Abstract: Spectroscopic measurements of the calcium niobate CaNb2O6 single crystal doped with samarium ions were performed. Polarized absorption and emission spectra as well as luminescence decay curves of this material were recorded as a function of temperature in the 5–300K temperature region. Analysis of low temperature spectra made it possible to determine energies of crystal field components of Sm3+ multiplets involved in the excitation and luminescence phenomena. Number of crystal field levels derived implies that Sm3+ ions in the CaNb2O6 host are accommodated in several different sites. Radiative lifetime of the 4G5/2 metastable level determined based on the Judd–Ofelt analysis of room temperature absorption spectra amounts to 777μs, a value close to that of luminescence lifetime determined from luminescence decay curve. Energy transfer between the NbO6 group and samarium ions was observed in wide temperature range. Intense luminescence related to the 4G5/2→6H7/2 and 4G5/2→6H9/2 transitions centered at 610nm and 660nm, respectively, combined with strong absorption band near 404nm that matches perfectly the pump light provided by commercial InGaN/GaN diode lasers points at a potential of CaNb2O6:Sm3+ for the design of all-solid-state visible lasers. [Copyright &y& Elsevier]

Abstract: Yb-doped PbClF crystals were obtained by a modified Bridgman method. Broadband emission (FWHM=58nm) with long lifetime (5.33ms) was observed in 2.0% Yb3+-doped PbClF crystals. The Stark splitting of Yb3+ 2F7/2 level was calculated to be 801cm−1 in 0.5% Yb3+-doped PbClF crystals, and the corresponding population of lower laser level is about 2.13%. All the results indicated that Yb-doped PbClF crystals should be a promising material to ultrashort pulses output at 1.0μm. [Copyright &y& Elsevier]