Tm3+-doped calcium niobium gallium garnet (Tm:CNGG) single crystals have been successfully grown by the micro-pulling-down (μ-PD) method. The crystal structure, absorption spectra, fluorescence spectra and lifetimes of Tm:CNGG crystals were investigated. The absorption and emission bandwidths of Tm:CNGG crystals are larger than those of other Tm3+ doped garnet crystals, which will be beneficial for laser diode (LD) pumping and ultrashort pulse generation. Additionally, continuous wave (CW) laser operation around 2 μm was achieved in the 2.0 at.% Tm:CNGG crystal by LD pumping. [ABSTRACT FROM AUTHOR]

In this paper, the Floating zone technique was used to grow high-quality Cr3+:YScO 3 crystals. The absorption cross-sections of the 4A 2 →4T 1 transition and 4A 2 →4T 2 transitions were calculated to be 1.71 × 10−20 cm2 at 488 nm and 0.72 × 10−20 cm2 at 666 nm, respectively. The crystal field strength Dq, Racah parameters B, and C were calculated to be 1502 cm−1, 533 cm−1, and 3362 cm−1, respectively. In the Cr3+:YScO 3 crystal, the effective phonon energy and Huang-Rhys factor S were calculated to be 284 cm−1 and 8.62, respectively. The emission cross-section at 988 nm corresponding to the 4T 2 →4A 2 transition was calculated to be 1.44 × 10−20 cm2 with full width at half maximum (FWHM) of 318 nm. All the results show that Cr3+:YScO 3 crystal has the potential to be a tunable and ultrafast laser crystal. • Cr:YScO 3 crystals were successfully grown by the Floating zone technique(FZ) method. • Broad emission spectrum with full width at half maximum (FWHM) of 318 nm in Cr:YScO 3 crystals was observed. • Spectral properties and crystal field parameters of Cr:YScO 3 crystals were investigated and analysed. [ABSTRACT FROM AUTHOR]

The polarization absorption spectra of Pr3+-doped GdScO 3 have been measured. Polarized emission spectra and fluorescence decay from the 3P 0 upper level have been investigated. The strongest absorption peaks are located at 448 nm for a, b and c polarization, the absorption cross sections are 1.29 × 10−20 cm2, 0.98 × 10−20 cm2 and 1.57 × 10−20 cm2, respectively. The maximum emission cross section is located at 662 nm, which is 18.55 × 10−20 cm2 (a polarization), 12.74 × 10−20 cm2 (b polarization) and 22.41 × 10−20 cm2 (c polarization), and the FWHM is 10.02 nm, 9.38 nm and 10.14 nm, respectively. The fluorescence lifetime of 3P 0 level is 12.39 μs. Those results indicated that Pr3+-doped GdScO 3 crystal grown by the Czochralski method is a potential laser medium for visible laser operation. •The spectra of Pr:GdScO 3 have been measured at room temperature. •Pr3+-doped GdScO 3 crystal is a potential laser medium for 662 nm laser. [ABSTRACT FROM AUTHOR]

Ho3+ and Eu3+ co-doping GdScO 3 crystal was successfully grown by special EFG method. The spectroscopic properties of the crystal were measured and analyzed. The absorption cross section was calculated to be 2.027 × 10−20 cm2 at 1161 nm. The J-O theory intensity parameters Ω t (t = 2, 4, 6), radiative transition rates, fluorescence branching ratios and radiative lifetimes were calculated. The Ho,Eu:GdScO 3 crystal has very strong emission at 2869 nm and the emission cross section was 13.524 × 10−21 cm2. The fluorescence lifetimes of the 5I 7 and 5I 6 levels were measured to be 4.457 ms and 1.265 ms. Confirmed that Eu3+ can be used as an effective deactivation ion of Ho3+ in GdScO 3 crystal. All those results show that the Ho,Eu:GdScO 3 crystal would be a potential laser material for ∼3 μm mid-infrared region. • Ho,Eu:GdScO 3 crystal was successfully grown. • The spectroscopic properties of the Ho,Eu:GdScO 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho,Eu:GdScO 3 crystal. • The energy transfer between Ho3+ and Eu3+ ions, spectroscopic characteristic of ∼3 μm emission were calculated and analyzed. [ABSTRACT FROM AUTHOR]

