Search

In this work, a detailed and systematic study of the plasmonic properties of a novel film over nanowell surface is investigated. These nanostructures are fabricated using nanosphere lithography and reactive ion etching and structurally characterized by AFM and SEM. The resulting structures show remarkably narrow plasmon bands in reflectance spectra (as little as 0.10 eV) and greater sensitivity to external dielectric environment than has been seen in other nanoparticle systems, resulting in an improvement in the figure of merit (FOM = refractive index sensitivity (eV.RIU(-1))/full width at half-maximum (eV)) for refractive index sensing. Theoretical modeling for the plasmon spectra of these nanostructures is done using discrete dipole approximation code under periodic boundary conditions. The modeling results match the measurements accurately in aspects of the variation of the plasmon line shape with altering internanowell distance and dielectric environment.

Atomic layer deposition (ALD) is used to deposit 1-600 monolayers of Al(2)O(3) on Ag nanotriangles fabricated by nanosphere lithography (NSL). Each monolayer of Al(2)O(3) has a thickness of 1.1 A. It is demonstrated that the localized surface plasmon resonance (LSPR) nanosensor can detect Al(2)O(3) film growth with atomic spatial resolution normal to the nanoparticle surface. This is approximately 10 times greater spatial resolution than that in our previous long-range distance-dependence study using multilayer self-assembled monolayer shells. The use of ALD enables the study of both the long- and short-range distance dependence of the LSPR nanosensor in a single unified experiment. Ag nanoparticles with fixed in-plane widths and decreasing heights yield larger sensing distances. X-ray photoelectron spectroscopy, variable angle spectroscopic ellipsometry, and quartz crystal microbalance measurements are used to study the growth mechanism. It is proposed that the growth of Al(2)O(3) is initiated by the decomposition of trimethylaluminum on Ag. Semiquantitative theoretical calculations were compared with the experimental results and yield excellent agreement.

A detailed wavelength-scanned surface-enhanced Raman excitation spectroscopy (WS SERES) study of benzenethiol adsorbed on Ag nanoparticle arrays, fabricated by nanosphere lithography (NSL), is presented. These NSL-derived Ag nanoparticle array surfaces are both structurally well-characterized and extremely uniform in size. The WS SERES spectra are correlated, both spatially and spectrally, with the corresponding localized surface plasmon resonance (LSPR) spectra of the nanoparticle arrays. The surface-enhanced Raman scattering (SERS) spectra were measured in two excitation wavelength ranges: (1) 425-505 nm, and (2) 610-800 nm, as well as with the 532-nm line from a solid-state diode-pumped laser. The WS SERES spectra have line shapes similar to those of the LSPR spectra. The maximum SERS enhancement factor is shown to occur for excitation wavelengths that are blue-shifted with respect to the LSPR lambda(max) of adsorbate-covered nanoparticle arrays. Three vibrational modes of benzenethiol (1575, 1081, and 1009 cm(-1)) are studied simultaneously on one substrate, and it is demonstrated that the smaller Raman shifted peak shows a maximum enhancement closer to the LSPR lambda(max) than that of a larger Raman shifted peak. This is in agreement with the predictions of the electromagnetic (EM) enhancement mechanism of SERS. Enhancement factors of up to approximately 10(8) are achieved, which is also in good agreement with our previous SERES studies.

A novel method to produce solution-phase triangular silver nanoparticles is presented. Ag nanoparticles are prepared by nanosphere lithography and are subsequently released into solution. The resulting nanoparticles are asymmetrically functionalized to produce either single isolated nanoparticles or dimer pairs. The structural and optical properties of Ag nanoparticles have been characterized. Mie theory and the Discrete Dipole Approximation method (DDA) have been used to model and interpret the optical properties of the released Ag nanoparticles.

Frequency-scanned excitation profiles of coherent second harmonic generation (SHG) were measured for silver nanoparticle arrays prepared by nanosphere lithography. The frequency of the fundamental beam did not coincide with the localized surface plasmon resonance (LSPR) of the nanoparticles and was tuned so that the coherent second harmonic (SH) emission was in the region of the LSPR at 720-750 nm. The SH emission from the arrays was compared with a smooth silver film to identify an enhancement of SH emission efficiency that peaks near approximately 650 nm for nanoparticles 50 nm in height. The polarization and orientation dependence of this enhancement suggests that it is related to a dipolar LSPR mode polarized normal to the plane of the substrate. Linear extinction spectra are dominated by in-plane dipoles and do not show this weak out-of-plane LSPR mode. The nanoparticle arrays are truncated tetrahedrons symmetrically oriented by nanosphere lithography to cancel SH from in-plane dipoles which allows observation of the weak out-of-plane component.