Search

Zr65Al7.5Ni10Cu12.5Nb5 glass was found to exhibit a large plastic compressive strain of over 10% and the property was suggested to be due to deformation-induced nanocrystallization. A transmission electron microscopic observation, however, only revealed obscure ordered clusters with a size of ˜2 nm in the fracture surface of a deformed sample, instead of well-identified crystals as previously reported for the Zr–Al–Ni–Cu–Pd system. This phenomenon is suggested to correlate with the higher viscosity of supercooled liquid and the slower grain growth of icosahedral phase during primary crystallization in the Zr65Al7.5Ni10Cu12.5Nb5 compared to those in the Zr65Al7.5Ni10Cu12.5Pd5 alloy. The role of the deformation-induced nanoclusters on the enhanced compressive plasticity was discussed. [ABSTRACT FROM AUTHOR]

A new type of Mg-Zn-Cu-Gd-based alloy strengthened by quasicrystal and Laves phase was developed. This alloy exhibits much better creep properties compared to AE42(Mg-4 wt% Al-2 wt% rare-earth) alloy, which is the benchmark creep-resistant magnesium die-casting alloy under the compressive creep condition of 180°C and 80 MPa. The new alloy also exhibits high room-temperature mechanical properties close to that of AZ91 alloy. The good mechanical properties are attributed to the special microstructure; the thermally stable icosahedral quasicrystals phase (i-phase) and Laves phase distributed along the grain boundary as a hard skeleton, and some fine β′1 precipitates distributed homogenously on the matrix. The dislocation morphology after the creep test was studied, and the strengthening mechanism was proposed. [ABSTRACT FROM AUTHOR]

The primary transformation reaction of the Zr65Al7.5Cu27.5 ternary glassy alloy with a low oxygen impurity of approximately 100 mass ppm was investigated. We have discovered the precipitation of the metastable icosahedral phase with a fine grain size of 50-100 nm in diameter accompanying with the formation of stable Zr2Cu phase at the annealing temperatures ranging from 715 to 730 K. The lattice spacing of Zr2Cu phase decreases at higher temperatures, which is attributed to the rearrangement of Zr and Cu in the decomposition of the icosahedral phase. It is suggested that the formation of the icosahedral phase in the primary stage originates from the existence of the quenched-in icosahedral local atomic configuration in the glassy state. [ABSTRACT FROM AUTHOR]

Mechanical properties and fracture characteristics of Zr-based bulk metallic glass (BMG) composites containing carbon nanotube (CNT) addition were investigated in detail. The interfacial reaction between the added CNTs and the glass matrix causes the formation of some V-shape nicks on the residual CNTs. These nicks have significant effect on the mechanical properties and fracture modes of the BMG composites. The compressive fracture strength increases with increasing the volume fraction of CNT addition at first, and starts to decrease gradually when the volume fraction of CNT addition is more than 5.0%. The fracture modes of the BMG composites also change from typical shear flow deformation behavior to completely embrittling fracture gradually. The V-shape nicks originating from the interfacial reaction are responsible for the decrease of fracture strength and the variation of fracture modes. [ABSTRACT FROM AUTHOR]