A method for phosphors solid-phase synthesis under high pressure is proposed. Using the method, phosphors based on rare earth garnets were synthesized at a temperature considerably lower (1300 °C) than the temperature of the synthesis by conventional method (above 1650 °C). Using organic, inorganic ligaments and synthesized phosphors, remote phosphors were created. The chromaticity coordinates of created LEDs on the base of blue LEDs and remote phosphors fall into the bin of white and green colours. Luminous efficiency reaches 140 lm/W.

Composite material with high thermal conductivity was obtained by the method of thermal sintering of diamonds (synthetic and impact) and copper powder and by further hot isostatic pressing. The content of diamond (the particle size is 20 - 250 μm) in the diamond copper composite was 30 - 45 weight percent. The coefficient of thermal conductivity of copper diamond composite materials based on synthetic diamonds was measured to be 700 - 750 Wm-1K-1. The coefficient of thermal conductivity of copper diamond composite materials based on impact diamonds was measured to be 850 - 900 Wm-1 K-1. The coefficient of thermal expansion (CTE) was measured to be 5.5 - 6.5 • 10-6/°C for synthetic diamonds and 6.1 - 6.5 •10-6/°C for impact diamonds. The obtained copper diamond composite materials are promising to be used as crystal holders for semiconductor crystals in THz and microwave devices.

Composite material with high thermal conductivity was obtained by the method of thermal sintering of a diamond (50 – 75%) with a size of 20 to 250 μm in a matrix of copper.Coefficient of thermal conductivity of copper diamond composite materials was measured and is 450 – 650 Wm-1K-1. The coefficient of thermal expansion CTE was measured and is 5.5 – 7.5 10-6/°C. The obtained copper diamond composite materials are promising objects for use in THz and microwave devices.