Search

The microstructure, cryogenic magnetic properties, magneto-caloric effect (MCE) and refrigeration performance of equi-atomic HoErGdCuNi ribbons have been investigated. Fully amorphousized structure with uniform distribution for all constituent elements is obtained. A table-like MCE that covers the temperature region from liquid nitrogen to liquid hydrogen is observed, which leads to a giant refrigerant capacity. Accordingly, the maximum magnetic entropy change (- Δ S M max) , temperature-averaged entropy change [ TEC (10)] and refrigerant capacity (RC) are 15.8 J/kgK, 15.7 J/kgK and 903 J/kg, respectively, at the magnetic field change (Δ H) of 0–7 T. The equi-atomic HoErGdCuNi amorphous ribbons with good MCE parameters especially those with large RC values, are an attractive candidate for cryogenic magnetic refrigeration materials. • Magnetism and magnetocaloric effect (MCE) of HoErGdCuNi ribbons were investigated. • A giant refrigerant capacity (RC) in HoErGdCuNi ribbons was obtained. • The origin of MCE and its potential application in HoErGdCuNi were discussed. [ABSTRACT FROM AUTHOR]

The magnetic and magnetocaloric properties in the equiatomic intermetallic compounds of TmZnAl and TmAgAl have been investigated. The compounds undergo a second order magnetic transition from paramagnetic to ferromagnetic state around its own Curie temperatures T C ∼2.8 K and 3.3 K for TmZnAl and TmAgAl, respectively. A considerable reversible magnetocaloric effect (MCE) was observed at low temperature. For a magnetic field change of 7 T, the maximum values of magnetic entropy change (−Δ S M max ) and relative cooling power ( RCP ) are 11.8 J/kg K and 289 J/kg for TmZnAl, respectively, and the corresponding values for TmAgAl are 14.1 J/kg K and 315 J/kg. [ABSTRACT FROM AUTHOR]

Magnetism and magnetocaloric effect in RE AgAl ( RE = Er and Ho) intermetallic compounds have been studied. Both compounds undergo a second order magnetic phase transition from paramagnetic to ferromagnetic state. A large reversible magnetocaloric effect was observed around its own Curie temperatures T C ∼ 14 and 18 K for ErAgAl and HoAgAl, respectively. For a field change of 0–7 T, the maximum magnetic entropy change reaches 13.7 and 13.8 J/kg K for RE = Er and Ho, respectively. The corresponding relative cooling powers are evaluated to be 398 and 525 J/kg. [ABSTRACT FROM AUTHOR]

The rare-earths (RE) based amorphous materials with large magnetocaloric (MC) effects and excellent glass forming ability (GFA) have been recognized as promising candidates for magnetic refrigeration (MR). In this work, the RE 60 Co 20 Al 20 (RE = Ho, Er, Tm) amorphous ribbons were successfully fabricated and systematically determined with respect to the GFA, magnetic properties and MC effects. A second order magnetic phase transition (MPT) from ferromagnetic to paramagnetic (FM to PM) without noticeable field or thermal hysteresis has been observed around the Curie temperatures, T C ~ 22.3 K for Ho 60 Co 20 Al 20 , ~ 10.3 K for Er 60 Co 20 Al 20 , and ~ 5.0 K for Tm 60 Co 20 Al 20 , respectively. The MC parameters including the maximum magnetic entropy change (| Δ S M max |), temperature-averaged entropy change with 3 K lift [ TEC (3 K)], and relative cooling powder/refrigerant capacity (RCP/RC) have been determined to check the MC performances, and the corresponding values are determined to be 14.16, 15.57 and 15.06 J/kgK, to be14.04, 15.38 and 14.78 J/kgK, and to be 625.0/478.7, 505.7/391.8 and 334.0/243.4 J/kg for Ho 60 Co 20 Al 20 , Er 60 Co 20 Al 20 and Tm 60 Co 20 Al 20 under the field change Δμ 0 H = 5 T, respectively. The present results indicate that RE 60 Co 20 Al 20 (RE = Ho, Er, Tm) amorphous ribbons are considerable for cryogenic MR application. • The RE 60 Co 20 Al 20 (RE = Ho, Er, Tm) amorphous ribbons are fabricated. • The glass forming ability in RE 60 Co 20 Al 20 amorphous ribbons was investigated. • Large magnetocaloric effect in RE 60 Co 20 Al 20 has been observed. • RE 60 Co 20 Al 20 ribbons are considerable for cryogenic magnetic refrigeration. [ABSTRACT FROM AUTHOR]