A series of 0.5 at.% Tm:Ca 1-x Y x F 2+x (x = 0, 0.01, 0.04, 0.06, 0.08, 0.12) crystals have been successfully grown by the temperature gradient technique (TGT) method. The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. By comparison, it is found that when the concentration of Y3+ ions reaches 8 at.%, the absorption cross section corresponding to the 3H 6 →3H 4 energy level is 2.56 × 10−21 cm2 at 793 nm, which is suitable for GaAlAs LD pumping. The J-O strength parameters Ω 2 , Ω 4 , and Ω 6 were obtained. With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. When the concentration of Y3+ ions reaches 8 at.%, the emission cross sections are 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, and the full widths at half maximum (FWHM) are 76 nm and 195 nm, respectively. The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. • With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. • When the concentration of Y3+ ions reaches 8 at.%, the emission cross section is 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, respectively. • The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. [ABSTRACT FROM AUTHOR]

Ho:Lu 2 O 3 crystal was successfully grown by TGT method. The spectroscopic properties of the crystal were analyzed. The absorption cross section of Ho:Lu 2 O 3 were 0.307 × 10−20 cm2 at 1147 nm and 1.076 × 10−20 cm2 at 1929 nm. J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. The intensity parameters Ω t (t = 2,4,6), radiative transition rates, branching ratios and radiative lifetime were calculated. The Ho:Lu 2 O 3 crystal had very strong emission at 2027 nm and 2849 nm and emission cross sections were calculated to be 3.271 × 10−21 cm2 and 8.852 × 10−21 cm2, respectively. The fluorescence lifetimes of the Ho3+5I 7 and 5I 6 levels were measured to be 12.400 ms and 0.622 ms. All those results show that the Ho: Lu 2 O 3 crystal would be a potential laser material for mid-infrared region. • Ho: Lu 2 O 3 crystal was successfully grown by TGT method. • The spectroscopic properties of the Ho: Lu 2 O 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. • The gain cross-section of Ho:Lu 2 O 3 crystal for ∼2 μm region and ∼3 μm region were calculated. [ABSTRACT FROM AUTHOR]

Tm3+, Pr3+ co-doped Bi 4 Ge 3 O 12 (Tm,Pr:BGO) crystals with various Pr3+ doping concentration were successfully grown using the micro-pulling-down (μ-PD) method. The use of Pr3+ co-doping for deactivating the Tm3+ ions at 1.5 μm emission was investigated in the BGO single crystal for the first time. The effect of Pr3+ concentration on the spectroscopic properties of Tm,Pr:BGO crystals were demonstrated. In addition, the fluorescence lifetime of Tm3+:3F 4 level of 0.5 at.% Pr, 2 at.% Tm:BGO crystal was quenched effectively (from 5.64 ms down to 0.36 ms) and the population inversions between Tm3+:3H 4 and 3F 4 levels are enhanced to achieve a four-level laser system at 1.5 μm. • Tm,Pr:BGO crystals with different Pr3+ concentration were grown using by the micro-pulling-down method. • The effect of Pr3+ concentration on the spectroscopic properties of Tm,Pr:BGO crystals was studied. • The use of Pr3+ co-doping for deactivating the Tm3+ ions at 1.5 μm emission was investigated in BGO crystal. [ABSTRACT FROM AUTHOR]

