurred adhesively at the interface, whereas the experimental two-step adhesive showed no significant difference in microtensile bond strength between two differently cut surfaces., Conclusion: The all-in-one adhesives tested here improved bond strengths when bonded to superfine bur-cut dentin as a substrate, whereas the experimental two-step adhesive system showed unchanged bonding to both regular and superfine bur-cut dentin surfaces.