Search

A series of composites manganese oxide/carbon with one-dimensional structure are synthesized using electrospinning. The phase composition, morphology and electrochemical performance of MnO x /carbon are studied, which affected by the manganese concentration in precursor and subsequent carbonization conditions. The manufacture of MnO x /carbon is composed of two steps including thermal stabilization (at 250 °C in air) and carbonization (at 700 °C in nitrogen). The main functional groups of samples are well identified by FT-IR spectra. The sample Mn33_3h with the lowest manganese content presents the construction structure which amorphous and/or nanosized MnO x with smaller crystal size are grown and enwrapped in carbon fiber during carbonization. Mn33_3h presents the initial charge and discharge capacities of 1054.1 and 665.6 mAh g−1, and the discharge capacity at the 50th cycle remains 99.7% of that at the 2nd cycle. Beside the well rate capability at the range of current densities from 20 to 1000 mA g−1, Mn33_3h presents very good recovery ability after high rate cycling at 1000 mA g−1. The advantages of this composite structure as well as its high capacity make manganese oxide a very attractive candidate as an anode material for the next generation of rechargeable lithium ion batteries. [ABSTRACT FROM AUTHOR]

Abstract: Monoclinic Li3V2(PO4)3 can be rapidly synthesized at 750°C for 5min (MW5m) by using temperature-controlled microwave solid-state synthesis method (TCMS). The carbon-free sample MW5m presents well electrochemical properties. In the cut-off voltage 3.0–4.3, MW5m presents a charge capacity 132mAhg−1, almost equivalent to the reversible cycling of two lithium ions per Li3V2(PO4)3 formula unit (133mAhg−1), and discharge capacity 126.4mAhg−1. In the cut-off voltage 3.0–4.8V, MW5m shows an initial discharge capacity of 183.4mAhg−1, near to the theoretical discharge capacity. In the cycle performance, the capacity fade of Li3V2(PO4)3 is dependent on the cut-off voltage and the preparation method. [Copyright &y& Elsevier]

Abstract: To substitute minor Mn2+ by the transition metal ion M=Mg2+, V3+, Fe2+, Co2+, or Gd3+, LiMn0.95M0.05PO4 samples are synthesized by a solid-state reaction route. The interpretation of doping effects is complicated by the interrelations between doping microstructure and morphology, because the crystal structure would be affected by the doped elements. The lattice structure and deviation of Li–O bond lengths of the doped LiMnPO4 are refined by XRD refinement. All the samples present a couple of oxidation and reduction peaks in cyclic voltammetry, corresponding to a redox Mn3+/Mn2+ reaction coupled with the extraction/reinsertion process of Li+ in LiMnPO4 structure. During charge/discharge process, the electron flowing and Li+ cation diffusion in the various doped LiMnPO4 samples should be different thermodynamic and kinetic process. For further studying which step in thermodynamic and kinetic process would affect or control the electrochemical performance, the initial charge/discharge capacities and cycleability of doped LiMnPO4 samples are obtained under different voltage range (from 2.7 to the upper cut-off voltage 4.4, 4.6 and 4.8V, respectively) and different environment temperatures (0, 25, and 50°C). At relative higher measuring temperature, the discharge capacity of Co-doped LiMnPO4 shows 151.9mAhg−1. [Copyright &y& Elsevier]