Search

A novel Yb,Ho,Pr:LuYAG laser crystal was successfully grown and investigated in detail, which belongs to the cubic system with a space group of I a-3d. The X-ray rocking curve of the as-grown crystal implied high crystalline quality. The dislocation defects were revealed by the chemical method. Moreover, the density, thermal expansion coefficient and thermal conductivity were determined. The absorption coefficient at 935 nm and the emission cross-section at 2.911 μm were obtained to be about 15.18 cm−1 and 2.23 × 10−21 cm2, respectively. The lifetime of the lower laser level 5I 7 was shown to decrease from 7.58 to 5.88 ms, while that of the upper laser level 5I 6 basically remained unchanged, suggesting that the co-doped Pr3+ possessed an efficient deactivation effect and was beneficial in attaining population inversions of Ho3+. The corresponding findings illustrate that the Yb,Ho,Pr:LuYAG crystal can serve as a novel promising gain medium for realizing the 2.911 μm laser pumped by ~ 940 nm high-power InGaAs laser diode. • A novel Yb,Ho,Pr:LuYAG laser crystal was successfully grown by Czochralski method. • The crystal possesses a high thermal conductivity, which is helpful in dissipating heat during laser action. • Yb3+ makes the crystal suitable for 935 nm LD pumping and Pr3+ can inhibit self-termination phenomenon. • High absorption coefficient at 935 nm and large emission cross-section at 2911 nm are beneficial in realizing ∼2.9 μm laser. • The Yb,Ho,Pr:LuYAG crystal is a new promising gain medium for realizing 2.911 μm laser. [ABSTRACT FROM AUTHOR]

Er3+-doped YAP crystals with concentrations of 5 at%, 10 at%, 15 at% and 20 at% were grown successfully by Czochralski method. X-ray rocking curves suggest high crystalline quality. Lifetime ratio of 4I 13/2 and 4I 11/2 levels decreases obviously with the increase of Er3+ concentrations, which is beneficial to realize population inversion and decrease the laser threshold. Spectroscopy and laser show the 15 at% Er:YAP crystal has strongest mid-infrared fluorescence intensity and best laser performance by 968-nm LD side-pumping. Maximum average powers of 23.52 and 11.08 W are achieved at 250 and 1000 Hz, corresponding to the slope efficiency of 12.0% and 6.2%, respectively. Therefore, the 15 at% Er:YAP crystal is a promising candidate for the high-power and high-frequency mid-infrared laser. • High-quality Er:YAP crystals with four concentrations were grown by the Cz method. • Influences of Er3+ concentrations on the performance of Er:YAP crystals were studied. • Energy transfer and luminescence mechanism in the Er:YAP crystals were analyzed. • LD side-pumped high-power and high-frequency Er:YAP laser is demonstrated. • Maximum average power of 23.52 W was obtained on the 15 at% Er:YAP crystal. [ABSTRACT FROM AUTHOR]

We report on the spectroscopic and laser performance of a novel 30 at.% Er:LuYSGG mixed crystal grown by Czochralski method. The XRC result shows the crystal has a high crystalline quality. A strong absorption peak is located at 966 nm with a FWMH of about 11 nm. The lifetimes of the upper 4I 11/2 and lower 4I 13/2 levels are 1.91 ms and 6.53 ms, respectively. A maximum output power of 909 mW with LD end-pumping is achieved, corresponding to optical-to-optical conversion efficiency of 18.1% and slope efficiency of 21.6%. The laser wavelength of 2794 nm and beam quality factors M x 2 /M y 2 of 1.78/1.83 are displayed. These results indicate that Er:LuYSGG mixed crystal is a promising gain medium for 2.8 μm laser. • The Er:LuYSGG mixed crystal with high optical quality was grown by the Cz method. • It has a longer upper laser level lifetime of 1.91 ms. • A maximum output power of 909 mW with LD end-pumping was obtained. • Results indicate the Er:LuYSGG is a promising gain medium for 2.8 μm laser. [ABSTRACT FROM AUTHOR]