Search

Abstract: Alloys formed by Ti–Al intermediary phases have low density and very good high-temperature oxidation resistance. Further improvement of high-temperature behaviour can be achieved by a suitable addition of silicon. In this work, Ti–Al–Si alloys containing 20wt.% of aluminium and 10–20wt.% of silicon produced by a reactive sintering technology were tested. Isothermal oxidation tests were carried out at 1000°C in air. The oxidation rate was determined from weight gains caused by oxide formation. Microstructure and phase composition of the oxide layers were studied. Microstructure and hardness changes after various annealing durations were described. [ABSTRACT FROM AUTHOR]

Abstract: In this work, the dependence of microstructure of Fe–Al–Si alloy on conditions of reactive sintering was studied. It was shown that heating rate strongly affects the structure of this alloy. The microstructure consisting of uniformly distributed Al2Fe3Si3 particles in Al2FeSi matrix can only be obtained in this material by rapid heating (over 300Kmin−1). Sufficient reactive sintering temperature to obtain Al2Fe3Si3–Al2FeSi two-phase structure is 750°C. Further increase of the reaction temperature reduces porosity but causes a growth of Al2Fe3Si3 particles. Reactive sintering process is completed during less than 10min in the investigated material. Temperatures over 1050°C produce material composed of FeSi, FeAl and Al2Fe3Si3 phases. However, strongly exothermal reaction of FeSi formation causes melting of the sample. [Copyright &y& Elsevier]

Abstract: In this work, Ti–Al–Si alloys were prepared by reactive sintering. The contents of silicon and aluminium ranged between 0–30wt.% and 0–36wt.%, respectively. Powders of titanium, aluminum, silicon and AlSi30 master alloy prepared by mechanical machining and/or milling were used for sintering. Powders were blended and pressed at room temperature. Sintering was carried out at 900°C for 30min. It was found that it is possible to produce compact materials with the structure corresponding to the as-cast materials when silicon is in the range of 15–20wt.% and aluminium content between 8 and 30wt.%. It was shown that these materials contain two phases—Ti5Si3 and TiAl. The central porosity can be reduced by induction heating. [Copyright &y& Elsevier]

• Ti-Al-Si-X (X˭Co, Cr, Fe, Mo, Nb, Ni) alloys prepared using mechanical alloying and Spark Plasma Sintering. • Alloys have fine-grained and homogeneous microstructure with low porosity. • Alloyed elements increased hardness and compressive strength values. Intermetallic alloys based on Ti-Al-Si system are significant for their excellent high-temperature properties, especially for resistance against oxidation and for achieving good mechanical properties at elevated temperatures. The main problem of these materials is high brittleness at room temperature. In the previous work, selected alloying elements were added into the Ti-Al-Si alloys prepared by reactive sintering, but the properties did not meet the requirements for subsequent use in the automotive or aerospace industry, since the materials had a very porous microstructure. Here, the addition of cobalt, chromium, iron, molybdenum, niobium and nickel into the TiAl15Si15 alloy prepared by mechanical alloying and Spark Plasma Sintering is tested and it is expected to improve the mechanical and high-temperature properties. In this paper, the Ti-Al-Si alloys have been assessed on basis of microstructure, phase composition, mechanical and tribological properties, such as hardness, fracture toughness and compressive strength. Cyclic oxidation tests were performed for 400 h at the temperatures of 800 and 1000 °C. The cyclic oxidation tests simulate industrial processes, where the material is alternately exposed to elevated temperature and subsequent cooling (eg, engine components). From the viewpoint of most of the tested properties, alloying by niobium seems to be the most promising. [ABSTRACT FROM AUTHOR]