Abstract: The roughness evolutions of micro-crystalline silicon thin films (μc-Si:H) with different growth rates prepared by chemical vapor depositions have been investigated by atomic force microscopy. The growth exponent β was measured as 0.8±0.03, 1.1±0.07 and 0.75±0.02 for three sets of samples prepared by PECVD with and without hydrogen dilution ratio modulation and by HWCVD, respectively, and does not correlated with the deposition rate in a set. However, the root-mean-square roughness and lateral correlation length decrease with increasing the deposition rate for both PECVD and HWCVD process. We suggested that the nonstationary growth with large β is correlated with the shadowing effect. The influence of the deposition rate on the surface roughness could be related to the diminishing of the shadowing effect by surface species diffusion with higher mobility on an H-covered surface. The initial surface and nucleation condition play an important role in the surface roughness evolution. [Copyright &y& Elsevier]

Abstract: Indium tin oxide (ITO) films were grown without external heating in an ambient of pure argon by RF-magnetron sputtering method. The influence of argon ambient pressure on the electro-optical properties of as-deposited ITO films was investigated. The morphology, structural and optical properties of ITO films were examined and characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM) and UV–VIS transmission spectroscopy. The deposited ITO films with a thickness of 300nm show a high transparency between 80% and 90% in the visible spectrum and 14–120Ω/□ sheet resistance under different conditions. The ITO films deposited in the optimum argon ambient pressure were used as transparent electrical contacts for thin film Cu(In,Ga)Se2 (CIGS) solar cells. CIGS solar cells with efficiencies of the order of 7.0% were produced without antireflective films. The results have demonstrated that the developed ITO deposition technology has potential applications in thin film solar cells. [Copyright &y& Elsevier]