Abstract: Crystals of Ce3+-doped (Lu x Y1−x )3Al5O12 (LuYAG) have been grown and studied by X-ray powder diffraction, emission spectroscopy, excitation spectroscopy and X-ray excited fluorescence spectroscopy. The X-ray powder diffraction pattern revealed that the as-grown LuYAG:Ce crystal possessed the garnet structure. Compared with Ce3+-doped Y3Al5O12 (YAG), the absorption bands associated with the 4f–5d transition shifted to shorter wavelengths, the emission band that originated from a transition from the lowest 5d level to the 2F ground state of the Ce3+ ions shifted to the blue, which was probably due to a larger Stokes shift of the emission, and the reduction of relative intensity of antisite defect emission in the X-ray excited fluorescence spectra revealed that introducing Lu ions into YAG could reduce the antisite defect. [Copyright &y& Elsevier]

Abstract: A Yb3+-doped CaYAlO4 laser crystal has been grown by the Czochralski technique. The segregation coefficient was measured by Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES). The cell parameters were analyzed with X-ray diffraction experiments. Color defects in Yb:CaYAlO4 have been evidenced to be similar to those in undoped CaYAlO4. The polarized absorption spectra and the fluorescence spectrum of the Yb:CaYAlO4 crystal were measured at room temperature. The fluorescence decay time of the Yb3+ ion was investigated. The results show that Yb:CaYAlO4 has potential as a laser gain medium for an ultrashort laser system. [Copyright &y& Elsevier]

Five atomic percent Yb:YAG laser crystals have been grown by Czochralski (CZ) and temperature gradient technique (TGT) method. The absorption spectra of as-grown and annealed Yb:YAG crystals have been investigated. There is no Yb2+ and color center absorption in TGT-grown Yb:YAG crystals; the absorption peak of CZ-grown Yb:YAG crystals after O2-annealing at 255 nm is attributed to Fe3+ ions. The longitudinal distribution of Yb3+ ions has also been studied; TGT-grown Yb:YAG crystal has a larger distributing inhomogeneity of Yb3+ although it is large sized. [Copyright &y& Elsevier]