Abstract: Yb-doped PbClF crystals were obtained by a modified Bridgman method. Broadband emission (FWHM=58nm) with long lifetime (5.33ms) was observed in 2.0% Yb3+-doped PbClF crystals. The Stark splitting of Yb3+ 2F7/2 level was calculated to be 801cm−1 in 0.5% Yb3+-doped PbClF crystals, and the corresponding population of lower laser level is about 2.13%. All the results indicated that Yb-doped PbClF crystals should be a promising material to ultrashort pulses output at 1.0μm. [Copyright &y& Elsevier]

Ho3+-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed growth (EFG) method. The spectroscopic properties of Ho:GdScO 3 crystal were investigated at room temperature. The peak absorption cross-sections were 0.33 × 10−20 cm2 and 1.24 × 10−20 cm2 at 1160 nm and 653 nm with full widths at half maximum of 171.7 nm and 11.5 nm. The peak emission cross-sections of 5I 7 →5I 8 and 5I 6 →5I 7 transitions for the crystal were 0.49 × 10−20 cm2 and 1.24 × 10−20 cm2, respectively. The fluorescence lifetimes of the 5I 6 and 5I 7 multiplets were measured to be 1.12 ms and 6.13 ms, respectively. The results show that Ho:GdScO 3 crystal is a very promising material for 3 μm laser operation. • Ho:GdScO 3 crystal was successfully grown by the edge-defined film-fed growth (EFG) method. • The structure parameters of Ho:GdScO 3 crystal were studied by X-ray diffraction (XRD). • Spectral properties and Judd-Ofelt parameters of Ho:GdScO 3 crystal were investigated and compared. [ABSTRACT FROM AUTHOR]

Tm3+-doped bismuth germanate crystals (Tm:BGO) with various doping concentrations of 0.5, 0.75, 1.0, 1.5, and 2.0 at.% were grown by the micro-pulling-down method (μ-PD). The effect of thulium concentration on the growth, structure, absorption spectra, emission spectra and fluorescence lifetime of 3H 4 and 3F 4 state was studied. Under excitation of 792 nm, Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. The fluorescence lifetime of 3H 4 state decreased strongly as the thulium concentration increased, while the lifetime of 3F 4 state was relatively constant for all thulium concentrations. • Tm:BGO crystals with different Tm3+ concentration were grown by the micro-pulling-down method. • The effect of Tm3+ concentration on the growth, structure and spectroscopic properties of Tm:BGO crystals was studied. • Tm:BGO crystals exhibit two fluorescence bands corresponding to the 3H 4 → 3F 4 and the 3F 4 → 3H 6 transitions. [ABSTRACT FROM AUTHOR]

Abstract: For the first time, a quaternary doping system of Er3+, Yb3+, Ce3+, Na+: CaF2 single crystal was demonstrated to have high fluorescence yield in the 1.5μm region. Through a simplified model, the branching ratio of the Er3+ 4I11/2→4I13/2 transition was estimated to be improved more than 40 times by the deactivating effect of Ce3+ in the quaternary-doped CaF2 crystal with dopants of 0.2-at% Er3+ and 2.0-at% Ce3+. Owing to the broad emission bandwidth and large emission cross-section, the quaternary-doped CaF2 system shows the great potential to achieve the high laser performance in the 1.5μm region. [Copyright &y& Elsevier]

High-quality Dy:PbWO 4 crystal has been successfully grown by the Bridgman method. Fluorescence properties of the grown crystal at the yellow-light region were discussed. The absorption cross-section of Dy3+ ions at 454 nm was calculated to be 0.142 × 10−20 cm2, which corresponded to the transition from 6H 15/2 to 4I 15/2 level. Based on Judd-Ofelt theory, the J-O intensity parameters Ω t and the emission cross-section were calculated. The fluorescence lifetime of 4F 9/2 level was measured to be 193 μs. • Dy: PbWO 4 crystal was grown successfully by the Bridgman method. • Judd-Ofelt theory was used to analyze the spectral properties of Dy: PbWO 4 for the first time. • Dy: PbWO 4 crystal is a potential laser medium for yellow laser operation. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]

