Search

Our previous studies have confirmed the superior biocompatibility of the poly-L-lactic acid/amorphous calcium phosphate (PLLA/ACP) scaffolds (PowerScaffold) compared to PLLA scaffolds and their similar 6-month radial strength compared with TAXUS stents. In order to conduct further dynamic observations on the performance of the PowerScaffold after 12-month implantation compared with the TAXUS stents. Twenty PowerScaffold and 20 TAXUS were implanted in porcine coronary arteries. At 12-month follow-up, Quantitative Coronary Angiography showed that the stent reference vessel diameter (3.19 ± 0.25 mm vs. 2.75 ± 0.22 mm, p < 0.05), the mean lumen diameter (3.07 ± 0.22 mm vs. 2.70 ± 0.17 mm, p < 0.05) and the late lumen gain (0.45 ± 0.07 mm vs. 0.06 ± 0.06 mm, p < 0.01) were all significantly greater with the PowerScaffold than the TAXUS. As well, Intravascular Ultrasound showed the stent reference vessel area (7.74 ± 0.48 mm2 vs. 6.96 ± 0.51 mm2, p < 0.05), the mean stent area (7.49 ± 0.46 mm2 vs. 6.53 ± 0.47 mm2, p < 0.05) and the mean lumen area (7.22 ± 0.50 mm2 vs. 6.00 ± 0.48 mm2, p < 0.01) were all significantly greater with the PowerScaffold than the TAXUS. The luminal patency rate of the PowerScaffold significantly increased from 72.45 ± 6.84% at 1 month to 93.54 ± 8.15% at 12 months (p < 0.01) while the TAXUS stents were associated with a non-significant decreasing trend (89.44 ± 8.44% vs. 86.53 ± 8.22%). Pathology indicated the average thickness of the struts degraded by 14.25 ± 3.04 μm at 1 month, 23.39 ± 2.45 μm at 6 months and 35.54 ± 2.20 μm at 12 months. Immunohistochemical examination showed that the expression of inflammatory factors NF-κB gradually decreased from 1-month to 12-month (36.79 ± 4.78 vs. 5.79 ± 2.85, P < 0.01). As the late lumen gain of arteries implanted with the PowerScaffold increases over time with the growth of vessels, it effectively reverse the late vascular negative remodeling observed with the TAXUS stents, providing a better option for lumen restoration treatment in clinical practice.

Biodegradable polymers used as vascular stent coatings and stent platforms encounter a major challenge: biocompatibility in vivo, which plays an important role in in-stent restenosis (ISR). Co-formulating amorphous calcium phosphate (ACP) into poly(lactic-co-glycolic acid) (PLGA) or poly-L-lactic acid (PLLA) was investigated to address the issue. For stent coating applications, metal stents were coated with polyethylene-co-vinyl acetate/poly-n-butyl methacrylate (PEVA/PBMA), PLGA or PLGA/ACP composites, and implanted into rat aortas for one and three months. Comparing with both PEVA/PBMA and PLGA groups after one month, the results showed that stents coated with PLGA/ACP had significantly reduced restenosis (PLGA/ACP vs. PEVA/PBMA vs. PLGA: 21.24 +/- 2.59% vs. 27.54 +/- 1.19% vs. 32.12 +/- 3.93%, P < 0.05), reduced inflammation (1.25 +/- 0.35 vs. 1.77 +/- 0.38 vs. 2.30 +/- 0.21, P < 0.05) and increased speed of re-endothelialization (1.78 +/- 0.46 vs. 1.17 +/- 0.18 vs. 1.20 +/- 0.18, P < 0.05). After three months, the PLGA/ACP group still displayed lower inflammation score (1.33 +/- 0.33 vs. 2.27 +/- 0.55, P < 0.05) and higher endothelial scores (2.33 +/- 0.33 vs. 1.20 +/- 0.18, P < 0.05) as compared with the PEVA/PBMA group. Moreover, for stent platform applications, PLLA/ACP stent tube significantly reduced the inflammatory cells infiltration in the vessel walls of rabbit iliac arteries relative to their PLLA cohort (NF-kappaB-positive cells: 23.31 +/- 2.33/mm2 vs. 9.34 +/- 1.35/mm2, P < 0.05). No systemic biochemical or pathological evidence of toxicity was found in either PLGA/ACP or PLLA/ACP. The co-formulation of ACP into PLGA and PLLA resulted in improved biocompatibility without systemic toxicity.

Rationale We reported previously, in porcine coronary arteries, that the novel biodegradable PowerStent Absorb paclitaxel-eluting stent had improved and sustained structural strength and functional performance at one month post-implantation. Objective To report the stent performance at 6-month follow-up. Methods and results Six PowerStent Absorb and six TAXUS stents were randomly implanted in the left anterior descending and right coronary arteries of six Tibet miniature pigs. Quantitative coronary angiography (QCA) and intravascular ultrasound (IVUS) images were obtained at the time of implantation (T0) and at 6 months (T6). Two animals were sacrificed at T6 for histopathological evaluation. At T6, QCA showed that the mean luminal vascular diameter (mLD) between the PowerStent and the TAXUS stents were similar (2.36 ± 0.38 vs. 2.61 ± 0.31, respectively). Based on the IVUS analysis, the mLD and the mean lumen cross-sectional area (mCSA) in the PowerStent-treated arteries were similar between T0 and T6 (mLD: 2.74 ± 0.13 vs. 2.70 ± 0.20 and mCSA: 6.81 ± 0.62 mm2 vs. 6.68 ± 0.94 mm2). Histopathology showed that the PowerStent stents were well apposed to the vessel wall with no recoil, strut fracture and thrombus formation. The stents were fully covered with a layer of endothelial cells. Conclusions At six-month post-implantation, the PowerStent Absorb stents maintained their structural strength and functional performance. The development of restenosis was controlled, no stent thrombosis was observed and the stents were fully re-endothelialized. These results suggest the PowerStent Absorb stent is safe and effective for up to 6 months when implanted in porcine coronary arteries.