Search

Er3+-doped and Er3+/Yb3+-codoped GeO2-Nb2O5-K2O glasses were prepared by conventional melt-quenching method. Thermal and spectroscopic analysis were performed. The niobium insertion into the glass structure has decreased the OH groups resulting in a slight increase in the luminescence efficiency as the niobium content. Glass network structure is modified depending on rare earth doping concentration and niobium content. The number of bridge oxygen bonds and nonbridge oxygen bonds is altered and consequently the crystallization composition. The spectroscopic features were discussed in terms of niobium concentration and its influence on the applications as optical devices. The addition of niobium broadens the emission band in the region of 1.5 µm covering C, S and L-telecommunication bands. The gain coefficient has calculated establishing high potentiality to use the niobium germanate glasses for optical amplification. The codoping by Er3+/Yb3+ intensifies the emission in the NIR and visible (upconversion) region in relation to the doped samples and may be interesting for application as visible and near-infrared emitters. In addition, the codoped samples with variable niobium contents have potential as visible tunable phosphors emitting either green or red light. Accordingly, the niobium germanate glasses are interesting matrices for rare earth ions doping and for the development of optical devices, such as visible and NIR laser and optical amplifiers.

High photoluminescence efficiency, unusual NIR broadband and tunable emission are possible in erbium-doped and tantalum germanate glasses and nanostructured glass-ceramics. The chemical microenvironment around erbium ions and their influence on optical properties are dependent on the TaO6 clusters formation and tantalum perovskite-like bronze crystallization, which are strongly related to the tantalum oxide content and annealing. Erbium ions are preferably distributed close to tantalum-rich environment, providing an intense emission with minimized nonradiative processes and inhomogeneous broadband NIR emission with increasing site numbers. A more pronounced broadening in the nanocrystalline samples is due to the multi-sites of the tantalum perovskite-like bronze crystalline structure. Green/red tunable emission from up conversion processes was observed since the erbium ions occupy a chemical environment with low phonon energy in the tantalum germanate glass and with close neighbors in the tantalum germanate glass-ceramics. Accordingly, the highly tantalum germanate glasses and glass ceramics are promising for photonic applications in optical amplification, lighting and lasing, as well as for nonlinear optical applications and studies considering the perovskite-like bronze crystalline samples.

The relentless pursuit for materials containing rare earth ions with photoluminescent properties has led to several studies with applications in the development of new technologies. The main focus of this work is the preparation of Er 3+ -doped polycrystalline Y 2 O 3 with photoluminescent properties using PEG as an organic precursor and heat-treated at different temperatures. The methodology used in this synthesis is highly attractive due to its high feasibility for improved technology and low cost for preparing materials. The behavior of the viscous resin has been evaluated and the final compounds exhibited the formation of a cubic polycrystalline phase, which is able to support variations in Er 3+ doping concentrations up to 10 mol%, without significant changes in the polycrystalline parameters. The values of the nanocrystallite size calculated by Scherrer׳s equation showed direct dependence on the heat-treatment temperature as well as the Er 3+ concentration. Intense emission in the visible region under excitation at 980 nm was attributed to an upconversion phenomenon assigned to the intraconfigurational f–f transitions of Er 3+ ions. The upconversion mechanism was investigated and it was demonstrated that the higher intense emission in the red region in comparison to the emission in the green region is related to the crystallite size. The studies about the intensity showed the dependence of upconversion emission of power source, indicating that two-photon are responsible for the green and red photoluminescence. These polycrystalline materials exhibit properties that make them promising for use in solar energy systems, C-telecom band or solid-state laser devices.