Search

Tin sulfide (SnS), a typical IV–VI compound with low-cost, abundant-earth and eco-friendly elements, has aroused widespread attentions in the thermoelectric community due to its similar electron and phonon structures with SnSe. However, undoped SnS possesses the features of low carrier concentration and inferior band structures, which produces indecent thermoelectric performance. In this work, we successfully resolved these shortcomings of SnS through stepwise Na doping and Se alloying. Firstly, the carrier concentration of SnS was increased and optimized through Na doping, which leads to an enhancement both in electrical conductivity and Seebeck coefficients through activating multiple valance bands. Secondly, the electronic band structure of SnS was modified through Se alloying, both narrowing band gap and flatting valence band shape contribute excellent electrical transport properties, resulting in maximum power factor ∼6.0 μWcm−1K−2. After synergistically optimizing interdependent thermoelectric parameters through Na doping and Se alloying, a record high ZT of 0.70 at 873 K was obtained in polycrystalline SnS. Our work indicates that SnS is one of very promising earth-abundant thermoelectric materials for power generation in mediate-temperature range. • Power factor of p -type SnS was improved from 2.5 μWcm−1K−2 to 4.8 μWcm−1K−2 at 923 K through Na doping. • Power factor of p -type SnS was improved from 4.8 μWcm−1K−2 to 6.0 μWcm−1K−2 at 873 K through Se alloying. • ZT max of p -type SnS is distinctly enhanced from 0.25 to 0.70 at 873 K after Na doping and Se alloying. [ABSTRACT FROM AUTHOR]

BiSbSe 3 is a promising medium-temperature thermoelectric material on account of its intrinsically low thermal conductivity. To further enhance the thermoelectric performance in n -type BiSbSe 3 , we conduct Br doping at Se sites to optimize its carrier concentration and electrical conductivity, finally a maximum ZT of ∼0.8 in nanostructured BiSb(Se 0.94 Br 0.06) 3 is obtained at 700 K through mechanical alloying. Based on the optimal BiSb(Se 0.94 Br 0.06) 3 composition, we perform percolation effect with mixed grain sizes in nanoscale and microscale to enhance carrier mobility. It is found that carrier mobility is favorably improved by the addition of microscale grains (∼30 μm) in nanostructured BiSb(Se 0.94 Br 0.06) 3 matrix due to the reduced grain boundaries to carrier scattering, which benefits high electrical conductivity and power factor. Simultaneously, the BiSb(Se 0.94 Br 0.06) 3 matrix with mixed grain sizes still maintains very low thermal conductivity due to its intrinsically strong lattice anharmonicity. Owing to the optimized electrical properties and maintained low thermal conductivity, we obtain a maximum ZT value of ∼1.0 at 700 K in BiSb(Se 0.94 Br 0.06) 3 –4C matrix with 40% microscale grains. This work provides a feasible method to optimize thermoelectric performance by designing microstructure with percolation effect. • Carrier concentration was improved to ∼1.91 × 1020 cm−3 in n -type BiSbSe 3 by Br doping. • PF max of n -type BiSbSe 3 was significantly enhanced to ∼6.0 μW cm−1 K−2 at 700 K through improving carrier mobility via utilizing percolation. • ZT max of n -type BiSbSe 3 was enhanced from ∼0.1 to ∼1.0 at 700K. [ABSTRACT FROM AUTHOR]

