Search

Organosilane-based thin coating on top of galvannealed (GA) coating, known as secondary coating, provides extra protection from corrosion and thus is used for manufacturing automotive fuel tanks. In the present investigation, resistance seam weldability of 0.8-mm-thick secondary-coated GA interstitial free steel has been evaluated and compared with conventional GA sheets of identical thickness, chemistry, and mechanical properties. It has been found that the 1-3-µm-thick layer of organosilane-based secondary coating increases the electrical contact resistance by up to 50%. Consequently, the heat input increases by 34% when welding secondary coated steel as compared to conventional GA steel. This higher heat-input ensures suitable nugget formation over a wide range of parameters viz. a wider weldability lobe. This paper also addresses the test results on the service life of the welding electrodes. It has been found that the electrodes can withstand up to 30 m of continuous welding of secondary-coated steel without affecting the weld quality in terms of the joint strength. However, for conventional GA sheets, the same electrodes lay up to 20 m of welding length prior to dressing. Higher electrode face widening takes place during welding of plain GA sheets which lowers the current density and thereby affects formation of high-quality weld nugget.

Resistance spot welding (RSW) of Al-Si-coated PHS was undertaken, and the effect of Al-Si coating on nugget formation and mechanical properties was investigated. Press-hardened steel (PHS) has long been applied to automotive body structure construction to support mass and corresponding greenhouse gas emission reductions. PHS materials are often combined with an Al-Si coating applied as an oxidation barrier though unfortunately, the Al-Si coating poses a challenge to the resistance spot welding (RSW) of PHS containing stack-ups. As a newly developed coating for the hot stamping process, the property of Al-Si coating is different from base metal and traditional coatings, and the influence mechanism of Al-Si coating on the welding process is not clear. It would remain at nugget edge and might cause severe stress concentration. To investigate this problem, RSW of 1.5-mm Al-Si-coated PHS was undertaken, and the results indicate that a large portion of the Al-Si coating is extruded and forms a sharp notch close to the nugget edge during the welding process. During the post-weld cooling stage, a thin layer of residual coating is formed between the nugget and notch root. The mechanical performance of the welded joints is limited by the thin residual Al-Si layer which acts as a preexisting crack and supports the interfacial fracture. The presence of the Al-Si coating at the faying interface also significantly delays nugget formation, though it contributes to a larger nugget size by inhibiting expulsion events at the faying interface.

The present paper deals with the joining of 22MnMoB hot-stamping annealed steel carried out by the spot welding process. Microstructural characterization, microhardness testing and tensile-shear testing were conducted. The effects of the welding parameters, including the electrode tip diameter, welding current, welding time and electrode force upon the tensile-shear properties of the welded joints, were investigated. The results showed that a weld size of 9.6 mm was required to ensure pullout failure for the 1.8-mm-thick hot-stamping annealed steel sheet. The welding current had the largest influence upon the tensile-shear properties of the 22MnMoB steel welded joint. The bulk resistance should play an important role in the nugget formation. In pullout failure mode, failure was initiated at the heat-affected zone, where softening occurs owing to the tempering of martensite.

This paper investigates the weld nugget formation in three-sheet aluminum alloy resistance spot welding. The nugget formation process in three equal thickness sheets and three unequal thickness sheets of 5052 aluminum alloy were studied. The results showed that the nugget was initially formed at the workpiece/workpiece interfaces (i.e., both upper interface and lower interface). The two small nuggets then grew along the radial direction and axial direction (welding direction) as the welding time increased. Eventually, the two nuggets fused into one large nugget. During the welding process, the Peltier effect between the Cu-Al caused the shift of the nugget in the welding direction. In addition, the mechanical strength and fracture mode of the weld nuggets at the upper and lower interfaces were also studied using tensile shear specimen configuration. Three failure modes were identified, namely interfacial, mixed, and pullout. The critical welding time and critical nugget diameter corresponding to the transitions of these modes were investigated. Finally, an empirical failure load formula for three-sheet weld similar to two-sheet spot weld was developed.