Search

Nanocrystalline silicon carbide has been prepared via reacting magnesium silicide (Mg2Si) with carbon tetrachloride (CCl4) in an autoclave at 450–600°C. X-ray diffraction patterns of the products can be indexed as the cubic cell of SiC with the lattice constant, a=4.352 Å, in good agreement with a=4.349 Å (JCPDS card No. 75-0254). The transmission electron microscopy images show that the sample mainly consists of nanoparticles with an average size from 30 to 80 nm co-existing with a small fraction of nanorods and nanowires. Typically the nanorods range from 20 to 40 nm in diameter and the nanowires have diameters of 20 nm and lengths up to 10 μm. The Raman spectrum shows a characteristic sharp peak at 790 cm-1. X-ray photoelectron spectra (XPS) gives an atomic ratio of Si to C as 1.08:1.00 from the quantification of the peak intensities. Photoluminescence spectrum reveals that the SiC sample emits ultraviolet light of 328 nm. A possible mechanism and the influence of temperature on the formation of crystalline SiC are proposed. [Copyright &y& Elsevier]

Nanocrystalline boron nitride (BN) with needle-like and hollow spherical morphology has been synthesized by nitriding of MgB2 with NH4Cl and NH4Cl–NaN3, respectively. The amount of NaN3 has an obvious effect on the size of the hollow spheres. The samples were characterized by X-ray powder diffraction, Fourier transformation infrared spectroscopy, X-ray photoelectron spectra, and transmission electron microscopy. The possible mechanism of morphology control is also discussed. [Copyright &y& Elsevier]

Abstract: Four types of BN nanotubes are selectively synthesized by annealing porous precursor in flowing NH3 and NH3/H2 atmosphere at temperature ranging from 1000 to 1200°C in a vertical furnace. The as-synthesized BN nanotubes, including cylinder, wave-like, bamboo-like and bubble-chain, are characterized by XRD, FTIR, Raman, SEM, TEM and HRTEM. Three phenomenological growth models are proposed to interpret growth scenario and structure features of the four types of BN nanotubes. Selectivity of nanotubes formation is estimated as approximately 80–95%. The precursor containing B, Mg, Fe and O prepared by self-propagation high-temperature synthesis (SHS) method plays a key role in selective synthesis of the as-synthesized BN nanotubes. Chemical reactions are also discussed. [Copyright &y& Elsevier]

Abstract: Nanocrystalline Mo2C powders were successfully synthesized at 500°C by reacting molybdenum chloride (MoCl5) with C (graphite or carbon nanotube) in metallic sodium medium. X-ray powder diffractometer (XRD), transmission electron microscope (TEM), X-ray photoelectron spectroscope (XPS) and surface area analyzer (BET method) were used to characterize the samples. Experiments reveal that the carbon source used for the carbide synthesis has a great effect on the particle size and the surface area of the samples. When micro-sized graphite was used as C source the obtained nanocrystalline Mo2C powder consists of particles of 30∼100nm, with a surface area of 2.311m2/g. When carbon nanotubes were used as C source, the as-synthesized Mo2C sample is composed of particles of 20∼50nm, with a surface area of 23.458m2/g, which is an order of magnitude larger than that of the carbide prepared from the graphite. [Copyright &y& Elsevier]