Biofilm plays an important role on microbial corrosion and biofouling in marine environments. Inhibiting biofilm formation on construction surfaces is of great importance. Photocatalytic material with visible-light response, especially BiVO4, is regarded as a promising material for biofilm inhibition due to its green biocidal effect and high antibacterial efficiency. Approaches which can immobilize the photocatalytic particles onto metal surfaces with high mechanical strength are requisite. In this study, zinc matrixes were served as carriers for BiVO4 particles. The BiVO4-inserted zinc matrixes were successfully obtained by ultrasound assisted electrodeposition. The insertion content of BiVO4 showed positive correlation with ultrasound power. Highly enhanced biofilm inhibition properties were obtained by BiVO4 inserted zinc matrixes with an over 95 % decreased bacterial coverage. It was proved that O2− (chief) and OH (subordinate) radicals were responsible for the high biocidal performance. Possible antibacterial mechanism was proposed, indicating that the photoinduced holes would both attack zinc crystals to generate active electrons to form O2− radicals, and react with H2O to generate OH, finally. Furthermore, corrosion resistance of the matrixes was proved to be stable due to the insertion of BiVO4. This study provides a potential application for photocatalyst in marine antifouling and anti-biocorrosion aspects.

Microbiologically influenced corrosion caused by sulfate-reducing bacteria (SRB) poses a serious threat to marine engineering facilities. This study focused on the interaction between the corrosion behavior of two aluminum alloys and SRB metabolic activity. SRB growth curve and sulfate variation with and with aluminum were performed to find the effect of two aluminum alloys on SRB metabolic activity. Corrosion of 5052 aluminum alloy and Al-Zn-In-Cd aluminum alloy with and without SRB were performed. The results showed that both the presence of 5052 and Al-Zn-In-Cd aluminum alloy promoted SRB metabolic activity, with the Al-Zn-In-Cd aluminum alloy having a smaller promotion effect compared with 5052 aluminum alloy. The electrochemical results suggested that the corrosion of the Al-Zn-In-Cd aluminum alloy was accelerated substantially by SRB. Moreover, SRB led to the transformation of Al-Zn-In-Cd aluminum alloy corrosion product from Al(OH)3 to Al2S3 and NaAlO2.