Search

Self-assembled monolayers (SAMs) of functionalized azobenzene thiols (RAzoCnSH, n=3-6 for R=H, abbreviated as AzoCnSH; and n=4 for R=CH(3)CONH, abbreviated as aaAzoC4SH) on different substrates RAzoCnSz.sbnd;z.sfnc;S (S represents substrates of vacuum-deposited gold (Au), silver foil (Ag), HNO(3) etched silver foil (EAg), and silver mirror (mAg)) have been studied by SERS in the near-infrared region. SERS of the SAMs on EAg and/or mAg exhibit SERS effects that vary with etching time and/or deposition time. The most appropriate time is 5 s for etching in 1:1 HNO(3) and 40 s for deposition in 0.1 M Ag(NH(3))(2)NO(3). Further, a layer of Ag mirror was conveniently deposited on the top of the SAMs on different substrates, yielding a more efficient SERS-active system possessing a "sandwiched" structure of mAgz.sfnc;RAzoCnS-z.sfnc;S. An appropriate surface roughness is required for the strongest SERS effect. Scanning electron microscopy (SEM) indicates that there exist a large number of projects around 100 nm on the surface showing the strongest SERS effect. When the surface roughness is decreased or increased, the SERS effect decreases sharply. The relationship between the SERS effect and the structural nature was investigated and showed that the enhancement factor decays exponentially with increasing in distances of the azobenzene group from the underlying substrate or the overlying silver mirror. This result reveals that the SERS effect may be the result of the electromagnetic coupling effect between two metal layers.

A series of thiol-functionalied azobenzene derivatives (RAzoCnSH: R=H for n=3-6, abbreviated as AzoCnSH; R=CH(3)CONH for n=4, abbreviated as aaAzoC4SH) on gold electrodes were prepared and their self-assembly and electrochemical properties were studied by cyclic voltammetry. They all formed uniform and reproducible self-assembled monolayers (SAMs) on gold and showed well-behaved voltammetric responses in aqueous solution. Both the length of the alkyl chain spacer and the H-bonding of the end acetamino group had effects on the stability and the electrochemical kinetics of the SAMs, and the effect of the H-bonding was dominant. The surface coverage of the SAMs (AzoCnSH) is gradually increased with an increase of the alkyl chain spacer length, whereas the presence of the terminal acetamino group leads to a greater increase of the surface coverage. At a low scan rate, voltammetric responses corresponding to an irreversible two-electron, two-proton reduction/oxidation of the trans-azobenzene redox center were obtained in the range of +300 mV and -800 mV, which exhibited very large peak-to-peak splitting. At a high scan rate of 500 mV/s, two steps of reversible one-electron, one-proton reduction/oxidation corresponding to the cis-isomer in azobenzene-thiol SAMs (n is odd) was clearly observed between +300 and -200 mV. The apparent electron-transfer rate is decreased with increasing distance between the azobenzene redox center and the gold electrode. The existence of the end acetamino group which restricted the conformational change during the redox process also led to a decrease of the standard rate constant, and this restriction effect is more predominant than the distance effect.

Nanocrystalline Co(x)Ni(y)Cu(100-x-y) particles were synthesized by the reduction of metal acetates in a mixture of polyol and Tween 80. Inductively coupled plasma (ICP) analysis revealed that the actual wt% of Co, Ni, and Cu in these nanoparticles was nearly the same as in the starting solutions. The structures of the particles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED) spectroscopy, and vibrating sample magnetometry (VSM). The results of XRD and VSM confirmed that there was no metastable alloying in the particles. The particles were composites, consisting of nanoscale crystallites of face-centered cubic (fcc) Cu, face-centered cubic (fcc) Ni, and face-centered cubic (fcc) Co. During preparation the nucleation of Cu occurred first; then small Cu nuclei acted as cores for the precipitation of Co and Ni. The particles showed an increase in saturation magnetization (M(s)) as the concentration of Co or Ni in the particles was increased. The changes of both M(s) and coercivity of the particles with increasing annealing temperatures were studied. The coercivity of the particles was very high; it could reach as high as 489 Oe for Co34.3Ni31.2Cu34.5) .

Self-assembled monolayers (SAMs) of 4-acetamino-4'-(4-mercaptobutoxy)azobenzene (CH3)CONH-ph-N=N-ph-O(CH2)(4)SH, abbr. aaAzoC4SH) and 4-mercaptobutoxy azobenzene (ph-N=N-ph-O(CH2)(4)SH, abbr. AzoC4SH) on a gold surface have been studied by X-ray photoelectron spectroscopy (XPS), FT Raman spectroscopy, and electrochemistry. A surface-enhanced Raman scattering (SERS)-active system with a "sandwiched" structure of Ag/R-Azo-C4S-/Au was conveniently obtained by the method of Tollen's test. The relationship between the SERS effect and the structural nature of the system indicates that the enhancement correlates to both the silver islands above and the gold substrate underneath. The redox behaviors of the self-assembly on gold electrodes showed that the SAMs of the two compounds exhibit well-behaved voltammetric responses in a Britton-Robinson buffer corresponding to the irreversible two-electron, two-proton reduction-oxidation of azobenzene. The apparent electron-transfer rate kinetics is very sluggish, and the rate constant k(app) of aaAzoC4SH/Au (1.34 x 10(-6) s(-1)) is lower than that of AzoC4SH/Au (1.63 x 10(-4) s(-1)), which may be attributed to the different spatial restriction of close-packing structures on the conformational change accompanied by electron and proton transfer in the SAMs.

Self-assembled multilayer thin films have been prepared on Au substrate by alternate surface derivatization with L-cysteine hydrochloride and cupric perchlorate. The layer-by-layer structure at each step of multilayer formation was investigated by X-ray photoelectron spectroscopy. The measurements indicate that there are two structure modes in the multilayers. One is that Cu(2+) sandwiches between two amino acid groups. The other one is that Cu(+) is bonded through disulfide and thiolate. This process is also confirmed by cyclic voltammetry of Cu ion at different self-assembled multilayers. Steps further on will lead to repeated multilayer films.