The n -type PbTe still maintains relatively low thermoelectric performance compared with its p -type counterpart. Thus, to promote its performance in n -type PbTe, we conduct successive strategies that firstly suppressing the lattice thermal conductivity (κ lat) through alloying with ternary compound AgSbSe 2 , and then optimizing carrier density with Sb, Bi or I doping. In AgSbSe 2 -alloyed PbTe samples, the κ lat can be evidently reduced, and the minimum κ lat decreases from ∼1.1 Wm−1K−1 in undoped PbTe to ∼0.8 Wm−1K−1 in PbTe–5%AgSbSe 2. Based on PbTe–5%AgSbSe 2 matrix, several dopants (Sb, Bi or I) are used to optimize its carrier density, and found that I element is verified to be the most effective dopant to enhance its electrical transport properties. In I-doped PbTe–5%AgSbSe 2 samples, the carrier density raises from ∼2.49 × 1016 cm−3 in PbTe–5%AgSbSe 2 to ∼1.15 × 1019 cm−3 in PbTe 0.992 I 0.008 -5%AgSbSe 2 , which contributes to the maximum power factor ∼14.8 μWcm−1K−2. Combining the reduced lattice thermal conductivity and improved power factor, the maximum ZT max and average ZT ave values in PbTe 0.992 I 0.008 -5%AgSbSe 2 are boosted to ∼1.0 at 723 K and ∼0.77 at 300–823 K, respectively. This work points out a valid avenue to improve thermoelectric transport property in n -type PbTe with separately successive strategies to adjust its thermal and electrical performance. • κ min ∼0.8 Wm−1K−1 was achieved in n -type PbTe through introducing AgSbSe 2. • PF max of n -type PbTe was significantly enhanced from ∼3.4 μWcm−1K−2 to ∼14.8 μWcm−1K−2 by I doping. • ZT max of n -type PbTe was enhanced from ∼0.45 to ∼1.00. [ABSTRACT FROM AUTHOR]

In this work, the thermoelectric performance of p -type PbS was boosted remarkably through Na doping and introducing Cu 2 S. Firstly, the electrical transport properties (power factor) of p -type PbS was optimized via Na doping, and the maximum ZT ∼ 0.67 was achieved in Pb 0.98 Na 0.02 S. Secondly, the total thermal conductivity of Pb 0.98 Na 0.02 S was suppressed through introducing Cu 2 S by means of significantly reducing the electronic thermal conductivity by 80% at 823 K through Cu counter-doping, meanwhile, the power factor of Pb 0.98 Na 0.02 S was further enhanced through optimizing carrier concentrations via introducing Cu. The combination of decreasing total thermal conductivities and the optimizing power factors leads to peak ZT ∼1.2 at 823 K in p -type Pb 0.98 Na 0.02 S–2%Cu 2 S. Present results illustrate that introducing Cu 2 S is an effective method to enhance the thermoelectric performance of p -type PbS through decreasing the electronic thermal conductivity which also has great potential in other thermoelectric materials system. • Thermoelectric performance of p -type PbS was remarkably boosted by reducing electronic thermal conductivity κ ele. • κ ele of p -type Pb 0.98 Na 0.02 S was reduced by 80% from ∼0.53 W m−1K−1 to ∼ 0.11 W m−1K−1 at 823 K with introducing Cu 2 S. • The maximum ZT ∼1.2 at 823 K was realized in p -type Pb 0.98 Na 0.02 S–2%Cu 2 S. [ABSTRACT FROM AUTHOR]

PbTe-based thermoelectric materials are considered to be a medium-temperature thermoelectric candidates and the high-performance n -type PbTe is urgently to be developed to match its p -type counterpart on account of practical application. Herein, we firstly optimized the carrier density of n -type PbTe through Sb doping, and obtained a maximum ZT value of ∼1.0. Then, based on the optimized carrier density, we introduced ternary compounds AgSb(Se, Te) 2 to suppress the lattice thermal conductivity. Minimum lattice thermal conductivity of n -type PbTe was reduced as low as ∼0.53 W m−1K−1 and ∼0.62 Wm−1K−1 through introducing AgSbSe 2 and AgSbTe 2 , respectively. Combining the maintained electrical properties with suppressed thermal conductivity, maximum ZT values ∼1.2 and ∼1.3 were obtained in PbTe+2%AgSbSe 2 and PbTe+2%AgSbTe 2 , respectively. This work provides an effective strategy of synergistically balancing charge and phonon transports in n -type PbTe with ternary AgSb(Se, Te) 2 compounds. • κ min of n -type PbTe was reduced to ∼ (0.53–0.62) Wm−1K−1 through introducing AgSb(Se, Te) 2. • Power factor ∼20.0 μWcm−1K−2 was realized in n -type PbTe through maintaining carrier mobility. • ZT max of n -type PbTe was enhanced from ∼1.0 to ∼ (1.17–1.25). [ABSTRACT FROM AUTHOR]