Search

Nanocrystalline Ni-Mo alloy coatings with excellent brightness, high hardness, and corrosion resistance were prepared. Nanocrystalline Ni-Mo alloy coating with a Mo content of 14.94 at% was electrodeposited on the copper foil substrate under the optimized conditions with the current efficiency of 51.64%. The electrodeposition behavior of Ni-Mo alloy coatings was studied by cathodic polarization curve and chronopotentiometry. Chronopotentiometry showed that the nucleation rate of Ni-Mo alloys can be accelerated with the increase of current density. Meanwhile, the cathodic polarization curves show that the additives can effectively inhibit the electrodeposition of Ni-Mo alloys. The (2 0 0) and (2 2 0) diffraction peaks of Ni gradually disappeared and the grain size gradually decreased with the increase of Mo content in the alloy coating according to XRD and TEM analysis. Scanning electron microscope (SEM) and confocal microscope observation results show that the coating becomes smoother and denser with the increase of Mo content when Mo content was lower than 14.94 at%, after which the density of the coating saw a decline due to the intensified hydrogen evolution reaction. The microhardness results of the alloy coating show that the microhardness of the alloy coating is related to the solid solution strengthening, texture evolution, and plastic deformation of the alloy. Meanwhile, the alloy coating has a Hall-Petch relationship and inverse Hall-Petch relationship, and the critical grain size is 5.5 nm. The corrosion resistance of Ni-Mo alloy coating is better than that of pure Ni coating, and the corrosion resistance is optimal when the Mo content is about 15 at%. In addition, in the plating solution containing additives, the deposited Ni-Mo alloy coating is smoother and denser, and the hardness and corrosion resistance of the alloy coating is also greatly improved. [Display omitted] • The minimum grain size of nanocrystalline Ni-Mo alloy coatings can reach 2.7 nm. • The hardness and corrosion resistance of nanocrystalline Ni-Mo alloy coatings are higher than pure Ni coatings. • Composite additives can significantly increase Ni-Mo alloy polarization. [ABSTRACT FROM AUTHOR]

Rational design and fabrication of high-efficiency electrocatalysts is essential for improving the kinetics of both oxygen evolution reaction (OER) and oxygen reduction reaction (ORR), so as to constructing high-performance rechargeable zinc-air batteries (ZABs). Among the promising candidates, transition metal-based (oxy)hydroxides have attracted extensive attention for their considerable catalytic potential on oxygen-involved reaction, while unsatisfactory intermediate adsorption/desorption strength and low conductivity limit their practical feasibility. In this work, interface engineering modification strategy is proposed, and a metal–organic framework derived heterostructure catalyst of CoFeO x H y -CoP@CC is fabricated. Comprehensively analyses demonstrate that the interaction between phosphide-(oxy)hydroxide induces the interfacial electronic redistribution, while the formed Schottky heterostructure facilitates rapid electron transfer. All these kinetically favorable for both OER and ORR, and leads to remarkable bifunctional performance on CoFeO x H y -CoP@CC, with the OER overpotential of 240 mV to deliver the current density of 10 mA·cm−2, which is better than CoP@CC, CC and RuO 2. In practical applications, liquid zinc-air cells assembled by CoFeO x H y -CoP@CC deliver the peak power density up to 117.55 mW cm−2, which is close to that of 20% Pt/C catalyst (108.48 mW cm−2), and considerable operational performance has also been achieved in all solid-state flexible ZABs. • A metal–organic framework derived phosphide-hydroxide heterostructure of CoFeO x H y -CoP@CC was fabricated. • Heterogenous interaction tunes the electronic configuration and facilitates rapid electron transfer, so that enhances electrocatalytic OER and ORR performance. • CoFeO x H y -CoP@CC employed as cathode in both liquid and solid zinc-air cells show considerable operational performance. [ABSTRACT FROM AUTHOR]

