Search

Tm3+-doped calcium niobium gallium garnet (Tm:CNGG) single crystals have been successfully grown by the micro-pulling-down (μ-PD) method. The crystal structure, absorption spectra, fluorescence spectra and lifetimes of Tm:CNGG crystals were investigated. The absorption and emission bandwidths of Tm:CNGG crystals are larger than those of other Tm3+ doped garnet crystals, which will be beneficial for laser diode (LD) pumping and ultrashort pulse generation. Additionally, continuous wave (CW) laser operation around 2 μm was achieved in the 2.0 at.% Tm:CNGG crystal by LD pumping. [ABSTRACT FROM AUTHOR]

Pr 3+ -doped YAlO 3 (YAP) single crystal was successfully grown by the Czochralski (Cz) method. Polarized absorption and polarized fluorescence spectra were measured at the room temperature. The spectroscopic parameters based on the polarized absorption spectra were calculated by Judd-Ofelt (J-O) theory for the first time. The fluorescence lifetime of 3 P 0 energy level was fitted to be 19.16 μs with the quantum efficiency of 95.8%. Through the analyzing of the spectroscopic properties, Pr:YAP crystal was demonstrated to be a promising candidate for solid state laser operation. [ABSTRACT FROM AUTHOR]

Yb,Tb:YAG crystals with various Yb3+ and Tb3+ concentration were grown by the micro-pulling-down method (μ -PD). The absorption spectra, fluorescence spectra and fluorescence decay curves of Yb,Tb:YAG crystals were measured at room temperature. Under 980 nm excitation, Yb,Tb:YAG crystals exhibited intense visible up-conversion luminescence due to the cooperative energy transfer from two Yb3+ ions to one Tb3+ ion. Under 485 nm excitation, Yb,Tb:YAG crystals yielded near-infrared down-conversion emission, ascribing to the cooperative absorption of pumping photons and cooperative energy transfer from one Tb3+ ion to two Yb3+ ions. The energy transfer processes from Yb3+ ions to Tb3+ ions were discussed, and the energy transfer efficiency was calculated. Based on studies of the obtained results, Yb3+/Tb3+ co-doped YAG crystal shows promising potential for sensing, volumetric displays, optical data storage, light emitting diodes. • Yb,Tb:YAG single crystals grown by the micro-pulling-down technique. • The cooperative energy transfer process was analyzed. • The effect of doped concentration on energy transfer efficiency was discussed. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]

Dy3+-doped Y 3 Al 5 O 12 (YAG) and Y 3 ScAl 4 O 12 (YSAG) single crystals have been successfully grown by the micro-pulling-down (μ-PD) technique for the first time. The room temperature absorption spectra, fluorescence spectra and fluorescence decay curves were measured. Dy:YAG and Dy:Y 3 ScAl 4 O 12 crystals exhibit strongest emission centered at 583 nm, corresponding to the 4F 9/2 → 6H 13/2 transition. The decay lifetime of the 4F 9/2 level was measured to be 634 μs and 667 μs, respectively. All these results indicate that the Dy:YAG and Dy:Y 3 ScAl 4 O 12 crystals are promising candidates for yellow laser operation. • Dy:YAG and Dy:YSAG crystals were grown by the micro-pulling-down method. • Dy:YAG and Dy:YSAG crystals exhibit strong emission centered at 583 nm. • Dy:YSAG crystal has a wide emission bandwidth due to the disordered crystalline structure. [ABSTRACT FROM AUTHOR]