Search

In this work, we present a systematic study of the effect of the stoichiometry of BaTiO3 (BTO) films grown on the Ge(001) substrate by molecular-beam-epitaxy using different characterization methods relying on beam diffraction, including reflection high-energy electron diffraction (RHEED), X-ray diffraction (XRD), and selected-area electron diffraction in transmission electron microscopy. Surprisingly, over a wide range of [Ba]/[Ti] ratios, as measured by the Rutherford backscattering spectrometry, all the BTO layers exhibit the same epitaxial relationship h100iBTO(001)// 〈110〉Ge(001) with the substrate, describing a 45° lattice rotation of the BTO lattice with respect to the Ge lattice. However, varying the [Ba]/[Ti] ratio does change the diffraction behavior. From RHEED patterns, we can derive that excessive [Ba] and [Ti] generate twinning planes and a rougher surface in the non-stoichiometric BTO layers. XRD allows us to follow the evolution of the lattice constants as a function of the [Ba]/[Ti] ratio, providing an option for tuning the tetragonality of the BTO layer. In addition, we found that the intensity ratio of the 3 lowest-order Bragg peaks I(001)/ I(002), I(101)/I(002), and I(111)/I(002) derived from ω-2θ scans characteristically depend on the BTO stoichiometry. To explain the relation between observed diffraction patterns and the stoichiometry of the BTO films, we propose a model based on diffraction theory explaining how excess [Ba] or [Ti] in the layer influences the diffraction response. [ABSTRACT FROM AUTHOR]

The tunneling current through an atomic force microscopy (AFM) tip is used to evaluate the effective electrical contact area, which exists between tip and sample in contact-AFM electrical measurements. A simple procedure for the evaluation of the effective electrical contact area is described using conductive atomic force microscopy (C-AFM) in combination with a thin dielectric. We characterize the electrical contact area for coated metal and doped-diamond tips operated at low force (<200 nN) in contact mode. In both cases, we observe that only a small fraction (<10 nm2) of the physical contact (~100 nm2) is effectively contributing to the transport phenomena. Assuming this reduced area is confined to the central area of the physical contact, these results explain the sub-10 nm electrical resolution observed in C-AFM measurements. [ABSTRACT FROM AUTHOR]

Band-to-band tunneling parameters of strained indirect bandgap materials are not well-known, hampering the reliability of performance predictions of tunneling devices based on these materials. The nonlocal band-to-band tunneling model for compressively strained SiGe is calibrated based on a comparison of strained SiGe p-i-n tunneling diode measurements and doping-profile-based diode simulations. Dopant and Ge profiles of the diodes are determined by secondary ion mass spectrometry and capacitance-voltage measurements. Theoretical parameters of the band-to-band tunneling model are calculated based on strain-dependent properties such as bandgap, phonon energy, deformation-potential-based electron-phonon coupling, and hole effective masses of strained SiGe. The latter is determined with a 6-band k.p model. The calibration indicates an underestimation of the theoretical electron-phonon coupling with nearly an order of magnitude. Prospects of compressively strained SiGe tunneling transistors are made by simulations with the calibrated model. [ABSTRACT FROM AUTHOR]

Polycrystalline silicon (pc-Si) thin-films with a grain size in the range of 0.1–100 μm grown on top of inexpensive substrates are economical materials for semiconductor devices such as transistors and solar cells and attract much attention nowadays. For pc-Si, grain size enlargement is thought to be an important parameter to improve material quality and therefore device performance. Aluminum-induced crystallization (AIC) of amorphous Si in combination with epitaxial growth allows achieving large-grained pc-Si layers on nonsilicon substrates. In this work, we made pc-Si layers with variable grain sizes by changing the crystallization temperature of the AIC process in order to see if larger grains indeed result in better solar cells. Solar cells based on these layers show a performance independent of the grain size. Defect etching and electron beam induced current (EBIC) measurements showed the presence of a high density of electrically active intragrain defects. We therefore consider them as the reason for the grain size independent device performance. Besides dislocations and stacking faults, also Σ3 boundaries were electrically active as shown by combining electron backscattered diffraction with EBIC measurements. The electrical activity of the defects is probably triggered by impurity decoration. Plasma hydrogenation changed the electrical behavior of the defects, as seen by photoluminescence, but the defects were not completely passivated as shown by EBIC measurements. In order to reveal the origin of the defects, cross section transmission electron microscopy measurements were done showing that the intragrain defects are already present in the AIC seed layer and get copied into the epitaxial layer during epitaxial growth. The same types of intragrain defects were found in layers made on different substrates (alumina ceramic, glass ceramic, and oxidized silicon wafer) from which we conclude that intragrain defects are not related to the relatively rough alumina ceramic substrates often used in combination with high temperature epitaxy. Further improvement of the material quality, and hence device performance, is therefore not simply achieved by increasing the grain size, but the intragrain quality of the material also needs to be taken into account. For pc-Si layers based on AIC and epitaxial growth, the seed layer has a crucial impact on the intragrain defect formation. [ABSTRACT FROM AUTHOR]

Atomic layer deposition (ALD) is used in applications where inorganic material layers with uniform thickness down to the nanometer range are required. For such thicknesses, the growth mode, defining how the material is arranged on the surface during the growth, is of critical importance. In this work, the growth mode of the zirconium tetrachloride/water and the trimethyl aluminum/water ALD process on hydrogen-terminated silicon was investigated by combining information on the total amount of material deposited with information on the surface fraction of the material. The total amount of material deposited was measured by Rutherford backscattering, x-ray fluorescence, and inductively coupled plasma–optical emission spectroscopy, and the surface fractions by low-energy ion scattering. Growth mode modeling was made assuming two-dimensional growth or random deposition (RD), with a “shower model” of RD recently developed for ALD. Experimental surface fractions of the ALD-grown zirconium oxide and aluminum oxide films were lower than the surface fractions calculated assuming RD, suggesting the occurrence of island growth. Island growth was confirmed with transmission electron microscopy (TEM) measurements, from which the island size and number of islands per unit surface area could also be estimated. The conclusion of island growth for the aluminum oxide deposition on hydrogen-terminated silicon contradicts earlier observations. In this work, physical aluminum oxide islands were observed in TEM after 15 ALD reaction cycles. Earlier, thicker aluminum oxide layers have been analyzed, where islands have not been observed because they have already coalesced to form a continuous film. The unreactivity of hydrogen-terminated silicon surface towards the ALD reactants, except for reactive defect areas, is proposed as the origin of island growth. Consequently, island growth can be regarded as “undesired surface-selective ALD.” [ABSTRACT FROM AUTHOR]

The polycrystalline silicon (pc-Si) layers with variable grain sizes were constructed by changing the crystallization temperature of the AIC process and determine if larger grains resulted in better solar cells. The crucial impact of seed layer on the intragrain defect formation for the pc-Si layers based on AIC and epitaxial growth suggested that in addition to increased grain size, the intragrain quality of the material should also be considered in order to improve material quality and achieve high device performance.