The nature of layers formed by cellulose nanofibrils that had been surface modified (hydrophobized) at the oil/water (o/w) interface was investigated. The aim of the study was to clarify the mechanism underlying the excellent ability of these nanoparticles to stabilize emulsions. Layers of hydrophobized nanofibrillated cellulose spread at the o/w interface were deposited on glass slides by the Langmuir-Blodgett deposition technique. Overall evaluation of layer structures was performed by image analysis based on a Quadtree decomposition of images obtained from a flatbed scanner. A more detailed characterization of the layer structures was performed by Atomic Force Microscopy (AFM), and Field-Emission Scanning Electron Microscopy (FE-SEM). The results show that nanofibrils that were able to stabilize emulsions occur as single, dispersed fibrils or form large, network-like aggregates at the o/w interface. Fibrils that were insufficiently hydrophobized and therefore did not stabilize emulsions were only partially deposited and formed small, compact aggregates. We conclude that it is likely that the network formation is the main mechanism by which the fibrils prevent coalescence of emulsion droplets.

Alkylsiloxane and perfluoroalkylsiloxane monolayers are prepared on siliceous surfaces using the techniques of Langmuir-Blodgett deposition and solid-liquid chemical adsorption. Acid-catalyzed hydrolysis and polycondensation reactions provide two-dimensional siloxane networks at the liquid-vapor interface, which can be compressed to mean molecular areas of approximately 22 and approximately 32 A(2) for pendent hydrocarbon and fluorocarbon chains, respectively. Subsequent Langmuir-Blodgett transfer onto glass substrates at moderate surface pressures leads to compact monolayers for single-component precursors, while mixed alkyl- and perfluoroalkylsilanes produce nonhomogeneous films characterized by transfer ratios greater than unity. As an alternate monolayer preparation technique, silane polymerization was performed directly on siliceous surfaces via a chemical adsorption mechanism. XPS analysis of a chemically adsorbed 1H,1H,2H,2H-perfluorodecylsiloxane film confirms a single adsorbed monolayer thickness in which the pendent fluoroalkyl chains align nonperpendicularly with respect to the surface. The surface free energy was determined to be 11.4 dyn cm(-1) based on static contact angle measurements. AFM imaging shows the presence of surface defects due to oligomer deposition during the drying process. The use of solubilized trichloro-based silane coupling agents under anhydrous conditions is shown to produce surfaces with a minimal number of surface defects. The presence of undissolved silane material in the bulk solution significantly increases the number of surface defects.