The absorption spectra, emission under 940 nm excitation by laser diode, and fluorescence lifetimes of as-grown and annealed Cr,Yb:YAG crystal have been investigated at room temperature. The increase of absorption coefficients at 941 and 1030 nm and the quenching of Yb3+ emission intensity and fluorescence lifetime after annealing are due to the increase of the concentration of Cr4+ ions. The data of thermal expansion and specific heat of the crystal have been measured. The thermal expansion coefficient is α=8.71×10−6 /K. The specific heat is 89.9 cal/mol K at 320.5 K. [Copyright &y& Elsevier]

Abstract: A large and transparent Yb:FAP crystal with dimensions up to ∅30mm×85mm has been grown by the Czochralski method. The preparation of the raw material has been investigated. X-ray power diffraction studies of Yb:FAP crystal confirm that the as-grown crystal is isostructural with the FAP crystal. The crystalline quality has been studied using X-ray rocking curve analysis. The segregation coefficient of Yb3+ in the Yb:FAP crystal has been also determined. Linear thermal expansion coefficients in [001] and [100] directions have been measured in the 30–800°C temperature range. [Copyright &y& Elsevier]

Abstract: Gd2SiO5 (GSO) single crystal codoped with Yb3+ and Er3+ (Abbr. as Er:Yb:GSO) was successfully grown by the Czochralski (CZ) method for the first time and the spectral characteristics were investigated. The absorption and fluorescence spectra were measured. The emission lifetime of the 4I13/2–Er-level was measured to be 5.84ms and the emission cross-section at 1529nm was calculated to be 1.03×10−20 cm2. The results indicate that Er:Yb:GSO is a potential laser material at ∼1.55μm wavelength region. [Copyright &y& Elsevier]

Abstract: The effects of Na+ doping level on the thermal conductivities, absorption and emission spectra, and fluorescence lifetimes of Yb3+,Na+:CaF2 crystals were systematically studied. Sites structure, covalent force, and crystal field strength of Yb3+:CaF2 crystals were markedly varied by codoping Na+ as charge compensator. The 2.0at% Yb3+ and 3.0at% Na+-codoped CaF2 crystal was demonstrated to operate in diode-pumped passively mode-locking scheme. Transform-limited 1ps laser pulses were obtained, showing the crystal capable of producing ultra-short laser pulses. [Copyright &y& Elsevier]