This research revisited the preparation of the pure titanium dioxide. Through the aerosol-assisted technology and our self-made setup, a kind of titanium dioxide with higher activity than commercial product P25 was successfully fabricated, while this aerosol-assisted process takes only about 10 s. By adjusting the operation temperature, the obtained titanium dioxide nanoparticles have different crystalline sizes and phase compositions, which are two major factors determining the catalytic activity of the materials. The results show that the optimum temperature was 600 °C, and the AST-600 particle prepared under this condition has the rate constant at 1.49 in the removal of methyl orange, which is 2.36 times that of Degussa P25. Although the AST-600 particle could only be activated by UV light similar to P25, the efficiency of AST-600/g-C3N4 is higher than that of P25/g-C3N4 under the visible condition. Meanwhile, the as-prepared titanium dioxide particles have been thoroughly characterized by TEM, SEM, XRD, PL, XPS, DRS, Raman and nitrogen adsorption in the study. Hence, we prepared a pure titanium dioxide with higher catalytic activity than P25, but the process is still very convenient, low cost and easy to scale up, holding great potential as an alternative to commercial product P25.

The modified 9Cr–1Mo steel was selected to conduct friction stir welding experiment. Defect-free welded joints were successfully obtained with the welding parameters of 300 rpm–50 mm/min and 400 rpm–50 mm/min. The microstructures of the welded joint were observed by scanning electron microscopy, electron backscatter diffraction and transmission electron microscope. The main microstructural characteristics of the weld zone (WZ) and the high-temperature heat affected zone are the formation of fresh quenched martensite, dissolution of M23C6 carbides, grain refinement and increase in kernel average misorientation. The WZ is significantly hardened, and the maximum hardness of this region is about twice that of the base material (BM). The ultimate tensile strength of the welded joint is up to 98% that of BM. The absorbed impact energies of the SZ and HAZ reach 77.8% and 87.4% that of the BM, respectively. Besides, the influence of post weld heat treatment on the microstructure and mechanical properties of the welded joint was also investigated.

Fatigue properties of FS welds with a kissing bond (bonded welds) were studied by comparing the test results of bonded welds with those of sound welds. The fatigue life of bonded welds is 21∼43 times shorter than that of sound welds under the stress ratio R = 0.1, and the fatigue characteristic values of each welds have decreased from 100.24 MPa for sound welds to 65.57 MPa for bonded welds at 2 × 106 cycles. At the macroscopic level there is no evidence of failure by shear. The fatigue fracture revealed cracks initiated from the root tip of kissing bond.