Search

Nano-sized Zr-Co doped nickel ferrites with nominal composition, NiZr x Co x Fe 2-2x O 4 ( x =0.0, 0.2, 0.4, 0.6, 0.8) were synthesized using the micro-emulsion route. The structural elucidation of the synthesized materials was carried out by X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The XRD analysis confirmed face centered cubic (FCC) structure of all compositions of NiZr x Co x Fe 2-2x O 4 nanocrystallites. Crystallite size was calculated by Scherrer's formula found in the range 10–15 nm. The variation in lattice parameter as determined by XRD data agreed with size variation of host (Fe 3+ ) and guest (Zr 4+ and Co 2+ ) cations. FTIR spectra of doped NiFe 2 O 4 exhibited the typical octahedral bands at 528.4 cm −1 which is the characteristic feature of spinel structure of spinel ferrites. The characterized spinel NiZr x Co x Fe 2-2x O 4 nano-ferrites were evaluated for their potential applications by magnetic hysteresis loops and dielectric measurements. The value of saturation magnetization ( M s ) decreased from 47.9 to 13.09 emu/g up to x =0.8 with ups and downs fluctuations in between x=0.0 to x=0.8. The high values of Ms of some compositions predicted the potential applications in high density perpendicular recording media and microwave devices. The frequency dependent behavior of permittivity (ε') is recorded and discussed with the help of hopping mechanism of both holes and electrons. The dielectric and magnetic data of NiZr x Co x Fe 2-2x O 4 nano-ferrites suggested the potential applications of these ferrite nanoparticles in high frequency and magnetic data storage devices fabrication. [ABSTRACT FROM AUTHOR]

Ni 0.5 Sn 0.5 Co x Mn x Fe 2−2x O 4 ferrites with x = 0.0–0.8 have been prepared by the micro-emulsion method, using CTAB as a surfactant material. X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR) and vibrational sample magnetometer (VSM) were used to investigate the effects of Co and Mn substitutions on cationic distribution, crystallite size, lattice constant, spectral, magnetic and dielectric properties. Lattice constant and crystallite size were found to increase from 7.4 to 9.25 Å and from 11.8 to 19.7 nm respectively with increasing substitution of Co and Mn ions. Saturation magnetization (M S ) gradually increased from 20.5 to 47.6 emu/g with increase in the value of x. However, Coercivity increased from 152.7 to 462.4 Oe up to x = 0.4 and then it decreased thereafter. The dielectric constant, complex dielectric constant and tan loss (tanδ) were observed to decrease with increase in frequency, depicting the semiconductor behavior of the ferrites. Dc resistivity was observed to decrease considerably upon addition of Co and Mn content. The outcome for the tunable magnetic properties and achieved modification of the synthesized nanocrystallites may be chosen for tremendous applications; such as miniaturized memory devices that are based on the energy storage principles and capacitive components. [ABSTRACT FROM AUTHOR]

• Sol-gel route was used to prepare Ba 3 Co 2-x Mg x Fe 24 O 41 hexaferrites. • The occupancy of Mg2+ ions at the octahedral site was altered by Fe3+ ions. • The dielectric permittivity was decreased by incorporating of Magnesium. • Cole – Cole plots revealed a single semi-circle. • Magnetic investigations unfolded ferrimagnetic nature of all samples. The Ba 3 Co 2-x Mg x Fe 24 O 41 hexaferrites were prepared by the sol–gel combustion route. The materials were annealed at 1350 °C and displayed the single-phase characteristics. X-ray density (D x) decreases owing to increasing Mg-concentration. Crystallite size was calculated with the help of Debye Scherrer's formula and found within the 17–18 nm range. Fourier transform infrared spectroscopy was used to determine the specific absorption peaks of hexagonal ferrites. It was executed in the region of 420–700 cm−1—the occupancy of Mg2+ ions at the octahedral site at delayed alternation of Fe3+ ions. As a result, the dielectric permittivity decreased. The grain boundary contribution was clearly seen in synthesized ferrites' cole plots. The cole – cole plots show a single semi-circle which reveals that grain boundaries play a significant role in the conduction process. Magnetic measurement indicated the ferrimagnetic behavior of all samples. [ABSTRACT FROM AUTHOR]

• Sol-gel technique was employed to synthesize Ba 4 Cu 2-x Ni x Fe 36 O 60 ferrites. • Cole-Cole plots markedly distinguished grain boundary contribution. • Coercivity (H c) increased (1844.44–2946.83 Oe) by increasing Ni contents. • The squareness ratio (0.471–0.450) revealed single magnetic domain. • The results suggest their potential use in high-frequency applications. This paper reports the impacts of nickel substitution on dielectric, magnetic, and structural characteristics of Ba 4 Cu 2-x Ni x Fe 36 O 60 hexaferrites prepared via the sol–gel method. The sample was annealed for 5 h at 1200 °C. The crystalline structure, magnetic and dielectric features were examined by X-ray diffraction, vibrating sample magnetometer, and impedance analyzer individually. The specific absorption bands of hexagonal ferrites were identified by FTIR spectroscopy and in the 420–600 cm−1 range. M−H loops of samples were determined to examine the magnetic properties of synthesized materials. Magnetic measurement shows that samples exhibit ferrimagnetic behavior at room temperature. The magnetic properties are described in cation distribution and grain size effect. Dielectric properties of the samples were observed in the frequency range (1–3 GHz). Cole-Cole graphs of prepared materials revealed the influence of grain boundaries. A single semi-circle in the impedance Cole-Cole plots approves a special part of grain boundaries in the conduction process. Dielectric properties are affected by the electron hopping mechanism between Fe2+ and Fe3+ ions. These performances expose that these nanomaterials are appropriate for high-frequency applications. [ABSTRACT FROM AUTHOR]