Search

Abstract In the present study, the effect of high current pulsed electron beam (HCPEB) surface treatments on the microstructure, composition, stress states and properties of a Mg-8Gd-3Y-0.5Zr alloy has been investigated. The surface layers showed different features in microstructure and residual stress states under different number of pulses. Such a variation is essentially due to the different level of the dissolution of β-Mg 5 (Gd,Y) particles in remelted layers and the impact from thermal stresses generated by HCPEB treatments. The results have shown that, after 5 pulses of HCPEB treatment, maximum hardness in the surface layer of the sample was increased by 35% and the corrosion rate in 3.5 wt% NaCl water solution was reduced by 30% as compared with those of the untreated sample. The formation of nano structured cells of Mg-RE solid solution and β-Mg 5 (Gd,Y) nano precipitates, together with the residual compressive stress in the surface layer of the 5 pulsed sample account for the increased microhardness and improved corrosion resistance of the HCPEB treated Mg-8Gd-3Y-0.5Zr Mg alloy. Highlights • Mg 5 (Gd,Y) precipitates in the Mg-8Gd-3Y-0.5Zr alloy were dissolved into matrix after HCPEB treatment. • Hardness is increased in the HCPEB treated surface layers due to the formation of nanostructures and residual stresses. • Increased Gd/Y content and residual compressive stress in the 5 pulsed sample account for the improved corrosion resistance. [ABSTRACT FROM AUTHOR]

In the present work, the microstructure modifications and corrosion behaviors of a Mg-4Sm alloy treated by high current pulsed electron beam (HCPEB) with different number of pulses were investigated. The microstructure, composition and phase component in the treated surface layers were characterized by using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM) equipped with energy dispersive spectrometer (EDS) and transmission electron microscope (TEM). The results showed the dissolution of large Mg 41 Sm 5 segregates, the formation of Mg 41 Sm 5 nano-precipitates and twins in the surface layers after treatments. Electrical impedance spectroscopy (EIS) and polarization tests in the 3.5 wt% NaCl solution showed that the 15 pulses treated Mg-4Sm alloy sample exhibited the lowest corrosion current density, highest corrosion potential and polarization resistance among all samples. This is attributed to the homogeneous microstructure and composition with fewer defects in the surface layer after sufficient number of HCPEB pulses. [ABSTRACT FROM AUTHOR]