Search

The crystal structures of Sb2Te3-ySey(y = 0.6 and y = 1.2) at 0 - 24 GPa were investigated by synchrotron X-ray diffraction (XRD). The stoichiometry of Sb2Te3-ySeyused in this study was determined to be Sb2Te2.19(9)Se0.7(2)for y = 0.6 and Sb2Te1.7(1)Se1.3(3)for y = 1.2, on the basis of energy-dispersive X-ray spectroscopy. The sample of Sb2Te2.19(9)Se0.7(2)showed a structural phase transition from a rhombohedral structure (space group No. 166,R3I…m) (phase I) to a monoclinic structure (space group No. 12,C2/m) (phase II), with increasing pressure up to ~9 GPa. A new structural phase (phase II') emerged at 17.7 GPa, a monoclinic structure with the space groupC2/c (No.15). Finally, a 9/10-fold monoclinic structure (space group No. 12,C2/m) (phase III) was observed at 21.8 GPa. In contrast, the sample of Sb2Te1.7(1)Se1.3(3) provided only phase I (space group No. 166,R3I…m) and phase II (space group No. 12,C2/m), showing one structural phase transition from 0 - 19.5 GPa. These samples were not superconductors at ambient pressure, but superconductivity suddenly appeared with increasing pressure. Superconductivity with superconducting transition temperatures (Tc's) of 2 and 4 K was observed above 6 GPa in phase I of Sb2Te2.19(9)Se0.7(2). In this sample, theTcvalues of 6 and 9 K were observed in phase II and phase II' or III of Sb2Te2.19(9)Se0.7(2), respectively. Superconductivity withTc's of 4 and 5 K suddenly emerged in Sb2Te1.7(1)Se1.3(3)at 13.6 GPa, which corresponds to phase II, and it evolved to 6.0 K under further increased pressure. ATcvalue of 9 K was finally found above 15 GPa. The magnetic field dependence ofTcin phase II of Sb2Te2.19(9)Se0.7(2)and Sb2Te1.7(1)Se1.3(3)followed ap-wave polar model, suggesting topologically nontrivial superconductivity.

The crystal structure of BiSbTeSe2 (Bi2-x Sb x Te3-y Se y (x = 1.0 and y = 2.0)) at 0-29 GPa is investigated through synchrotron x-ray diffraction (XRD) and two structural phase transitions are discovered. The stoichiometry of BiSbTeSe2 employed in this study is Bi1.19(4)Sb0.81(4)Te0.83(4)Se2.17(4), as determined from energy-dispersive x-ray spectroscopy. The sample demonstrated structural transitions, from a rhombohedral structure (space group no 166, R [Formula: see text] m) (phase I) to a monoclinic structure (space group no 12, C2/m) (phase II), and from phase II to a 9/10-fold monoclinic structure (space group no 12, C2/m) (phase III). The temperature dependence of resistance (R-T plot) exhibited a semiconducting behavior in a low pressure range and changed from semiconducting to metallic behavior with increasing pressure. Pressure-driven superconductivity is observed above 9.1 GPa in Bi1.19(4)Sb0.81(4)Te0.83(4)Se2.17(4). The pressure phase corresponds to phase II. The superconducting transition temperature, T c, increased with pressure. The maximum T c value is 8.3 K at 19.1 GPa. The magnetic field dependence of T c in phase II of Bi1.19(4)Sb0.81(4)Te0.83(4)Se2.17(4) is proceeded by a p-wave polar model, indicating topologically nontrivial superconductivity. In addition, the emergence of superconductivity and the change in superconducting behavior are closely associated with the structural transitions.

We synthesized the alkaline-earth metal-doped FeSe compounds (NH3) y AE x FeSe (AE: Ca, Sr and Ba), using the liquid NH3 technique, to determine their superconducting properties and crystal structures. Multiple superconducting phases were obtained in each sample of (NH3) y Ca x FeSe and (NH3) y Ba x FeSe, which showed two superconducting transition temperatures (T c's) as high as 37-39 K and 47-48 K at ambient pressure, hereinafter referred to as the 'low-T c phase' and 'high-T c phase', respectively. The high-T c phases in (NH3) y Ca x FeSe and (NH3) y Ba x FeSe were metastable, and rapidly converted to their low-T c phases. However, T c values of 38.4 K and 35.6 K were recorded for (NH3) y Sr x FeSe, which displayed different behavior than (NH3) y Ca x FeSe and (NH3) y Ba x FeSe. The Le Bail fitting of x-ray diffraction (XRD) patterns provided lattice constants of c = 16.899(1) A and c = 16.8630(8) A for the low-T c phases of (NH3) y Ca x FeSe and (NH3) y Ba x FeSe, respectively. The lattice constants of their high-T c phases could not be determined due to the disappearance of the high T c phase within a few days. The XRD pattern for (NH3) y Sr x FeSe indicated the coexistence of two phases with c = 16.899(3) A and c = 15.895(4) A. The former value of c in (NH3) y Sr x FeSe is almost the same as those of the low-T c phases in (NH3) y Ca x FeSe and (NH3) y Ba x FeSe. Therefore, the phase with c = 16.899(3) A in (NH3) y Sr x FeSe must correspond to the superconducting phase with the T c of 38.4 K, while the superconducting phase with T c = 35.6 K is assigned to the crystal phase with c = 15.895(4) A. For (NH3) y Sr x FeSe, a high-T c phase with T c = 47-48 K has not yet been obtained, but a new phase showing the T c value of 35.6 K was clearly obtained. This is the first systematic study of the preparation, crystal structure, and superconductivity of alkaline-earth metal-doped FeSe, (NH3) y AE x FeSe.

Herein, we investigated the pressure dependence of electric transport in a new type of superconducting metal iridate compound, SrIr2, that exhibits a superconducting transition temperature, T c, as high as 6.6 K at ambient pressure, in order to complete the T c-pressure (p ) phase diagram. Very recently, this sample's superconductivity was discovered by our group, but the superconducting behavior has not yet been clarified under pressure. In this study, we fully investigated this sample's superconductivity in a wide pressure range. The T c value decreased with an increase in pressure, but the onset superconducting transition temperature, [Formula: see text], increased above a pressure of 8 GPa, indicating an unconventional superconductivity different from a BCS-type superconductor. The magnetic field dependence of electric resistance (R) against temperature (R - T plot) recorded at 7.94 and 11.3 GPa suggested an unconventional superconductivity, followed by a p -wave polar model, supporting the deviation from a simple s-wave pairing. Moreover, we fully investigated the pressure dependence of crystal structure in SrIr2 and discussed the correlation between superconductivity and crystal structure. This is the first systematic study on superconducting behavior of a new type of metal iridate compound, MIr2 (M: alkali-earth metal atom), under pressure.