Abstract: An environmental-friendly electrolyte of silicate and borate, which contained an addition agent of 1H-benzotriazole (BTA) with low toxicity (LD50 of 965mg/kg), was used to prepare an anodized film on AZ31B magnesium alloy under the constant current density of 1.5A/dm2 at room temperature. Effects of BTA on the properties of the anodized film were studied by scanning electron microscopy (SEM), energy dispersion spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), loss weight measurement, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS), respectively. The results demonstrated that anodized growth process, surface morphology, thickness, phase structure and corrosion resistance of the anodized film were strongly dependant on the BTA concentration, which might be attributed to the formation of an BTA adsorption layer on magnesium substrate surface. When the BTA concentration was 5g/L in the electrolyte, a compact and thick anodized film could provide excellent corrosion resistance for AZ31B magnesium alloy. [Copyright &y& Elsevier]

In order to replace the highly poisonous cyanide zincate process of Al alloy, an eco-friendly approach was developed, i.e., electrodeposition of Cu-Zn coating from ionic liquid/ethanol mixed bath. It was demonstrated that the Cu 5 Zn 8 alloy produced from 1-ethyl-3-methylimidazolium trifluoromethylsulfonate (EMImTfO) and 20% (Volume percent) ethanol mixtures under optimal conditions showed cauliflower-shaped structure with a (330) preferred orientation, which could significantly improve the corrosion resistance of Al substrate in Watts bath, thereby elevating Ni coating quality. The overall property of Cu-Zn intermediate layer and its subsequent coating, including compactness, adhesive strength and corrosion resistance is approximately the same as that of cyanide zincate layer and its surface coating, suggesting that the new method is an ideal alternative to conventional zincate treatment. • Cu-Zn coating is electrodeposited from EMImTfO ionic liquid/ethanol mixtures. • Its overall property is approximately the same as that of cyanide zincate layer. • A high-quality Ni coating can be obtained on Cu-Zn coating from Watts bath. • It also has similar property to the Ni coating deposited on cyanide zincate layer. • This method has the great potential to replace cyanide zincate process of Al alloy. [ABSTRACT FROM AUTHOR]

Developing transitional metal-based electrocatalysts with outstanding oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) performance is essential for energy-efficiency alkaline water electrolysis. Herein, a group of heterostructured electrocatalysts constructing of nickel-based hydroxide (NiX(OH) x , X = Co, Fe) nanosheets decorated on copper phosphide nanowires arrays，were fabricated. Both of the as-prepared NiCo(OH) x -CuP/CF and NiFe(OH) x -CuP/CF present outstanding HER and OER activity, with the overpotential of 79 and 202 mV to deliver 10 mA cm−2, respectively, along with considerable long-term stability. Encouragingly, the NiCo(OH) x -CuP/CF ǀǀ NiFe(OH) x -CuP/CF couple enables sustainable alkaline water electrolysis and powered by a solar-powered system. In-depth analyses elucidate that owing to the modulated heterogeneous interfacial states, both of the catalytic kinetics can be optimized targeting HER and OER, respectively. More significantly, a regulated electrode-electrolyte microenvironment induced by unique arrays nanostructure efficiently promote the electron-mass transfer capacity, thereby facilitating the catalytic activity expression. This work demonstrates the desirable catalytic performance by rationally designing of hydroxide-phosphide heterostructure, and highlights the structural features on catalytic performance promotion. • A delicate NiCo(OH) x -CuP/CF and NiFe(OH) x -CuP/CF catalysts were fabricated, in which the heterogeneous interfacial synergy effect between copper phosphide and nickel-based hydroxide enables the catalytic performance breakthrough. • The modulation of current distribution for the HER and OER optimizing the reaction kinetics, is achieved by interfacial synergy effect between Cu 3 P and nickel-based hydroxide. • The arrays nanostructure features high active area, good electrical conductivity, while also regulate the interfacial microenvironment between electrocatalysts and electrolyte that facilitates electro-mass transfer. [ABSTRACT FROM AUTHOR]