Microstructure inhomogeneity is imparted into the surface of a Vit1b Zr-based bulk metallic glass (BMG) using ultrasonic nanocrystal surface modification (UNSM). As a result, compressive residual stresses with a maximum magnitude of 1130 MPa were induced in the near-surface region. Substantial improvements in both fracture strain and strength were observed for the treated specimen in three-point bending tests. The microstructure inhomogeneity and free volume generated by severe plastic deformation resulted in increased shear band density during three-point bending tests, which is evidenced by the vein-like pattern observed on the fracture surface of the treated specimen. Moreover, the enrichment of shear bands can cause the interaction between shear bands and can thus obstruct their propagation, leading to work-hardening behavior. High magnitude compressive residual stresses are also believed to impede and slow down the propagation of the shear bands. The synergistic effect of induced inhomogeneity, increased free volume and compressive residual stresses improves the fracture stress and strain of the UNSM-treated BMG. [ABSTRACT FROM AUTHOR]

The efficacy of peening treatment depends on the plasticity of the target metal. In this study, the effectiveness of high-amplitude short duration pulsed current in improving the peening efficacy was examined in a process called electropulsing-assisted ultrasonic nanocrystal surface modification (EP-UNSM). During the EP-UNSM process, the target metal, i.e., Ti64, is subjected to simultaneous ultrasonic peening and electropulsing. The high energy pulsed current can generate a critical magnetic field that can induce the transition of the radical pairs formed by dislocations and the pinning obstacles from the singlet state to the triplet state. This leads to higher dislocation mobility and thus higher plasticity for more effective peening treatment. The results show that the sample treated with EP-UNSM had a deeper plastically deformed layer than that for samples subjected to UNSM and continuous current–assisted UNSM (CC-UNSM), and the maximum depth of plastic deformation was obtained when using the highest peak current density. Due to microstructure refinement, work hardening, and dynamic strain aging, the EP-UNSM sample had a 50% higher surface hardness compared with the control sample. Moreover, the compressive residual stresses generated by EP-UNSM were higher in magnitude and greater in depth compared to those generated by traditional UNSM. These results demonstrate that pulsed current can effectively improve the peening efficacy and EP-UNSM is an effective method for strengthening Ti64. • Pulsed current leads to higher dislocation mobility and thus higher plasticity for more effective peening treatment. • EP-UNSM generates a gradient nanocrystalline layer in Ti64. • EP-USM results in high surface hardness and higher residual stress magnitude and depth. [ABSTRACT FROM AUTHOR]