In this work, we employ the substrate hot electron injection technique as a characterization tool to examine the defect creation mechanisms in high-k HfSiON gate stacks, taking advantage of the independent control over oxide field, electron fluence, and injected electron energy which the technique allows. We show that defect creation and oxide breakdown are dependent on the energy of the injected electrons and not on the oxide field. Furthermore, we show that the energy of the injected electrons governs whether the majority of the defects are created at the Si/SiO2 interface or in the bulk of the material. Results show that at operating conditions, the primary threat to device reliability from hot carrier damage is the introduction of a permanent 3D positive bias temperature instability component introduced by increased interface trap generation, even for carriers with energy slightly above that of field accelerated electrons. We also discuss the feasibility of using substrate hot electron injection as a means to accelerate time dependent dielectric breakdown measurements, thereby allowing degradation at lower oxide fields to be probed. [ABSTRACT FROM AUTHOR]

The charge trapping is studied in metal-ferroelectric-insulator-semiconductor (MFIS) capacitors with SrBi2Ta2O9 (SBT)/Al2O3/SiO2 gate stack by high-frequency and pulsed capacitance-voltage (CV) measurements. The ferroelectric polarization is observed by high-frequency CV. Under fast gate voltage sweep in pulsed CV, the delay of electron trapping detrapping in the buffer layer induces an opposite CV hysteresis direction than that of the ferroelectric polarization. For memory programming, the hole trapping in the gate stack limits the electric field in SBT. Furthermore, the electron trapping during stress induces serious threshold voltage instability as well as erratic memory read out. All these charge trapping problems are important for the practical application and reliability of the memory with MFIS structure. [ABSTRACT FROM AUTHOR]

The charge trapping in metal-ferroelectric-insulator-semiconductor structure with SrBi2Ta2O9/AI2O3/SiO2 stack is discussed. The competition between hole trapping and polarization effect is examined.