Search

The conventional pyrometallurgical method for separating lead–antimony alloy produced from jamesonite has a lot of imperfections such as long-term process, tremendous energy cost and harm to the environment. Therefore, a new method to separate lead and antimony from lead–antimony alloy by fractional crystallization is investigated. The experimental results demonstrate that the lead content decreases with the increase of length to the metal column’s bottom. Lead content of the bottom can reach larger than 80% by weight after lifting. In the experimental speed range, the lifting speed has very small impact on the separation effect. After 4 times’ lifting, crude lead bullion (larger than 83% by weight) whose lead content is close to the eutectic point of lead–antimony binary system is gained in the bottom and the antimony can be used for further refining process without converting into Sb 2 O 3 . The separating efficiency of lead in the bottom has reached the theoretical level of fractional crystallization for lead–antimony alloy containing about 40% by weight antimony. [ABSTRACT FROM AUTHOR]

In order to gain insight into how the addition of Cu element affects the crystallization mechanism of amorphous nanocrystalline alloys and soft magnetic properties, the crystallization behavior of (Fe 0.83 B 0.11 Si 0.02 P 0.03 C 0.01) 100-x Cu x (x = 0 and 0.5) amorphous ribbons was investigated based on kinetic and thermodynamic behavior under non-isothermal and isothermal annealing conditions. The results show that under non-isothermal annealing conditions, the Cu0.5 amorphous ribbon not only favors the formation of the amorphous structure, but also enlarges the temperature window for annealing and improves the thermal stability of the α-Fe(Si) phase. At the same time, the Cu0.5 amorphous ribbon shows slow kinetic and is insensitive to heating rate change during annealing treatment. Under isothermal conditions, the addition of Cu decreases the nucleation activation energy (E n) and increases the growth activation energy (E g). This further indicates that the nucleation of α-Fe(Si) grains is easier than the growth process, which is conducive to the formation of a homogeneous nanostructure and improves the soft magnetic properties of the alloy. Compared to Cu0 amorphous ribbon, it is also shown that the Cu0.5 amorphous ribbon changes the crystallization mechanism from diffusion-controlled one-dimensional to two-dimensional growth when the crystallization volume fraction x is 10–30 vol%. While three-dimensional growth become dominated when x is reaches 60 vol% for both ribbons. Therefore, the kinetics of crystallization as well as microstructure supports that the Cu0.5 ribbon is able to exhibit uniformly fine nanocrystalline structures. Further, the Cu0.5 nanocrystalline ribbon shows a higher B s of 1.85 T and a lower H c of 2.55 A/m, respectively, and the favorable (100) orientation of α-Fe(Si) grains formed after annealing is another factor to increase B s. • The Cu-containing alloy show kinetic insensitivity and is suitable for a high heating rate. • The addition of Cu changes the crystallization mechanism when x is between 10% and 30%. • When the applied magnetic field is ND, precipitation of (100) orientation α-Fe grains favors enhancing B s. • The Cu0.5 alloy show B s of 1.85 T, H c of 2.55 A/m. [ABSTRACT FROM AUTHOR]