The ternary rare earth RE CoSi 2 (RE = Er and Tm) intermetallic compounds were synthesized by means of arc-melting technique and their crystal structure, magnetism and magneto-caloric effect (MCE) were studied systematically. Both ErCoSi 2 and TmCoSi 2 crystallize in a CeNiSi 2 -type structure (Cmcm space group) confirmed by FULLPROF Rietveld refinement. Magnetization data indicates the antiferromagnetic (AFM) ground state for both RE CoSi 2 compounds, and a magnetic field-induced ferromagnetic (FM) transition occurs below the Neel temperature T N ∼6.9 K for ErCoSi 2 and ∼5.4 K for TmCoSi 2. Considerable reversible MCE in ErCoSi 2 and TmCoSi 2 was observed. The MCE performances of RE CoSi 2 are evaluated by -Δ S M max (maximal magnetic entropy change), TEC (3) (temperature averaged entropy change), and RCP (relative cooling power) with the values of 7.1 J/kg K, 6.8 J/kg K and 165.9 J/kg for ErCoSi 2 , as well as 8.7 J/kg K, 8.5 J/kg K and 152.9 J/kg for TmCoSi 2 , respectively, under Δ H (field change) of 0–50 kOe. Image 1 • CeNiSi 2 -type RE CoSi 2 (RE = Er and Tm) compounds were fabricated. • AFM ordering at T N ∼6.9 K for ErCoSi 2 and ∼5.4 K for TmCoSi 2. • A field-induced AFM to FM transition for both compounds occur below T N. • Considerable values of -Δ S M max, TEC , RC and RCP were found. • RE CoSi 2 compounds are also considerable for cryogenic magnetic cooling. [ABSTRACT FROM AUTHOR]

The magnetic refrigeration (MR) by utilizing the magnetocaloric effect (MCE) of magnetic solids has been considered a promising, environmentally benign, energy-efficient cooling technology. However, the lack of promising magnetic substances has slowed the development of its active application. To identify suitable candidate materials, we herein identified the structural and magnetic properties together with the MCE and magnetocaloric performances of rare earth (RE) rich RE 6 Ni 2.25 Al 0.75 (RE = Dy, Ho and Er) compounds. All the RE 6 Ni 2.25 Al 0.75 compounds are confirmed to crystallized in orthogonal Ho 6 Co 2 Ga-type structure and underwent paramagnetic to antiferromagnetic magnetic transitions. Moreover, large direct (conventional) and inverse MCEs have been observed in all the RE 6 Ni 2.25 Al 0.75 compounds. The values of peak magnetic entropy changes, temperature-averaged magnetic entropy changes with 5 K-lift and relative cooling powers under magnetic field change of 0–7 T are evaluated to be − 4.44 J/kg-K, − 4.38 J/kg-K and 230.6 J/kg for Dy 6 Ni 2.25 Al 0.75 , to be − 12.68 J/kg-K, − 12.26 J/kg-K and 378.2 J/kg for Ho 6 Ni 2.25 Al 0.75 , and to be − 17.52 J/kg-K, − 17.33 J/kg-K and 465.7 J/kg for Er 6 Ni 2.25 Al 0.75 , respectively. • The RE6Ni2.25Al0.75 (RE = Dy, Ho and Er) compounds are fabricated. • The structural and magnetic properties were investigated. • Large direct and inverse magnetocaloric effects were observed. • The Er6Ni2.25Al0.75 is considerable for cryogenic magnetic refrigeration. [ABSTRACT FROM AUTHOR]