Nickel alloy 690 (Ni690) were fabricated by wire arc additive manufacturing (WAAM) with three kinds of TiC particles adding contents (no TiC addition, 0.5 wt% TiC, 1.0 wt% TiC) based on cold metal transfer (CMT) technology. The effects of TiC particles adding content on the microstructure, mechanical properties and corrosion resistance were investigated. After adding 1.0 wt% TiC particles, the average length of the γ grains decreased from 301 ± 61 µm to 114 ± 15 µm and the structure of grains changed from columnar dendrite into equiaxed dendritic at the top of each layer, which is results of the heterogeneous nucleation and increase of constitutional supercooling caused by TiC particles. The difference between horizontal and vertical mechanical properties of WAAM Ni690 component disappeared because the heterogeneous nucleation caused by TiC particles prevented the epitaxial growth. The ultimate tensile strength of the WAAM 1.0TiC-Ni690 component reached 590 MPa in both directions, which increased 10 % compared with no TiC addition. The improvement of mechanical properties was owing to the grain refinement and the formation of reinforcing TiC/(Ti, Nb)C second-phase particles. The potentiodynamic polarization tests showed that the improved corrosion resistance with the increased content of TiC particles. The electrochemical impedance spectroscopy (EIS) tests results showed that due to the refined γ columnar grains providing more nucleation sites, a denser and thicker passive film was formed, which improved the corrosion resistance. The composition of the passive film was analyzed by X-ray photoelectron spectroscopy (XPS). The results reflected the more content of oxides and hydroxides of Cr in the passive film of WAAM 1.0TiC-Ni690 sample represented the denser passive film and better corrosion resistance. • Nickel alloy 690 (Ni690) were fabricated by wire arc additive manufacturing (WAAM) with different kinds of TiC particles adding contents. The TiC particles improved the mechanical properties and corrosion resistance • With the addition of TiC particles, the anisotropy in strength of WAAM Ni690 component disappeared for heterogeneous nucleation and the reinforcing TiC/(Ti, Nb)C particles improved the strength of WAAM 1.0TiC-Ni690 component in both directions reaching 590 MPa. • The refiner columnar γ grains offered more nucleation sites on the grain boundaries for the formation of thicker passive film. The more content of oxides and hydroxides of Cr in the passive film of WAAM 1.0TiC-Ni690 component represented the denser passive film and better corrosion resistance. [ABSTRACT FROM AUTHOR]