Semi-insulating GaN films with controlled dopant profiles have significant potential to improve the performance of high-power electronics. Beryllium doped GaN (GaN:Be) films previously demonstrated a semi-insulating nature, but the Be-dopant profiles in these films exhibited Be surface segregation and accumulation, which would lead to undesired leakage current paths in devices and deterioration of breakdown voltage. Improved growth kinetics of metal modulated epitaxy at low growth temperatures are applied in the study of GaN:Be films to achieve selectively controlled and abrupt step-doped Be profiles. The GaN:Be films were found to be semi-insulating via Hall effect measurements at elevated temperatures of 495 K. The films were shown to effectively electrically compensate surface contaminants at regrowth interfaces. Surface contaminants (O, Si, and C) typically result in unintentional n-type doping at the GaN on GaN regrowth interface. In order to demonstrate the utility of Be doping, GaN:Mg p-type films are grown atop GaN:Be buffer, AlN buffer, and control samples without any insulating buffer on GaN:Fe templates. Remarkably, the p-type films grown atop control samples up to 400 nm thick are compensated from surface contaminants, whereas the films grown atop AlN and GaN:Be insulating layers effectively electrically neutralize the surface contaminants and result in high hole concentrations of 2.3 and 2.5 × 1019 cm−3, respectively. The use of GaN:Be instead of AlN buffers eliminates the need to deconvolve the effects of the AlN/GaN 2D sheet charges and defects from lattice mismatch, removes lateral conduction paths, and reduces inherently high static vertical electric fields that detract from power device performance. [ABSTRACT FROM AUTHOR]

The first step of a multi-cycle rapid thermal annealing process was systematically studied. The surface, structure, and optical properties of Mg implanted GaN thin films annealed at temperatures ranging from 900 to 1200 °C were investigated by Raman spectroscopy, photoluminescence, UV-visible spectroscopy, atomic force microscopy, and Nomarski microscopy. The GaN thin films are capped with two layers of in-situ metal organic chemical vapor deposition -grown AlN and annealed in 24 bar of N2 overpressure to avoid GaN decomposition. The crystal quality of the GaN improves with increasing annealing temperature as confirmed by UV-visible spectroscopy and the full widths at half maximums of the E2 and A1 (LO) Raman modes. The crystal quality of films annealed above 1100 °C exceeds the quality of the as-grown films. At 1200 °C, Mg is optically activated, which is determined by photoluminescence measurements. However, at 1200 °C, the GaN begins to decompose as evidenced by pit formation on the surface of the samples. Therefore, it was determined that the optimal temperature for the first step in a multi-cycle rapid thermal anneal process should be conducted at 1150 °C due to crystal quality and surface morphology considerations. [ABSTRACT FROM AUTHOR]