Yb,Pr:CaF 2 crystals have been grown successfully by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, fluorescence decay lifetime of Pr3+ ions in CaF 2 crystal sensitized by different Yb3+ ions concentration have been measured. The effective J-O intensity parameters were fitted to be Ω 2 =0.36 × 10−20cm2, Ω 4 =2.89 × 10−20cm2, Ω 6 =6.69 × 10−20cm2 for 0.3 at.%Pr,1.5 at.%Yb:CaF 2. And the emission cross sections of 3P 1 →3H 5 (535 nm), and 3P 0 →3F 4 (750 nm) are calculated to be 2.02 × 10−20cm2, and 2.50 × 10−20cm2 with the FWHM of 17.2 nm, and 10.5 nm, respectively. The fluorescence lifetime of 3P 0 has achieved great increasing by sensitizing of Yb3+ ion. Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed. The results show that Yb,Pr:CaF 2 could be a potential laser gain medium for visible and near-IR laser operation. • Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed by Yb3+ ion sensitizing. • Spectral properties and Judd-Ofelt parameters of Yb,Pr:CaF 2 crystal were investigated and analysed. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]

The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were grown by Floating zone method. The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were investigated. After co-doping small concentration of Pr3+, the depopulated influence of Pr3+ to the NIR emission was much stronger than the MIR emission. The near-infrared and up-conversion fluorescence were significantly quenched. Moreover, the fluorescence lifetime of 4I 13/2 abviously decreases from 4.02 ms to 1.71 ms in 7% Er, 0.05% Pr: Lu 2 O 3 crystal, and the lifetime ratio is 1.63 with large fluorescence lifetime of 4I 11/2 which is desirable lifetime ratio in these crystals. Thus, the spectral performance was significantly improved by co-doping 0.05 at.% of Pr3+. The high laser performance at 2.7 μm of 7% Er, 0.05% Pr: Lu 2 O 3 crystal is expectable. • The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly grown by Floating zone method. • The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly investigated. • After co-doping low concentration of Pr3+, the near-infrared, ESA and up-conversion fluorescence were significantly quenched. • The spectral performance of Er:Lu 2 O 3 crystal was significantly improved at 2.7 μm by co-doping 0.05 at.% of Pr3+. [ABSTRACT FROM AUTHOR]

LaMgAl 11 O 19 (LMA) crystal with nominal Sm3+ concentrations of 8 at.% was grown by the Czochralski method. Polarized absorption spectra, polarized emission spectra and fluorescence decay curve of Sm:LMA crystal were recorded at room temperature. The absorption cross-sections at 404 nm were calculated to be 2.33 × 10−20 cm2 and 0.86 × 10−20 cm2 for σ and π polarization, respectively. The spontaneous transition rates, branching ratios and the radiative lifetime of the 4G 5/2 multiplet, were calculated. The Judd-Ofelt theory has been applied to evaluate the Ω t (t = 2, 4, 6) intensity parameters. The highest stimulated emission cross-sections for the 4G 5/2 → 6H 7/2 transition around 594 nm were calculated to be 1.67 × 10−21 cm2 for σ polarization and 1.15 × 10−21 cm2 for π polarization, with full width at half maximum (FWHM) of 7.68 nm and 7.27 nm, respectively. The fluorescence lifetime of the 4G 5/2 manifold was 1.84 ms. All the results show that Sm:LMA crystal would be a promising orange-red solid state laser material. • The most intensive absorption line of Sm3+ ion, suitable for 405 nm InGaN laser diode. • The rigidity of Sm:LMA crystal is higher than some host crystals. • The value Ω 2 of Sm:LMA crystal is comparable to Sm:LiYF 4. • The large parameter σ em τ of Sm3+ in LMA is beneficial for the solid state laser. [ABSTRACT FROM AUTHOR]